Interpolymers suitable for use in hot melt adhesives and processes to prepare same
The present invention relates to an ethylene/α-olefin interpolymer product comprising at least one α-olefin interpolymerized with ethylene and, characterized in at least one aspect, as having improved properties when utilized in a hot melt adhesive formulation. The invention also relates to a process for manufacturing the interpolymer product wherein the process comprises employing two or more single site catalyst systems in at least one reaction environment (or reactor) and wherein the at least two catalyst systems have (a) different comonomer incorporation capabilities or reactivities and/or (b) different termination kinetics, both when measured under the same polymerization conditions. The interpolymer products are useful, for example, in applications such as hot melt adhesives, and also for impact, bitumen and asphalt modification, adhesives, dispersions or latexes and fabricated articles such as, but not limited to, foams, films, sheet, moldings, thermoforms, profiles and fibers.
1. An ethylene interpolymer having the following properties:
i) a number average molecular weight (Mn) from 1,000 to 9,000; and
ii) a Brookfield Viscosity (measured at 149° C./300° F.) from 500 to 9,000 cP; and wherein the interpolymer comprises a high weight average molecular weight polymer component (M wH ) and a low weight average molecular weight polymer component (M wL ), and wherein the ratio M wH /M wL is from about 1.5 to about 20.
2. The ethylene interpolymer of claim 1 , wherein interpolymer has iii) a density from 0.88 to 1.06 g/cm 3 .
3. The ethylene interpolymer of claim 2 , wherein the interpolymer is derived from olefinic comonomer reactants, comprising at least ethylene and styrene, and has iii) a density from 0.931 to 1.06 g/cm 3 .
4. The ethylene interpolymer of claim 2 , wherein the interpolymer has iii) a density from 0.88 to 0.93 g/cm 3 .
5. The ethylene interpolymer of claim 4 , wherein the interpolymer has the following properties:
i) a density from 0.89 to 0.92 g/cm 3 ;
ii) a number average molecular weight (Mn) from 1250 to 7,000; and
iii) a Brookfield Viscosity (measured at 149° C./300° F.) from 1,000 to 6,000 cP; and wherein, when the one or more tackifiers are added, in an amount from 20 to 35 percent by weight (based on the combined weight of interpolymer and tackifier), to said ethylene interpolymer, the resulting composition has the following properties:
a) a Brookfield Viscosity (measured at 177° C./350° F.) from 500 to 1,400 cP;
b) a Peel Adhesion Failure Temperature (PAFT) greater than, or equal to, 115° F.; and
c) a Shear Adhesion Failure Temperature (SAFT) greater than, or equal to, 150° F.; and
d) 100% paper tear from 35 to 140° F.
6. The ethylene interpolymer of claim 4 , wherein the interpolymer has the following properties:
i) a density from 0.895 to 0.915 g/cm 3 ;
ii) a number average molecular weight (Mn) from 1500 to 6,000; and
iii) a Brookfield Viscosity (measured at 149° C./300° F.) from 1,500 to 5,000 cP; and wherein, when the one or more tackifiers are added, in an amount from 20 to 35 percent by weight (based on the combined weight of interpolymer and tackifier), to said ethylene interpolymer, then the resulting composition has the following properties:
a) a Brookfield Viscosity (measured at 177° C./350° F.) from 750 to 1,200 cP;
b) a Peel Adhesion Failure Temperature (PAFT) greater than, or equal to, 120° F.; and
c) a Shear Adhesion Failure Temperature (SAFT) greater than, or equal to, 170° F.; and
d) a 100% paper tear from 0 to 140° F.
7. The ethylene interpolymer of claim 4 , wherein said interpolymer is a copolymer of ethylene/propylene, ethylene/1-butene, ethylene/4-methyl-1-pentene, ethylene/1-pentene, ethylene/1-hexene or ethylene/1-octene.
8. The ethylene interpolymer of claim 1 , produced by a process comprising:
a) contacting one or more olefinic monomers in the presence of at least a high molecular weight catalyst having a reactivity ratio r 1 H , and at least a low molecular weight catalyst having a reactivity ratio r 1 L , in a single reactor; and
b) effectuating the polymerization of the olefinic monomers in the reactor, to obtain an olefin polymer; and
wherein each of r 1 H and r 1 L is from about 1 to about 200, and r 1 H /r 1 L is from 0.03 to 30; and/or
wherein the high molecular weight catalyst is capable of producing a polymer with a high molecular weight M wH from the monomers, under selected polymerization conditions, and the low molecular weight catalyst is capable of producing a polymer with a low molecular weight M wL from the same monomers, under substantially the same polymerization conditions, and wherein M wH /M wL is from 1.5 to 20.
9. The ethylene interpolymer of claim 1 , wherein the interpolymer contains the residue of at least two catalysts, a first catalyst having a reactivity ratio r 1 H , and a second catalyst having a reactivity ratio r 1 L , and wherein each of r 1 H and r 1 L , independently, is a number from 1 to 200, and r 1 H /r 1 L is a number from 0.03 to 30.
10. The ethylene interpolymer of claim 9 , wherein the ratio r 1 H /r 1 L is a number greater than 1.
11. The ethylene interpolymer of claim 1 , wherein the interpolymer has a number average molecular weight from 2,000 to 9,000.
12. The ethylene interpolymer of claim 1 , wherein the interpolymer as a Brookfield Viscosity (measured at 149° C. (300° F.)) from 1,500 to 9,000 cP.
13. The ethylene interpolymer of claim 1 , wherein the ratio, M wH /M wL , is from about 2 to about 10.
14. The ethylene interpolymer of claim 1 , wherein the interpolymer has a molecular weight distribution (M w /M n ) from about 2 to about 20.
15. The ethylene interpolymer of claim 1 , wherein, when one or more tackifiers are added, in an amount of from 15 to 40 percent, by weight (based on the combined weight of interpolymer and tackifier), to said ethylene interpolymer, the resulting composition has the following properties:
a) a Brookfield Viscosity (measured at 177° C./350° F.) from 400 to 2,000 cP;
b) a Peel Adhesion Failure Temperature (PAFT) of greater than, or equal to, 110° F.; and
c) a Shear Adhesion Failure Temperature (SAFT) of greater than, or equal to, 140° F.