Method for the production of profiles of a light metal material by means of extrusion
A method, for the production of profiles ( 16 ) of a light metal material, in particular a magnesium material, by means of extrusion with a hydrostatic extrusion device ( 10 ), is disclosed. A volume of material ( 15 ) is pressed through a die ( 14 ), having the form of the desired profile ( 16 ) in order to form the profile ( 16 ). A grain refiner is added to the light metal material to form the material volume ( 15 ) used in the extrusion process.
1. A method for producing a profile of a magnesium-based material comprising:
(a) adding a grain refiner comprising a metal of the rare earths to a magnesium-based material in a first step; and
(b) hydrostatically extruding the grain refiner and magnesium-based material through a die at a material temperature of 150° C. to less than 300° C. and a press ratio from 200 to 500 to produce a profile of the magnesium material.
2. The method of claim 1 , wherein the extruder has a press speed of more than 125 m/min to 250 m/min.
3. Method according to claim 1 , characterised in that the extrusion is effected by means of a hydrostatic press method.
4. Method according to claim 1 , characterised in that the extrusion is effected by means of a hydrostatic press method.
5. Method according to claim 2 , characterised in that the extrusion is effected by means of a hydrostatic press method.