PVC plastisols comprising effect pigments, their preparation and use in coil coating
Disclosed herein are effect pigment PVC plastisol, uses thereof, and proceses for producing effect pigment PVC plastisol. In one embodiment, an effect pigment PVC plastisol comprises: (A) at least one finely divided PVC homopolymer having particle sizes of from 0.04 to 40 μm, and which as a dispersion in a plasticizer exhibits dilatancy, (B) at least one finely divided PVC homopolymer having particle sizes of from 1 to 400 μm, and which as a dispersion in a plasticizer exhibits pseudoplasticity, (C) at least one plasticizer, and (D) at least one effect pigment.
1. An effect pigment PVC plastisol comprising
(A) at least one finely divided PVC homopolymer, prepared by emulsion polymerization or microemulsion polymerization, having particle sizes of from 0.04 to 40 μm, and which as a dispersion in a plasticizer exhibits dilatancy,
(B) at least one finely divided PVC homopolymer, prepared by emulsion polymerization, having particle sizes of from 1 to 400 μm, and which as a dispersion in a plasticizer exhibits pseudoplasticity,
(C) at least one plasticizer,
(D) at least one effect pigment, and
(F) at least one additive,
wherein the at least one additive (F) comprises an organic solvent, and the weight ratio (A):(B) is chosen so that the PVC plastisol exhibits pseudoplasticity.
2. The PVC plastisol as claimed in claim 1 , comprising at least one pigment (E) different than effect pigment (D).
3. The PVC plastisol as claimed in claim 1 , comprising from 20 to 60% by weight, based on PVC plastisol, of finely divided PVC homopolymer (A).
4. The PVC plastisol as claimed in claim 1 , comprising from 5 to 30% by weight, based on PVC plastisol, of finely divided PVC homopolymer (B).
5. The PVC plastisol as claimed in claim 1 , wherein (A):(B)=5:1 to 1:5.
6. The PVC plastisol, as claimed in claim 1 comprising from 10 to 60% by weight, based on PVC plastisol, of plasticizers (C).
7. The PVC plastisol as claimed in claim 1 , wherein the effect pigments (D) are selected from the group consisting of organic pigments, inorganic pigments, optical effect pigments, color effect and optical effect pigments, magnetically shielding pigments, electrically conductive pigments, anticorrosion pigments, fluorescent pigments, and phosphorescent pigments.
8. The PVC plastisol as claimed in claim 7 , wherein the effect pigments (D) are selected from the group consisting of organic pigments, inorganic pigments, optical effect pigments, and color effect and optical effect pigments.
9. The PVC plastisol as claimed in claim 8 , wherein the effect pigments (D) are selected from the group consisting of metal effect pigments, and effect pigments composed of metals and nonmetals.
10. The PVC plastisol as claimed in claim 2 wherein the pigments (E) are selected from the group consisting of organic pigments, inorganic pigments, color pigments, extender pigments, pigments which combine at least two of these properties, and nanoparticles.
11. The PVC plastisol as claimed in claim 1 , wherein additives (F) are selected from the group consisting of PVC stabilizers, light stabilizers, organic solvents, and synergists for halogen flame retardants.
12. A process for producing an effect pigment PVC plastisol comprising effect pigments as claimed in claims 1 or 2 , which comprises mixing its constituents (A), (B), (C), (D), and (F); or (A), (B), (C), (D), (E), and (F); and homogenizing the resulting mixture.
13. The PVC plastisol as claimed in claim 8 , wherein the effect pigments (D) comprise nonmetallic effect pigments.
14. A method of producing an effect coating comprising applying the PVC plastisol of claim 1 onto a metal strip, and thermally curing the PVC plastisol.
15. The PVC plastisol as claimed in claim 1 , wherein the plasticizer comprises a phenolic ester.
16. The PVC plastisol as claimed in claim 1 , wherein the plasticizer comprises a phenolic ester, an adipic ester, and a butyric ester.
17. An effect pigment PVC plastisol comprising
(A) at least one finely divided PVC homopolymer prepared by emulsion polymerization or microemulsion polymerization having particle sizes of from 0. 04 to 40 μm, and which as a dispersion in a plasticizer exhibits dilatancy,
(B) at least one finely divided PVC homopolymer prepared by emulsion polymerization, having particle sizes of from 1 to 400 μm, and which as a dispersion in a plasticizer exhibits pseudoplasticity,
(C) at least one plasticizer, and
(D) at least one effect pigment,
wherein a coating formed from the PVC plastisol has a difference in L*, when measured at 15° and at 75°, of an absolute value of at least 41.3; a difference in a*, when measured at 15° and at 75°, of an absolute value of at least 15; and a difference in b*, when measured at 15° and at 75°, of an absolute value of at least 5.8.
18. A coil coating composition comprising the PVC plastisol of claim 1 .