Artificial stone material and method of manufacture thereof
View Patent ↗An artificial stone material having an improved natural stone appearance and texture is prepared from thermosetting resin, curing agent, microspheres and additives. The resin and curing agent are thoroughly mixed to form a catalyzed resin mixture. The microspheres are added to the catalyzed resin mixture and mixed to a viscosity of about 950×10 6 to about 1590×10 6 to form a catalyzed base material. The additives are worked into the catalyzed base material to provide a catalyzed stone mixture having a desired natural stone appearance. The catalyzed stone mixture is molded or applied to a surface at the point of use and allowed to cure to form the artificial stone material.
1. An artificial stone product comprising:
a cured thermoset resin;
about 8 percent to about 63 percent (by weight of thermoset resin) of microspheres homogeneously distributed within the thermoset resin; and
at least one member selected from dry temper color, dry mortar, dye, pigment, paint, wood ash, mica, stone particles and glass particles, the at least one member being non-homogeneously distributed in the resin;
wherein the artificial stone product has a density of 1.0 grams per cubic centimeter or less and an appearance characteristic of natural stone.
2. The artificial stone product of claim 1 wherein the cured resin is an polyester resin, and comprising about 22 percent to about 40 percent microspheres (by weight of resin), iron black dry temper color, light buff dry temper color and wood ash.
3. The artificial stone product of claim 1 comprising about 33 percent to about 40 percent microspheres (by weight of resin), iron black dry temper, light buff dry temper and wood ash, wherein the artificial stone material has the appearance of red-brown sandstone.
4. The artificial stone product of claim 1 having a specific gravity of less than 1.
5. An artificial stone product comprising:
a cured thermoset resin;
about 8 percent to about 63 percent (by weight of thermoset resin) of microspheres; and
at least one member selected from dry temper color, dry mortar, dye, pigment, paint, wood ash, mica, stone particles and glass particles, the at least one member being non-homogeneously distributed in the resin;
wherein the artificial stone product has a density of 1.0 grams per cubic centimeter or less and an appearance characteristic of natural stone and the thermoset resin in a catalyzed state when mixed with the microspheres has a viscosity of about 950×10 6 cps to about 1590×10 6 cps.
6. An artificial stone material produced by a process comprising:
providing a point of use;
adding a curing agent to a thermoset resin to form a catalyzed resin mixture in the vicinity of the point of use;
adding about 8 percent to about 63 percent (by weight of catalyzed resin mixture) of microspheres to the catalyzed resin mixture;
slowly mixing the microspheres and the catalyzed resin mixture to form a catalyzed base material having a viscosity of about 950×10 6 cps to about 1590×10 6 cps to form a catalyzed base material;
adding at least one additive to the catalyzed base material; and
lightly mixing the additive and catalyzed base material to form a catalyzed artificial stone mixture, wherein the additive is non-homogeneously distributed in the catalyzed artificial stone mixture and the artificial stone material closely approximates the look of natural stone.
7. The artificial stone product of claim 6 wherein the thermoset resin is an orthophthalate polyester resin, and comprising about 28 percent to about 39 percent microspheres (by weight of resin), iron black dry temper, light buff dry temper and wood ash, wherein the artificial stone material has the appearance of natural grey field stone.
8. The artificial stone product of claim 6 comprising about 33 percent to about 40 percent microspheres (by weight of resin), iron black dry temper, light buff dry temper and wood ash, wherein the artificial stone material has the appearance of red-brown sandstone.
9. The artificial stone material of claim 6 wherein the catalyzed artificial stone mixture has randomly oriented veins of additives.
10. The artificial stone material of claim 6 wherein the catalyzed base material is a substantially homogeneous mixture of microspheres and catalyzed resin.