High-strength, high conductivity copper alloy excellent in fatigue and intermediate temperature properties
View Patent ↗The present invention provides a Cu—Cr—Zr alloy material excellent in fatigue and intermediate temperature characteristics, which comprises 0.05 to 1.0% by mass of Cr and 0.05 to 0.25% by mass of Zr with a balance of Cu and inevitable impurities. The alloy comprises inclusion particles based on any one of Zr and a Cu—Zr alloy having a diameter of 0.1 μm or more, and the proportion of the inclusion particles containing 10% or more of sulfur as one of the inevitable impurities is one particle/mm 2 .
1. A high-strength high-conductive copper alloy excellent in fatigue and intermediate temperature characteristics comprising 0.05 to 1.0% by mass of Cr and 0.05 to 0.25% by mass of Zr with a balance of Cu and inevitable impurities,
the alloy comprising inclusion particles based on any one of Zr and a Cu—Zr alloy having a diameter of 0.1 μm or more,
the proportion of the inclusion particles containing 10% or more of sulfur as one of the inevitable impurities being one particles/mm 2 .
2. A high-strength high-conductive copper alloy excellent in fatigue and intermediate temperature characteristics comprising 0.05 to 1.0% by mass of Cr, 0.05 to 0.25% by mass of Zr and 0.05 to 2.0% by mass of Zn with a balance of Cu and inevitable impurities,
the alloy comprising inclusion particles based on any one of Zr and a Cu—Zr alloy having a diameter of 0.1 μm or more,
the proportion of the inclusion particles containing 10% or more of sulfur as one of the inevitable impurities being one particles/mm 2 .
3. A high-strength high-conductive copper alloy excellent in fatigue and intermediate temperature characteristics comprising 0.05 to 1.0% by mass of Cr and 0.05 to 0.25% by mass of Zr with a balance of Cu and inevitable impurities,
the alloy comprising inclusion particles based on any one of Zr and a Cu—Zr alloy having a diameter of 0.1 μm or more,
the proportion of the inclusion particles containing sulfur as one of the inevitable impurities being 1,000 particles/mm 2 .
4. A high-strength high-conductive copper alloy excellent in fatigue and intermediate temperature characteristics comprising 0.05 to 1.0% by mass of Cr, 0.05 to 0.25% by mass of Zr and 0.05 to 2.0% by mass of Zn with a balance of Cu and inevitable impurities,
the alloy comprising inclusion particles based on any one of Zr and a Cu—Zr alloy having a diameter of 0.1 μm or more,
the proportion of the inclusion particles containing sulfur as one of the inevitable impurities being 1,000 particles/mm 2 .