Method for producing individually dosed active substance-containing and, in particular, aromatics-containing film-shaped administration forms rapidly disintegrating upon contact with liquid
A method for producing individually dosed active substance-containing and, in particular, aromatic-containing, film-shaped administration form, rapidly disintegrating upon contact with a liquid, wherein the aromatic is present as an internal, liposoluble phase in the form of liquid droplets distributed within an outer, solid but water-soluble phase, is characterized in that the said outer phase contains: at least 40% (w/w) polyvinyl alcohol 0 to 30% (w/w), of a surface-active substance, and that the constituent amount of the inner phase, relative to the outer phase, is between 0.1 and 30% (w/w), in each case relative to the water-free portions.
1. A method for producing a dried film which disintegrates upon contact with saliva or water, said film comprising an inner phase of liposoluble liquid droplets of flavors and fragrances and a solid, water soluble outer phase containing at least 40% (w/v) polyvinyl alcohol, wherein both of said phases are water-free, said droplets being distributed within said water-free outer, solid, water-soluble phase, the size of said liquid droplets being in the range from 1 μm to 100 μm, said method comprising the steps of:
a) dissolving a polyvinyl alcohol in water to obtain a polyvinyl alcohol solution;
b) adjusting the temperature of the solution to below 40° C., and then generating said liquid droplets by adding, while stirring, at least one member of the group consisting of liposoluble flavors and fragrances in liquid form in an amount between 0.1 and 30 wt.-% relative to the water-free portion of the outer phase to the polyvinyl alcohol solution, and adjusting the size of the liquid droplets within the range of 1 μm to 100 μm by adding a surfactant to the outer phase, said surfactant being added at a concentration of up to 30%-wt. relative to the the outer phase, said solution becoming a liquid mass;
c) coating said liquid mass onto a carrier;
d) drying said liquid mass to obtain said dried film; and
e) separating the film from said carrier;
wherein said liposoluble flavors and fragrances are selected from the group consisting of ethereal oils and volatile odoriferous or flavoring substances having a limited miscibility with water.
2. The method according to claim 1 , wherein the amount of said at least one member of the group consisting of flavors and fragrances is between 1 and 5 wt.-% relative to the water-free portion of the outer phase.
3. The method according to claim 1 , wherein the liquid mass is coated in a layer thickness of between 200 and 300 μm.
4. The method according to claim 1 , wherein the drying step of said liquid mass is performed below 80° C.
5. The method according to claim 1 , further comprising the step of adding at least one substance selected from the group consisting of fillers, aroma-enhancing substances, sweeteners, salt, sugar derivatives, low-molecular organic acids, plasticizing additives, pigments, and light-scattering additives to the liquid mass.
6. The method according to claim 1 , wherein said drying step comprises drying in a canal dryer at increasing temperatures not exceeding 80° C.
7. The method according to claim 1 , wherein said drying step comprises the steps of drying the coated liquid mass initially at room temperature, and subsequently drying the coated liquid mass at 50° C.
8. The method according claim 1 , further comprising a step of equilibrating the dried product obtained in step (d) with 60% relative humidity for 24 hours.
9. The method according to claim 1 , wherein said carrier is selected from the group consisting of a film material and a metal roller.
10. The method according to claim 9 , wherein said film material is a polyethylene terephthalate film.
11. The method according to claim 1 , wherein the obtained products have a thickness of between 20 and 300 μm and a size ranging from 0.5 to 8 cm 2 .
12. The method according to claim 1 , wherein said polyvinyl alcohol is in a partially hydrolized form having between 1 and 20% of the hydroxyl groups replaced with acetyl groups.
13. The method according to claim 12 , wherein 12% of the hydroxyl groups are replaced by acetyl groups.
14. The method according to claim 1 , further comprising a step of adding polyethylene glycol to said solution.
15. A method for producing a dried film which disintegrates upon contact with saliva or water, said film comprising an inner phase of liposoluble liquid droplets of flavors and fragrances and a solid, water soluble outer phase containing at least 40% (w/v) polyvinyl alcohol, wherein both of said phases are water-free, said droplets being distributed within said water-free outer, solid, water-soluble phase, the size of said liquid droplets being in the range from 1 μm to 100 μm, said method comprising the steps of:
a) dissolving a polyvinyl alcohol in water to obtain a polyvinyl alcohol solution;
b) adjusting the temperature of the solution to below 40° C., and then generating said liquid droplets by adding, while stirring, at least one member of the group consisting of liposoluble flavors and fragrances in liquid form in an amount between 0.1 and 30 wt.-% relative to the water-free portion of the outer phase to the polyvinyl alcohol solution, said surfactant being added at a concentration of up to 30%-wt. relative to the outer phase, said solution becoming a liquid mass;
c) coating said liquid mass onto a carrier;
d) drying said liquid mass to obtain said dried film; and
e) separating the film from said carrier;
wherein said liposoluble flavors and fragrances are selected from the group consisting of ethereal oils and volatile odoriferous or flavoring substances having a limited miscibility with water.