Charge dissipation modifiers for olefinic interpolymer compositions
Olefinic interpolymer compositions comprising the olefinic interpolymer, residuals from a transition metal catalyst and boron containing activator package, and a charge dissipation modifier and methods for making them. The compositions have dissipation factors that are at least 50% less than the corresponding olefinic interpolymer compositions which have not been treated with charge dissipation modifiers. The compositions are useful in wire and cable applications.
1. An olefinic interpolymer composition comprising:
a. an olefinic interpolymer or a mixture of olefinic interpolymers each comprising at least one C 2 –C 20 α-olefin monomer, optionally comprising at least one polyene;
b. post-polymerization reactor residuals of at least one transition metal catalyst and a boron containing activator package; and
c. at least one charge dissipation modifier selected from the group consisting of:
i) amine compounds of the general formula (I) and (II):
NR x (I)
wherein x is 3 and each R is independently selected from linear, branched and cyclic hydrocarbyl groups and hydrogen or together two or more R substituents are a cyclic hydrocarbyl group and each R 1-5 is independently selected from linear, branched and cyclic hydrocarbyl groups and hydrogen or together two or more of the R 1-5 substituents are a cyclic hydrocarbyl group;
ii) silica compounds; and
iii) phosphoric acid;
and mixtures thereof,
wherein the olefinic interpolymer composition has a dissipation factor which is at least 50% lower than the dissipation factor of the same olefinic interpolymer composition which has not been treated with a charge dissipation modifier.
2. The olefinic interpolymer composition of claim 1 in which the charge dissipation modifier is selected from the group consisting of aniline, isopropylamine, pyridine, and N,N-octadecyl methyl amine.
3. The olefinic interpolymer composition of claim 1 in which the charge dissipation modifier is N,N-octadecyl methyl amine.
4. The olefinic interpolymer composition of claim 1 in which the charge dissipation modifier is a silica compound.
5. The olefinic interpolymer composition of claim 1 in which the charge dissipation modifier is phosphoric acid.
6. The olefinic interpolymer composition of claim 1 in which at least one α-olefin monomer is selected from the group consisting of ethylene, propylene, 1-butene, 1-hexene, 1-octene, and 4-methyl-1-pentene.
7. The olefinic interpolymer composition of claim 1 in which at least one olefinic interpolymer comprises two α-olefin monomers.
8. The olefinic interpolymer composition of claim 7 in which the α-olefin monomers are ethylene and octene.
9. The olefinic interpolymer composition of claim 7 in which the α-olefin monomers are ethylene and butene.
10. The olefinic interpolymer composition of claim 6 comprising a mixture of olefinic interpolymers each comprising two or three α-olefin monomers selected from ethylene, propylene, butene and octene.
11. The olefinic interpolymer composition of claim 1 in which at least one olefinic interpolymer comprises at least one polyene.
12. The olefinic interpolymer composition of claim 11 in which each polyene is selected from 5-ethylidene-2-norbornene and 5-vinyl-2-norbornene.
13. The olefinic interpolymer composition of any of claims 1 – 11 wherein the composition has a dissipation factor of about 0.10 or less.
14. A process for lowering the dissipation factor of an olefinic interpolymer composition comprising:
a. contacting an interpolymer composition-solvent solution comprising an olefinic interpolymer or mixture of olefinic interpolymers, post-polymerization reactor residuals of at least one transition metal catalyst and a boron containing activator package all dissolved in a solvent with a charge dissipation modifier selected from the group consisting of:
i) amine compounds of the general formula (I) and (II):
NR x (I)
wherein x is 3 and each R is independently selected from linear, branched and cyclic hydrocarbyl groups and hydrogen or together two or more R substituents are a cyclic hydrocarbyl group and each R 1-5 is independently selected from linear, branched and cyclic hydrocarbyl groups and hydrogen or together two or more of the R 1-5 substituents are a cyclic hydrocarbyl group;
ii) silica compounds; and
iii) phosphoric acid; and mixtures thereof, and
b. isolating the treated interpolymer composition.
15. A process for lowering the dissipation factor of a solid olefinic interpolymer composition comprising an olefinic interpolymer or mixture of olefinic interpolymers, post-polymerization reactor residuals of at least one transition metal catalyst and a boron containing activator package, the process comprising:
a. heating the olefinic interpolymer composition into a melt state;
b. contacting the olefinic interpolymer composition with a charge dissipation modifier selected from:
i) amine compounds of the general formula (I) and (II):
NR x (I)
wherein x is 3 and each R is independently selected from linear, branched and cyclic hydrocarbyl groups and hydrogen or together two or more R substituents are a cyclic hydrocarbyl group and each R 1-5 is independently selected from linear, branched and cyclic hydrocarbyl groups and hydrogen or together two or more of the R 1-5 substituents are a cyclic hydrocarbyl group;
ii) silica compounds; and
iii) phosphoric acid; and mixtures thereof;
c. allowing the charge dissipation modifier to physically interact with the catalyst and activator residuals sufficiently to modify the dissipation factor; and
d. recovering the treated interpolymer composition.
16. An olefinic interpolymer composition prepared by the process of claim 14 or claim 15 .
17. A cable comprising an electrical conductor and an electrically insulative olefinic interpolymer composition of any one of claims 1 – 12 .