Process for producing hollow comprising fiber-reinforced ceramic materials
A process for producing hollow bodies comprising fiber-reinforced ceramic materials, in which a green body comprising compressible cores and a mouldable composition comprising binders and fiber material which is pressed with compression of the core is produced, the green body is cured and carbonized and pyrolysed by heating in a nonoxidizing atmosphere and, if desired, the body is silicized, hollow bodies produced in this way and their use, in particular as brake and clutch disks
1. A process for producing hollow bodies comprising fiber-reinforced ceramic materials, which comprises
in a first step, producing compressible cores whose shape corresponds, at least in the plane perpendicular to the pressing direction, essentially to the geometry of the hollow spaces to be formed,
in a second step producing a green body by introducing the said compressible cores and a mouldable composition comprising binder and fiber material into a mould,
in a third step, pressing the composition containing fiber material with a pressure of from 0.1 MPa to 50 MPa so that the core is compressed in the pressing direction by at least 5% of its dimension in the pressing direction, which cores have at least three layers in the pressing direction of the third step, where the compressibility of directly adjacent layers differs for these said layers, and the compressibility of, the outermost layer is at least twice that of the inner layer, wherein the outer layers are made of foamed polymers and wherein the inner layer is made of thermoplastic materials which thermoplastic materials have a heat distortion temperature of at least 150° C., and a ball indentation hardness of at least 30 MPa, the thickness of the outer layers being from 10% to 40% of the total thickness of the core in the pressing direction for each of the outer layers, and from 20% to 80% of the total thickness in the pressing direction for the inner layer,
in a fourth step, curing the composition comprising fiber material to form a cured green body,
in a fifth step carbonizing the cured green body by heating to a temperature of from about 750° C. to about 1100° C. in a nonoxidizing atmosphere to produce a C/C body,
where the cores consist of material which pyrolyses in the fifth step or is at least partially pyrolysed with volume shrinkage, wherein during pressing, the outer layers are compressed to from 1/10 to 1/200 of their original thickness.
2. The process as claimed in claim 1 , wherein, subsequent to the fifth step,
the C/C body is in a sixth step infiltrated with a liquid metal with retention of its shape and with an at least partial reaction of the carbon component of the matrix of the C/C body with the metal occurring to form carbides.
3. The process as claimed in claim 1 , wherein
in the fourth step the composition comprising fiber material is cured by heating to a temperature of from 120° C. to 280° C.
4. The process as claimed in claim 1 , wherein the third and fourth steps are carried out simultaneously or partly overlapping in time.
5. A process for producing hollow bodies comprising fiber-reinforced ceramic materials, which comprises
in a first step, producing compressible cores whose shape corresponds, at least in the plane perpendicular to the pressing direction, essentially to the geometry of the hollow spaces to be formed,
in a second step producing, a green body by introducing the said compressible cores and a mouldable composition comprising binder and fiber material into a mould,
in a third step, pressing the composition containing fiber material with a pressure of from 0.1 MPa to 50 MPa so that the core is compressed in the pressing direction by at least 5% of its dimension in the pressing direction, wherein the cores have three layers in the pressing direction of the third step, where the compressibility of directly adiacent layers differs for these said layers, and the compressibility of the outermost layers is at least twice that of the inner layer, wherein the outer layers are made of foamed polymers and wherein the inner layer is made of thermoplastic materials which thermoplastic materials have a melting point in the range of 220° C. to 280° C., a heat distortion temperature of at least 150° C., and a ball indentation hardness of at least 30 MPa, and the thicknesses of the
outer layers are each from 15% to 35% of the total thickness of the core in the pressing direction, and the thickness of the inner layer is from 30% to 70% of the total thickness of the core in the pressing direction,
in a fourth step, curing the composition comprising fiber material to form a cured green body,
in a fifth step carbonizing the cured green body by heating to a temperature of from about 750° C. to about 1100° C. in a nonoxidizing atmosphere to produce a C/C body,
where the cores consist of material which pyrolyses in the fifth step or is at least partially pyrolysed with volume shrinkage, wherein during pressing, the outer layers are compressed to from 1/10 to 1/200 of their original thicknesses.
6. The process as claimed in claim 1 , wherein the compressible outer layers are compressed to from 1/12 to 1/100 of their original thickness during pressing.
7. The process as claimed in claim 1 , wherein the outer layers of the cores are melted during pressing.
8. The process as claimed in claim 1 wherein the hollow body is in the form of an annular disk in which at least one hollow space extends from the periphery to the inner edge of the annular disk.
9. The process of claim 5 , wherein, subsequent to the fifth step,
the C/C body is in a sixth step infiltrated with a liquid metal with retention of its shape and with an at least partial reaction of the carbon component of the matrix of the C/C body with the metal occurring to form carbides.