The invention relates to an inoculant mixture for the treatment of molten cast iron, comprising 5 to 75% by weight of a ferro-silicon alloy of type A where Si/Fe>2, containing 0.005 to 3% by weight of rare earths, 0.005 to 3% bismuth, lead and/or antimony and less than 3% calcium, with a ratio (Bi+Pb+Sb)/TR of between 0.9 and 2.2 and 25 to 95% of at least one alloy of type B, based on silicon or ferro-silicon such that Si/Fe>2, containing calcium to a level such that the total amount of calcium in the mixture is from 0.3 to 3%. The above mixtures have a good granulometric stability over time and provide an efficient inoculation of cast pieces, in particular of thin pieces.
1. An inoculant blend for the treatment of liquid cast iron, consisting of 5 to 75% by weight of at least one alloy of type A based on ferro-silicon such that Si/Fe>2, containing, by weight, 0.005 to 3% rare earths (RE), 0.05 to 3% bismuth, lead and/or antimony, and less than 3% calcium, with a (Bi+Pb+Sb)/RE ratio of between 0.9 and 2.2 per 25 to 95% of at least one alloy of type B based on silicon or ferro-silicon such that Si/Fe>2, containing less than 0.01% bismuth and calcium with a content greater than that of alloy A, such that the total calcium content of the blend is between 0.3 and 3%.
2. The inoculant blend as claimed in claim 1 , wherein it is in the form of grains having a size of less than 7 mm or powder with a particle size of less than 2.2 mm.
3. The inoculant blend as claimed in claim 1 , wherein alloy A contains 0.3 to 3% magnesium.
4. The inoculant blend as claimed in claim 1 , wherein alloy A contains 0.2 to 0.6% bismuth.
5. The inoculant blend as claimed in claim 1 , wherein alloy A contains less than 2% calcium.
6. The inoculant blend as claimed in claim 5 , wherein alloy A contains less than 0.8% calcium.
7. The inoculant blend as claimed in claim 1 , wherein lanthanum represents more than 70% of the rare earths of alloy A.
8. The inoculant blend as claimed in claim 1 , wherein alloy B contains less than 0.0 1% bismuth, lead and/or antimony.
9. The inoculant blend as claimed in claim 1 , wherein alloy B provides between 75% and 95% of the total calcium in the inoculant blend.
10. The inoculant blend as claimed in claim 9 , wherein alloy B provides between 80 and 90% of the total calcium in the inoculant blend.
11. The inoculant blend as claimed in claim 1 , wherein its total bismuth content is between 0.05 and 0.3%.
12. The inoculant blend as claimed in claim 1 , wherein its total content of rare earths is between 0.04 and 0.15%.
13. The inoculant blend as claimed in claim 1 , wherein its total oxygen content is less than 0.2%.
14. The inoculant blend as claimed in claim 1 , wherein it gives rise, on contact with water at 20° C., to a grain degradation factor, defined as the mass fraction in the 0 to 200 μm range appearing in 24 hours, of less than 10%.
15. The inoculant blend as claimed in claim 14 , wherein its grain degradation factor is less than 5%.
16. The inoculant blend as claimed in claim 1 , wherein alloy B or one of the alloys B is based on ferro-silicon with a silicon content of between 70 and 80%.
17. The inoculant blend as claimed in claim 1 , wherein one of the alloys B is a silicon-calcium alloy with a silicon content of between 54% and 68% and a calcium content of between 25 and 42%.
18. A method for manufacturing cast iron castings having parts with a thickness of less than 6 mm that comprises utilizing the inoculant blend of claim 1 .