Method of making polarizable electrode for electric double layer capacitor
View Patent ↗A method of making a polarizable electrode for an electric double layer capacitor, includes adding a binder assistant to a binder so that the binder is swollen and mixing a carbonaceous powder, a conductive assistant and thereafter the swollen binder, thereby obtaining a material mixture, kneading the material mixture into a primary forming material, forming the primary forming material into a secondary forming material, and rolling the secondary forming material into a sheet shape.
1. A method of making a polarizable electrode for an electric double layer capacitor, comprising:
a mixing step including a primary mixing in which a carbonaceous powder and a conductive assistant are mixed into a primary mixture, and a secondary mixing in which a binder and a binder assistant added to the binder before the secondary mixing so that the binder is swollen are added to the primary mixture so that the carbonaceous powder, the conductive assistant, the binder and the binder assistant are mixed into a material mixture;
a kneading step in which the material mixture is kneaded into a clayey forming material;
a forming step in which the clayey forming material is formed into fine grain thereafter into a sheet of forming material; and
a rolling step in which the sheet of forming material is rolled into a thinner sheet shape.
2. A method according to claim 1 , wherein the binder assistant is added to the clayey forming material and mixed immediately before the forming step of forming the fine grain forming material into the sheet of forming material.
3. A method according to claim 2 , wherein an amount of the binder assistant added to the fine grain of forming material ranges from 50 to 100% of a sum total mass of the carbonaceous powder, the conductive assistant and the binder.
4. A method according to claim 2 , wherein an amount of the binder assistant added to the binder in the mixing ranges from 70 to 130% of a mass of the binder, and an amount of the binder assistant added to the fine grain of forming material ranges from 50 to 100% of a sum total mass of the carbonaceous powder, the conductive assistant and the binder.
5. A method according to claim 2 , wherein the fine grain of forming material added with the binder assistant is mixed in a closed container.
6. A method according to claim 1 , wherein an amount of the binder assistant added to the binder in the mixing ranges from 70 to 130% of a mass of the binder.
7. A method according to claim 1 , wherein the material mixture is kneaded by a kneader, and the kneader includes a portion with which the material mixture is brought into contact during the kneading, and the material mixture is kneaded while a temperature of the portion of the kneader is controlled.