Aminofunctional silicone resins and emulsions containing them

View Patent ↗

Loading inventors, assignments & file history…

Monitor This Case

Get email alerts when status or documents change.

Order Certified Copies

Most orders are placed with the USPTO same day — all within 24 business hours.

Order via The Patent Place →

Pre-filled with this patent's details

Quick Facts

Patent No.: US 7,501,473
App. No.: 10/564,610
Granted: Mar 10, 2009
Kind: B2

External Links

USPTO Patent Center↗ Full Patent PDF↗

Abstract

This invention relates to aminofunctional silicone resins having high aryl content R 2 SiO 2/2 content and amine content. The aminofunctional silicone resins of this invention are useful in making tough, water, solvent, and heat resistant hybrid materials when used in combination with selected organic materials, particularly epoxy-containing organic materials. The aminofunctional resins of this invention have the ability to flexibilize epoxy compounds while maintaining low CTE and solvent resistance. This invention also relates to emulsion compositions containing the above described aminofunctional silicone resins.

Claims (188)

1. An aminofunctional silicone resin comprising the units:

(R 3 SiO 1/2 ) a (i)

(R 2 SiO 2/2 ) b (ii)

(RSiO 3/2 ) c (iii) and

(SiO 4/2 ) d (iv)

wherein R is independently an alkyl group, an aryl group, or an aminofunctional hydrocarbon group, a has a value of less than 0.4, b has a value of greater than 0.15, c has a value of greater than zero to 0.7, d has a value of less than 0.2, the value of a +b+c+d=1, with the provisos that 3 to 50 mole percent of silicon atoms contain aminofunctional hydrocarbon groups in units (i), (ii) or (iii), the —NH— equivalent weight of the aminofunctional silicone resin is from 100 to 1500, the aminofunctional silicone resin is in the form of a neat liquid, solution, or meltable solid, greater than 20 weight percent of unit (ii) is present in the aminofunctional silicone resin, less than 10 weight percent of unit (ii) are Me 2 SiO 2/2 units in the aminofunctional silicone resin, and greater than 50 weight percent of silicon-bonded R groups are silicon-bonded aryl groups.

2. An aminofunctional silicone resin comprising the units:

(R 3 SiO 1/2 ) a (i)

(R 2 SiO 2/2 ) b (ii)

(RSiO 3/2 ) c (iii) and

(SiO 4/2 ) d (iv)

wherein R is independently an alkyl group, an aryl group, or an aminofunctional hydrocarbon group, a has a value of less than 0.4, b has a value of greater than 0.15, c has a value of greater than zero to 0.7, d has a value of less than 0.2, the value of a+b+c+d=1, with the provisos that 3 to 50 mole percent of silicon atoms contain aminofunctional hydrocarbon groups in units (i), (ii) or (iii), the —NH— equivalent weight of the aminofunctional silicone resin is from 100 to 1000, the aminofunctional silicone resin is in the form of a neat liquid, solution, or meltable solid, greater than 20 weight percent of unit (ii) is present in the aminofunctional silicone resin, less than 10 weight percent of unit (ii) are Me 2 SiO 2/2 units in the aminofunctional silicone resin, and greater than 50 weight percent of silicon-bonded R groups are silicon-bonded aryl groups.

3. An aminofunctional silicone resin according to claim 1 wherein R is independently selected from methyl, phenyl, or an aminofunctional hydrocarbon group having the formula R 1 NHR 2 or —R 1 NHR 1 NHR 2 wherein each R 1 is independently a divalent hydrocarbon radical having at least 2 carbon atoms and R 2 is hydrogen or an alkyl group.

4. An aminofunctional silicone resin according to claim 1 wherein the aminofunctional hydrocarbon groups are selected from —CH 2 CH 2 NH 2 , —CH 2 CH 2 CH 2 NH 2 , —CH 2 CHCH 3 NH, —CH 2 CH 2 CH 2 CH 2 NH 2 , —CH 2 CH 2 CH 2 CH 2 CH 2 NH 2 , —CH 2 CH 2 CH 2 CH 2 CH 2 CH 2 NH 2 , —CH 2 CH 2 NHCH 3 , —CH 2 CH 2 CH 2 NHCH 3 , —CH 2 (CH 3 )CHCH 2 NHCH 3 , —CH 2 CH 2 CH 2 CH 2 NHCH 3 , —CH 2 CH 2 NHCH 2 CH 2 NH 2 , —CH 2 CH 2 CH 2 NHCH 2 CH 2 CH 2 NH 2 , —CH 2 CH 2 CH 2 CH 2 NHCH 2 CH 2 CH 2 CH 2 NH 2 , —CH 2 CH 2 NHCH 2 CH 2 NHCH 3 , —CH 2 CH 2 CH 2 NHCH 2 CH 2 CH 2 NHCH 3 , —CH 2 CH 2 CH 2 CH 2 NHCH 2 CH 2 CH 2 CH 2 NHCH 3 , and —CH 2 CH 2 NHCH 2 CH 2 NHCH 2 CH 2 CH 2 CH 3 —.

