Flame retarder, flame retardant resin composition and method of producing the flame retarder
A flame retardant resin composition is disclosed. An acrylonitrile-styrene based polymer, into which sulfonic acid groups and/or sulfonate groups have been introduced by sulfonating processing with a sulfonating agent containing less than 3 wt % of moisture, is contained in a resin to be made flame retardant, so that flame retardant properties will be conferred on the resin flame resistant.
1. A resin composition having flame retardant properties, the resin composition comprising:
a flame retarder in an amount from and including 0.001 to and including 30 wt %,
wherein,
the flame retarder includes an aromatic polymer containing monomer units having aromatic skeletons in a side chain ranging from and including 1 mol % to and including 100 mol %,
and sulfonic acid groups and/or sulfonate groups are introduced in an amount ranging from and including 0.10 mol % to and including 8 mol %.
2. The flame retarder according to claim 1 wherein a sulfonating agent is used and said sulfonating agent one or more selected from the group consisting of sulfuric anhydride, fuming sulfuric acid, chlorosulfonic acid and polyalkylbenzene sulfonic acid.
3. The flame retarder according to claim 1 wherein said aromatic polymer is redeemed resin originally produced for specified purposes and/or used up.
4. The flame retarder according to claim 1 wherein said aromatic polymer has an aromatic skeleton in a side chain and contains at least one or more of polystyrene, a styrene-butadiene copolymer (high impact polystyrene), an acrylonitrile-styrene copolymer, an acrylonitrile-butadiene-styrene copolymer, an acrylonitrile-chlorinated polyethylene-styrene resin, an acrylonitrile-styrene-acrylate copolymer, an acrylonitrile-ethylene-propylene rubber-styrene copolymer and an acrylonitrile-ethylene-propylene-diene-styrene resin.
5. The flame retarder according to claim 4 wherein said aromatic polymer has a weight average molecular weight ranging between 10,000 and 10,000,000.
6. A resin composition having flame retardant properties, the resin composition comprising:
a flame retarder in an amount from and including 0.001 to and including 30 wt %,
wherein,
the flame retarder includes an aromatic polymer containing monomer units having aromatic skeletons in a main chain ranging from and including 1 mol % to and including 100 mol %, and
sulfonic acid groups and/or sulfonate groups are introduced in an amount ranging between from and including 0.10 mol % to and including 8 mol %.
7. The resin composition according to claim 6 wherein said aromatic polymer is at least one or more of polycarbonate, polyphenylene oxide, polyethylene terephthalate, polybutylene terephthalate and polysulfone.
8. A resin composition comprising a flame retarder,
wherein,
the flame retarder is in an amount from and including 0.0001 to and including 30 wt %,
the flame retarder includes an aromatic polymer containing monomer units having aromatic skeletons in a side chain ranging from and including 1 mol % to and including 100 mol %, and
sulfonic acid groups and/or sulfonate groups are introduced in an amount ranging from and including 0.1 mol % to and including 8 mol % onto the aromatic polymer.
9. The resin composition according to claim 8 wherein a sulfonating agent is used and said sulfonating agent is one or more selected from the group consisting of sulfuric anhydride, fuming sulfuric acid, chlorosulfonic acid and polyalkylbenzene sulfonic acid.
10. The resin composition according to claim 8 wherein not less than 5 wt % of one or more of polycarbonate, an acrylonitrile-butadiene-styrene copolymer, polystyrene, an acrylonitrile-styrene copolymer, polyvinyl chloride, polyphenylene oxide, polyethylene terephthalate, polybutylene butylate, polysulfone, a thermoplastic elastomer, polybutadiene, polyisoprene, acrylonitrile-butadiene rubber and nylon is contained in the composition.
11. The resin composition according to claim 8 wherein said resin composition and/or said aromatic polymer is redeemed resin originally produced for specified purposes and/or used up.
12. The resin composition according to claim 8 further comprising a fluoro olefin resin as an anti-drip agent.
13. The resin composition according to claim 8 wherein said aromatic polymer has an aromatic skeleton in a side chain and contains at least one or more of polystyrene, a styrene-butadiene copolymer (high impact polystyrene), an acrylonitrile-styrene copolymer, an acrylonitrile-butadiene-styrene copolymer, an acrylonitrile-chlorinated polyethylene-styrene resin, an acrylonitrile-styrene-acrylate copolymer, an acrylonitrile-ethylene-propylene rubber-styrene copolymer and an acrylonitrile-ethylene-propylene-diene-styrene resin.
14. The resin composition according to claim 13 wherein said aromatic polymer has a weight average molecular weight ranging between 10,000 and 10,000,000.