Prefabricated membrane based on modified polyurethane bituminous binder and process for production
The present invention has for its object a prefabricated sealing membrane formed by a support, coated on at least one surface, and preferably impregnated throughout, with a modified bitumen base composition, characterized in that the thermoplastic bituminous composition for coating and/or impregnation is a bituminous binder modified by a thermoplastic polyurethane having the following weight proportion: 40 to 90% bitumen, 10 to 50% thermoplastic polyurethane, 0 to 10% aromatic oil, 0 to 50% filler, 0 to 0.5% catalyst.
1. A prefabricated sealing membrane, having high stability to UV exposure and formed of a support or reinforcement, the support or reinforcement being one of coated on at least one surface and impregnated throughout, with a modified bitumen base composition, characterized in that the thermoplastic bituminous coating and or impregnation composition is a bituminous binder modified by a thermoplastic polyurethane having the following weight proportion:
60 to 80% bitumen,
15 to 40% thermoplastic polyurethane,
0 to 5% aromatic oil,
0 to 40% filler,
0 to 0.5% catalyst,
the modified bituminous binder adapted to be softened by reheating and recover its properties after subsequent cooling,
the prefabricated membrane being adapted for application by heating by torch welding or hot air,
the prefabricated sealing membrane highly stable to UV exposure, wherein
the thermoplastic polyurethane is obtained from a diisocyanate of a functionality substantially equal to 2, a polyol of functionality substantially equal to 2, and a chain elongation agent,
the polyurethane molecules are free of double carbon-carbon bonds, and
the polyols are free of ethylene linkages.
2. The membrane according to claim 1 , characterized in that the bituminous composition has the following weight proportion:
60 to 80% bitumen,
20 to 30% thermoplastic polyurethane,
0 to 2% aromatic oil,
10 to 20% filler,
0 to 0.2% catalyst.
3. The membrane according to claim 1 , characterized in that the bituminous composition contains also between 0.01 and 20% by weight of one or several additives improving adhesion, resistance to fire or to flames and/or resistance to roots, of said composition.
4. The membrane according to claim 1 , characterized in that the thermoplastic polyurethane is constituted by a quantity of hard segments comprised between 10 and 40%.
5. The membrane according to claim 1 , characterized in that the material or materials forming the filler is or are selected from the group of mineral fillers formed by chalk, silica, talc, dolomite, kaolin and mixtures of two or several of these substances.
6. The membrane of claim 1 , wherein,
the support or reinforcement comprises plural fibrous backings impregnated throughout.
7. The membrane of claim 1 , wherein,
the support or reinforcement comprises a coated fibrous backing.
8. The membrane of claim 1 , wherein,
the functionality of the polyols is between 1.95 and 2.05, and
the functionality of the isocyanates is between 2.0 and 2.1.
9. The membrane of claim 8 , wherein a ratio of isocyanate/polyol is between 1.0 and 1.1.
10. The membrane of claim 1 , wherein a ratio of isocyanate/polyol is about 1.05.
11. A prefabricated sealing membrane having high stability, to UV exposure, comprising:
a support in the form of a fibrous backing; and
a modified bitumen base composition applied to a surface of the support or impregnated throughout the support,
the modified bitumen base composition comprising
60 to 80% bitumen,
15 to 40% thermoplastic polyurethane,
0 to 5% aromatic oil,
0 to 40% filler, and
0 to 0.5% catalyst,
the modified bituminous base composition being thermoplastic, softening under action of heat and recovering its properties after subsequent cooling, and
the prefabricated sealing membrane being adapted for application by torch welding or hot air and highly stable to UV exposure, wherein,
the thermoplastic polyurethane comprises a diisocyanate, a polyol, and a chain lengthening agent,
the thermoplastic polyurethane molecules are free of double carbon-carbon bonds,
the polyols are free of ethylene linkages,
the functionality of the polyols is between 1.95 and 2.05, and
the functionality of the isocyanates is between 2.0 and 2.1.
12. The membrane of claim 11 , wherein a ratio of isocyanate/polyol is between 1.0 and 1.1.
13. The membrane of claim 11 , wherein a ratio of isocyanate/polyol is about 1.05.
14. The membrane of claim 11 , wherein the modified bitumen base composition comprises 20 to 30% thermoplastic polyurethane.
15. A prefabricated sealing membrane having high stability to UV exposure, comprising:
a support; and
a modified bitumen base composition applied to the support,
the modified bitumen base composition comprising
60 to 80% bitumen,
15 to 40% thermoplastic polyurethane, comprising a diisocyanate, a polyol, and a chain lengthening agent,
0 to 5% aromatic oil,
0 to 40% filler, and
0 to 0.5% catalyst,
the modified bituminous base composition being thermoplastic, softening under action of heat and recovering its properties after subsequent cooling so that the prefabricated sealing membrane is suitable for application by torch welding or hot air, and
the prefabricated sealing membrane being highly stable to UV exposure, wherein,
the thermoplastic polyurethane molecules are free of double carbon-carbon bonds,
the isocyanate and polyol are present in a ratio of isocyanate/polyol is between 1.0 and 1.1,
the polyols are free of ethylene linkages, and
the functionality of the polyols is between 1.95 and 2.05.