5. An aminofunctional resin according to claim 1 wherein the aminofunctional silicone resin is selected from

aminofunctional silicone resins comprising the units:

(i) ((CH 3 ) 3 SiO 1/2 ) a

(ii) (C 6 H 5 (CH 3 )SiO 2/2 ) b

(iii) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 CH 2 CH 2 NH 2

(iv) (C 6 H 5 SiO 3/2 ) c ,

aminofunctional silicone resins comprising the units:

(i) (C 6 H 5 (CH 3 )SiO 2/2 ) b

(ii) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 CH 2 CH 2 NH 2

(iii) (C 6 H 5 SiO 3/2 ) c ,

aminofunctional silicone resins comprising the units:

(i) ((CH 3 ) 3 SiO 1/2 ) a

(ii) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 CH 2 CH 2 NH 2

(iii) (RSiO 3/2 ) c where R=—CH 2 CH 2 CH 2 NH 2

(iv) (C 6 H 5 SiO 3/2 ) c ,

aminofunctional silicone resins comprising the units:

(i) ((CH 3 ) 3 SiO 1/2 ) a

(ii) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 CH 2 CH 2 NH 2

(iii) (C 6 H 5 SiO 3/2 ) c or

aminofunctional silicone resins comprising the units:

(i) ((CH 3 ) 3 SiO 1/2 ) a

(ii) (C 6 H 5 (CH 3 )SiO 2/2 ) b

(iii) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 CH 2 CH 2 NH 2

(iv) (C 6 H 5 SiO 3/2 ) c

(v) (SiO 4/2 ) d

wherein a, b, c, and d are as defined above.

6. An aminofunctional resin according to claim 1 wherein the aminofunctional silicone resin is selected from aminofunctional silicone resins comprising the units:

(i) ((CH 3 ) 3 SiO 1/2 ) a

(ii) (C 6 H 5 (CH 3 )SiO 2/2 ) b

(iii) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 CH 2 CH 2 NH 2

(iv) (C 6 H 5 SiO 3/2 ) c ,

aminofunctional silicone resins comprising the units:

(i) (C 6 H 5 (CH 3 )SiO 2/2 ) b

(ii) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 CH 2 CH 2 NH 2

(iii) (C 6 H 5 SiO 3/2 ) c ,

aminofunctional silicone resins comprising the units:

(i) ((CH 3 ) 3 SiO 1/2 ) a

(ii) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 CH 2 CH 2 NH 2

(iii) (RSiO 3/2 ) c where R=—CH 2 CH 2 CH 2 NH 2

(iv) (C 6 H 5 SiO 3/2 ) c ,

aminofunctional silicone resins comprising the units:

(i) ((CH 3 ) 3 SiO 1/2 ) a

(ii) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 CH 2 CH 2 NH 2

(iii) (C 6 H 5 SiO 3/2 ) c

aminofunctional silicone resin comprising the units

(i) ((CH 3 ) 3 SiO 1/2 ) a

(ii) (CH 3 ) 2 SiO 2/2 ) b

(iii) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 CH 2 CH 2 NH 2

(iv) (C 6 H 5 SiO 3/2 ) c

aminofunctional silicone resin comprising the units:

(i) ((CH 3 ) 2 RSiO 1/2 ) a where R=—CH 2 (CH 3 )CHCH 2 NHCH 3

(ii) (CH 3 ) 2 SiO 2/2 ) b

(iii) (C 6 H 5 (CH 3 )SiO 2/2 ) b

(iv) (C 6 H 5 SiO 3/2 ) c

aminofunctional silicone resins comprising the units:

