System and method for fabricating three-dimensional objects using solid free-form fabrication
View Patent ↗A method for solid free-form fabrication of a three-dimensional object includes depositing a particulate blend in a defined region, the particulate blend including a calcium phosphate source, a reaction retardant, and a layered double hydroxide, and selectively ink-jetting a solubilizing binder onto a predetermined volume of the particulate blend to form a pre-ceramic object in the predetermined volume, wherein the solubilizing binder includes wetting agents, humectants, pH modifiers, and surfactants.
1. A solid three-dimensional prototype composition, comprising:
multiple layers of pre-ceramic deposited in contact with one another, each of said multiple layers of pre-ceramic comprising a particulate blend including a calcium phosphate source;
wherein said particulate blend was hydrated by a solubilizing binder to produce said pre-ceramic;
wherein said particulate blend comprises:
tetracalcium phosphate;
citric acid;
CaAl-LDH (NO 3 );
poly acrylic acid (60k);
Li 3 PO 4 ; and
magnesium fluoride.
2. The composition of claim 1 , wherein said pre-ceramic has a compression modulus of 0.05 Giga-Pascal.
3. The composition of claim 1 , wherein said pre-ceramic is configured to produce a ceramic upon firing.
4. The composition of claim 3 , wherein said ceramic is configured to have a compression modulus over 14.0 Giga-Pascal.
5. The composition of claim 1 , wherein said layers of pre-ceramic are disposed at edges of layers of said particulate blend so as to form a shell around a quantity of said particulate blend corresponding to a shape of an object being formed.
6. The composition of claim 1 , wherein said solubilizing binder comprises a humectant or a surfactant.
7. A composition for forming a solid three-dimensional prototype, said composition comprising:
a particulate blend including a calcium phosphate source from which pre-ceramic layers of an object being fabricated are formed, wherein said particulate blend comprises:
tetracalcium phosphate;
citric acid;
CaAl-LDH (NO 3 );
polyacrylic acid (60k);
Li 3 PO 4 ; and
magnesium fluoride; and
a solubilizing binder for selective introduction into said particulate blend, wherein said binder is configured to dissolve calcium phosphate of said calcium phosphate source, with reprecipitation of said calcium phosphate producing said pre-ceramic.
8. A composition for forming a solid three-dimensional prototype, said composition comprising:
a particulate blend including a calcium phosphate source from which pre-ceramic layers of an object being fabricated are formed, wherein said solubilizing binder comprises:
phosphoric acid (H 3 PO 4 );
2-pyrrolidone;
liponic ethylene glycol (LEG-1);
SURFYNOL 465;
water;
1,5-pentanediol; and
TERGITOL-15-s-7; and
a solubilizing binder for selective introduction into said particulate blend, wherein said binder is configured to dissolve calcium phosphate of said calcium phosphate source, with reprecipitation of said calcium phosphate producing said pre-ceramic.
9. The composition of claim 7 , wherein said binder comprises a pH modifier.
10. The composition of claim 9 , wherein said pH modifier comprises one of a phosphoric acid (H 3 PO 4 ), a mineral acid, a phytic acid, an acetic acid, an ethanoic acid, a potassium hydroxide (KOH), a lithium hydroxide (LiOH), a sodium hydroxide (NaOH), a NH 4 OH, an aluminum hydroxide (Al(OH) 3 ), a magnesium hydroxide (Mg(OH) 2 ), a a calcium hydroxide (Ca(OH) 2 ), or a barium hydroxide (Ba(OH) 2 ).
11. The composition of claim 8 , wherein said binder comprises a pH modifier.
12. The composition of claim 11 , wherein said pH modifier comprises one of a phosphoric acid (H 3 PO 4 ), a mineral acid, a phytic acid, an acetic acid, an ethanoic acid, a potassium hydroxide (KOH), a lithium hydroxide (LiOH), a sodium hydroxide (NaOH), a NH 4 OH, an aluminum hydroxide (Al(OH) 3 ), a magnesium hydroxide (Mg(OH) 2 ), a calcium hydroxide (Ca(OH) 2 ), or a barium hydroxide (Ba(OH) 2 ).