Method for production of thermally cured coatings
Method for production of a coating on a solid substrate comprising the steps of applying a liquid coating composition comprising a polyfunctional resin, a fatty acid or derivative thereof acting as a reactive diluent and optionally a curing agent and/or one or more additives, wherein the resin comprises functional groups capable of reacting with carboxyl or acyl groups of the fatty acid or derivative thereof, onto the substrate, and curing the coating by heat activation. The invention further relates to the liquid coating composition as well as a substrate comprising a coating obtained by heat activation of such a coating composition.
1. A method for production of a coating on a solid substrate, said method comprising the steps of:
applying a non-aqueous liquid coating composition onto the substrate, said non-aqueous liquid coating composition comprising a polyfunctional resin, a fatty acid derivative that is an acyl-group containing monofunctional or polyfunctional alkyl esters, a catalyst, optionally a curing agent and optionally one or more additives, wherein the polyfunctional resin comprises functional groups that react with acyl groups of the fatty acid derivative, and
curing the liquid coating composition by heat activation.
2. The method according to claim 1 , wherein the polyfunctional resin is an alkyd, a polyester, polyacrylate, polymethacrylate, phenolic, or amino resin.
3. The method according to claim 2 , wherein the curing agent is an epoxy functional compound, a phenolic functional crosslinker, a hydroxyl functional crosslinker, an amine functional crosslinker, a carboxylate functional crosslinker, or an isocyanate functional crosslinker.
4. The coating composition according to claim 3 , wherein the curing agent is (1) an amino compound that is hexamethoxymethylmelamine, or (2) an epoxyfunctional compound that is bisphenol-A-diglycidyl ether or triglycidylisocyanurate.
5. The method according to claim 1 , wherein the curing agent is an epoxy functional compound, a phenolic functional crosslinker, a hydroxyl functional crosslinker, an amine functional crosslinker, a carboxylate functional crosslinker, or an isocyanate functional crosslinker.
6. The method according to claim 5 , wherein the curing agent is (1) an amino compound that is hexamethoxymethylmelamine, or (2) an epoxy functional compound that is bisphenol-A-diglycidyl ether or triglycidylisocyanurate.
7. The method according to claim 1 , wherein the fatty acid derivative has a carbon chain length of not more than 22 carbon atoms.
8. The method according to claim 1 , wherein the substrate is a metal surface optionally pre-treated to be corrosion resistant and adhesive to the coating composition.
9. The method according to claim 8 , wherein the metal surface is steel.
10. A solid substrate having a coating produced according to the method of claim 1 .
11. The method according to claim 1 , wherein the fatty acid derivative is (1) a monofunctional alkyl ester that is methyl, or (2) a polyfunctional alkyl ester that is glycerol ester.
12. The method according to claim 1 , wherein the liquid coating composition is cured by heat activation at a temperature of 200° C. to 300° C. and for a time of 37 seconds to 5 minutes.
13. The method according to claim 1 , wherein the liquid coating composition is cured by heat activation at a maximum substrate temperature of 240° C.
14. A non-aqueous liquid coating composition that can cure by heat activation, said non-aqueous liquid coating composition comprising:
a polyfunctional resin, a fatty acid derivative that is an acyl-group containing monofunctional or polyfunctional alkyl esters, a catalyst, optionally a curing agent and optionally one or more additives,
wherein the polyfunctional resin comprises functional groups that react with acyl groups of the fatty acid derivative.
15. The coating composition of claim 14 , wherein the polyfunctional resin is an alkyd, polyester, polyacrylate, polymethacrylate, phenolic or amino resin.
16. The coating composition according to claim 15 , wherein the curing agent is an epoxy functional compound, a phenolic functional crosslinker, a hydroxyl functional crosslinker, an amine functional crosslinker, a carboxylate functional crosslinker, or an isocyanate functional crosslinker.
17. The coating composition according to claim 16 , wherein the curing agent is (1) an amino compound that is hexamethoxymethylmelamine, or (2) an epoxyfunctional compound that is bisphenol-A-diglycidyl ether or triglycidylisocyanurate.
18. The coating composition according to claim 14 , wherein the curing agent is an epoxy functional compound, a phenolic functional crosslinker, a hydroxyl functional crosslinker, an amine functional crosslinker, a carboxylate functional crosslinker, or an isocyanate functional crosslinker.
19. The coating composition according to claim 18 , wherein the curing agent is (1) an amino compound that is hexamethoxymethylmelamine, or (2) an epoxy functional compound that is bisphenol-A-diglycidyl ether or triglycidylisocyanurate.
20. The coating composition according to claim 14 , wherein the fatty acid derivative has a carbon chain length of not more than 22 carbon atoms.
21. The coating composition according to claim 14 , wherein the fatty acid derivative is (1) a monofunctional alkyl ester that is methyl, or (2) a polyfunctional alkyl ester that is glycerol ester.
22. The coating composition according to claim 14 , capable of being cured thermally at a temperature of 200° C. to 300° C. and for a time of 37 seconds to 5 minutes.
23. The coating composition according to claim 14 , capable of being cured thermally at a maximum substrate temperature of 240° C.