(i) ((CH 3 ) 2 RSiO 1/2 ) a where R=—CH 2 (CH 3 )CHCH 2 NHCH 3

(ii) (C 6 H 5 (CH 3 )SiO 2/2 ) b

(iii) (C 6 H 5 SiO 3/2 ) c ,

aminofunctional silicone resins comprising the units:

(i) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 (CH 3 )CHCH 2 NHCH 3

(ii) (C 6 H 5 (CH 3 )SiO 2/2 ) b

(iii) (C 6 H 5 SiO 3/2 ) c ,

aminofunctional silicone resins comprising the units:

(i) ((CH 3 ) 2 RSiO 1/2 ) a where R=—CH 2 (CH 3 )CHCH 2 NHCH 3

(ii) (C 6 H 5 (CH 3 )SiO 2/2 ) b

(iii) (SiO 4/2 ) d , or

aminofunctional silicone resins comprising the units:

(i) ((CH 3 ) 3 SiO 1/2 ) a

(ii) (C 6 H 5 (CH 3 )SiO 2/2 ) b

(iii) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 CH 2 CH 2 NH 2

(iv) (C 6 H 5 SiO 3/2 ) c

(v) (SiO 4/2 ) d

wherein a, b, c, and d are as defined above.

7. An emulsion composition comprising:

(A) an aminofunctional silicone resin comprising the units:

(R 3 SiO 1/2 ) a (i)

(R 2 SiO 2/2 ) b (ii)

(RSiO 3/2 ) c (iii) and

(SiO 4/2 ) d (iv)

wherein R is independently an alkvl group. an aryl group. or an aminofunctional hydrocarbon group, a has a value of less than 0.4, b has a value of greater than 0.15, c has a value of greater than zero to 0.7, d has a value of less than 0.2, the value of a+b+c+d=1, with the provisos that 3 to 50 mole percent of silicon atoms contain aminofunctional hydrocarbon groups in units (i), (ii) or (iii), the —NH— equivalent weight of the aminofunctional silicone resin is from 100 to 1500, the aminofunctional silicone resin is in the form of a neat liquid, solution, or meltable solid, greater than 20 weight percent of unit (ii) is present in the aminofunctional silicone resin, less than 10 weight percent of unit (ii) are Me 2 SiO 2/2 units in the aminofunctional silicone resin, and greater than 50 weight percent of silicon-bonded R groups are silicon-bonded aryl groups;

(B) at least one surfactant; and

8. An emulsion composition according to claim 7 wherein a has a value of 0.1 to 0.3, b has a value of 0.2 to 0.4, c has a value of 0.2 to 0.5, d has a value of 0, 10 to 30 mole percent of silicon atoms contain aminofunctional hydrocarbon groups in units (i), (ii) or (iii), the —NH— equivalent weight of the aminofunctional silicone resin is from 150 to 350, 20 to 50 weight percent of unit (ii) is present in the aminofunctional silicone resin, 0 to 5 weight percent of unit (ii) are Me 2 SiO 2/2 units in the aminofunctional silicone resin, and from 50 to 75 weight percent of silicon-bonded R groups are silicon-bonded aryl groups.

9. An emulsion composition according to claim 7 wherein the surfactant is selected from anionic surfactants, cationic surfactants, nonionic surfactants, amphoteric surfactants, or a combination thereof.

10. An emulsion composition according to claim 7 , wherein the emulsion composition further comprises at least one ingredient selected from fragrances, preservatives, vitamins, ceramides, amino-acid derivatives, liposomes, polyols, botanicals, conditioning agents, glycols, vitamin A, vitamin C, vitamin B, Pro-Vitamin B5, sunscreen agents, humectants, preservatives, emollients, occlusive agents, esters, pigments, or self-tanning agents.

11. An emulsion composition according to claim 7 , wherein the emulsion is in the form of spray-dried composite particles.

12. An aminofunctional silicone resin according to claim 2 wherein R is independently selected from methyl, phenyl, or an aminofunctional hydrocarbon group having the formula R 1 NHR 2 or —R 1 NHR 1 NHR 2 wherein each R 1 is independently a divalent hydrocarbon radical having at least 2 carbon atoms and R 2 is hydrogen or an alkyl group.

13. An aminofunctional silicone resin according to claim 2 wherein the aminofunctional hydrocarbon groups are selected from —CH 2 CH 2 NH 2 , —CH 2 CH 2 CH 2 NH 2 , —CH 2 CHCH 3 NH, —CH 2 CH 2 CH 2 CH 2 NH 2 , —CH 2 CH 2 CH 2 CH 2 CH 2 NH 2 , —CH 2 CH 2 CH 2 CH 2 CH 2 CH 2 NH 2 , —CH 2 CH 2 NHCH 3 , —CH 2 CH 2 CH 2 NHCH 3 , —CH 2 (CH 3 )CHCH 2 NHCH 3 , —CH 2 CH 2 CH 2 CH 2 NHCH 3 , —CH 2 CH 2 NHCH 2 CH 2 NH 2 , —CH 2 CH 2 CH 2 NHCH 2 CH 2 CH 2 NH 2 , —CH 2 CH 2 CH 2 CH 2 NHCH 2 CH 2 CH 2 CH 2 NH 2 , —CH 2 CH 2 NHCH 2 CH 2 NHCH 3 , —CH 2 CH 2 CH 2 NHCH 2 CH 2 CH 2 NHCH 3 , —CH 2 CH 2 CH 2 CH 2 NHCH 2 CH 2 CH 2 CH 2 NHCH 3 , and —CH 2 CH 2 NHCH 2 CH 2 NHCH 2 CH 2 CH 2 CH 3 —.

14. An aminofunctional resin according to claim 2 wherein the aminofunctional silicone resin is selected from

aminofunctional silicone resins comprising the units:

(i) ((CH 3 ) 3 SiO 1/2 ) a

(ii) (C 6 H 5 (CH 3 )SiO 2/2 ) b

(iii) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 CH 2 CH 2 NH 2

(iv) (C 6 H 5 SiO 3/2 ) c ,

aminofunctional silicone resins comprising the units:

(i) (C 6 H 5 (CH 3 )SiO 2/2 ) b

(ii) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 CH 2 CH 2 NH 2

(iii) (C 6 H 5 SiO 3/2 ) c ,

aminofunctional silicone resins comprising the units:

(i) ((CH 3 ) 3 SiO 1/2 ) a

(ii) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 CH 2 CH 2 NH 2

(iii) (RSiO 3/2 ) c where R=—CH 2 CH 2 CH 2 NH 2

(iv) (C 6 H 5 SiO 3/2 ) c ,

aminofunctional silicone resins comprising the units:

(i) ((CH 3 ) 3 SiO 1/2 ) a

(ii) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 CH 2 CH 2 NH 2

(iii) (C 6 H 5 SiO 3/2 ) c or

aminofunctional silicone resins comprising the units:

(i) ((CH 3 ) 3 SiO 1/2 ) a

(ii) (C 6 H 5 (CH 3 )SiO 2/2 ) b

(iii) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 CH 2 CH 2 NH 2

(iv) (C 6 H 5 SiO 3/2 ) c

(v) (SiO 4/2 ) d

wherein a, b, c, and d are as defined above.

15. An aminofunctional resin according to claim 2 wherein the aminofunctional silicone resin is selected from aminofunctional silicone resins comprising the units:

(i) ((CH 3 ) 3 SiO 1/2 ) a

(ii) (C 6 H 5 (CH 3 )SiO 2/2 ) b

(iii) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 CH 2 CH 2 NH 2

(iv) (C 6 H 5 SiO 3/2 ) c ,

aminofunctional silicone resins comprising the units:

(i) (C 6 H 5 (CH 3 )SiO 2/2 ) b

(ii) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 CH 2 CH 2 NH 2

(iii) (C 6 H 5 SiO 3/2 ) c ,

aminofunctional silicone resins comprising the units:

(i) ((CH 3 ) 3 SiO 1/2 ) a

(ii) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 CH 2 CH 2 NH 2

(iii) (RSiO 3/2 ) c where R=—CH 2 CH 2 CH 2 NH 2

(iv) (C 6 H 5 SiO 3/2 ) c ,

aminofunctional silicone resins comprising the units:

(i) ((CH 3 ) 3 SiO 1/2 ) a

(ii) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 CH 2 CH 2 NH 2

(iii) (C 6 H 5 SiO 3/2 ) c

aminofunctional silicone resin comprising the units

(i) ((CH 3 ) 3 SiO 1/2 ) a

(ii) (CH 3 ) 2 SiO 2/2 ) b

(iii) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 CH 2 CH 2 NH 2

(iv) (C 6 H 5 SiO 3/2 ) c

aminofunctional silicone resin comprising the units:

(i) ((CH 3 ) 2 RSiO 1/2 ) a where R=—CH 2 (CH 3 )CHCH 2 NHCH 3

(ii) (CH 3 ) 2 SiO 2/2 ) b

(iii) (C 6 H 5 (CH 3 )SiO 2/2 ) b

(iv) (C 6 H 5 SiO 3/2 ) c

aminofunctional silicone resins comprising the units:

(i) ((CH 3 ) 2 RSiO 1/2 ) a where R=—CH 2 (CH 3 )CHCH 2 NHCH 3

(ii) (C 6 H 5 (CH 3 )SiO 2/2 ) b

(iii) (C 6 H 5 SiO 3/2 ) c ,

aminofunctional silicone resins comprising the units:

(i) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 (CH 3 )CHCH 2 NHCH 3

(ii) (C 6 H 5 (CH 3 )SiO 2/2 ) b

(iii) (C 6 H 5 SiO 3/2 ) c ,

aminofunctional silicone resins comprising the units:

(i) ((CH 3 ) 2 RSiO 1/2 ) a where R=—CH 2 (CH 3 )CHCH 2 NHCH 3

(ii) (C 6 H 5 (CH 3 )SiO 2/2 ) b

(iii) (SiO 4/2 ) d , or

aminofunctional silicone resins comprising the units:

(i) ((CH 3 ) 3 SiO 1/2 ) a

(ii) (C 6 H 5 (CH 3 )SiO 2/2 ) b

(iii) ((CH 3 )RSiO 2/2 ) b where R=—CH 2 CH 2 CH 2 NH 2

(iv) (C 6 H 5 SiO 3/2 ) c

(v) (SiO 4/2 ) d

wherein a, b, c, and d are as defined above.

16. An emulsion composition comprising:

(A) an aminofunctional silicone resin comprising the units:

(R 3 SiO 1/2 ) a (i)

(R 2 SiO 2/2 ) b (ii)

(RSiO 3/2 ) c (iii) and

(SiO 4/2 ) d (iv)

wherein R is independently an alkyl group, an aryl group, or an aminofunctional hydrocarbon group, a has a value of less than 0.4, b has a value of greater than 0.15, c has a value of greater than zero to 0.7, d has a value of less than 0.2, the value of a+b=c+d=1, with the provisos that 3 to 50 mole percent of silicon atoms contain aminofunctional hydrocarbon groups in units (i), (ii) or (iii), the —NH— equivalent weight of the aminofunctional silicone resin is from 100 to 1000, the aminofunctional silicone resin is in the form of a neat liquid, solution, or meltable solid, greater than 20 weight percent of unit (ii) is present in the aminofunctional silicone resin, less than 10 weight percent of unit (ii) are Me 2 SiO 2/2 units in the aminofunctional silicone resin, and greater than 50 weight percent of silicon-bonded R groups are silicon-bonded aryl groups;

(B) at least one surfactant; and

17. An emulsion composition according to claim 16 wherein a has a value of 0.1 to 0.3, b has a value of 0.2 to 0.4, c has a value of 0.2 to 0.5, d has a value of 0, 10 to 30 mole percent of silicon atoms contain aminofunctional hydrocarbon groups in units (i), (ii) or (iii), the —NH— equivalent weight of the aminofunctional silicone resin is from 150 to 350, 20 to 50 weight percent of unit (ii) is present in the aminofunctional silicone resin, 0 to 5 weight percent of unit (ii) are Me 2 SiO 2/2 units in the aminofunctional silicone resin, and from 50 to 75 weight percent of silicon-bonded R groups are silicon-bonded aryl groups.

18. An emulsion composition according to claim 16 wherein the surfactant is selected from anionic surfactants, cationic surfactants, nonionic surfactants, amphoteric surfactants, or a combination thereof.

19. An emulsion composition according to any of claims 16 , wherein the emulsion composition further comprises at least one ingredient selected from fragrances, preservatives, vitamins, ceramides, amino-acid derivatives, liposomes, polyols, botanicals, conditioning agents, glycols, vitamin A, vitamin C, vitamin E, Pro-Vitamin B5, sunscreen agents, humectants, preservatives, emollients, occlusive agents, esters, pigments, or self-tanning agents.

20. An emulsion composition according to any of claims 16 , wherein the emulsion is in the form of spray-dried composite particles.

Assignments (1)

CHANGE OF NAME Recorded Feb 27, 2018

From: DOW CORNING CORPORATION

To: DOW SILICONES CORPORATION

Reel/Frame 045460/0278 →