Rust prevention coating agent and method of rust-proofing
A rust prevention coating agent which can be used even in uses requiring high corrosion-resistant performance because of having corrosion resistance superior to a conventional surface treatment agent, and is excellent in the adhesion to a coating film, and a method of rust-proofing using the same are provided. The prevention coating agent comprises a fluorine and zirconium-containing compound and certain guanidine compounds and/or salts thereof.
1. A rust prevention coating agent comprising a fluorine and zirconium-containing compound and a guanidine compound and/or salt thereof,
wherein said guanidine compound and/or salt thereof is a compound, having a weight-average molecular weight of 59 to 1000000, expressed by the following general formula (1) and/or salt thereof;
in the formula, Y represents the formula of —C(═NH)—NH—(CH 2 ) m —, —C(═O)—NH—(CH 2 ) m —, or —, —C(═S)—NH—(CH 2 ) m —, m is an integer of 0 to 20, n is a positive integer, k is 0 or 1, X represents hydrogen, an amino group, a hydroxyl group, a methyl group, a phenyl group, a chlorophenyl group or a methylphenyl group (tolyl group), and Z represents hydrogen, an amino group, a hydroxyl group, a methyl group, a phenyl group, a chlorophenyl group, a methylphenyl group (tolyl group) or a polymer, having a weight-average molecular weight of 200 to 1,000,000, being a polymer comprising, as a repeating unit, one of the polymerization groups represented by the following general formula (2);
in the formula, p is an integer
and wherein the guanidine compound and/or salt thereof has a biguanide structure represented by the following general formula (3) in a molecule thereof;
2. The rust prevention coating agent according to claim 1 ,
wherein the guanidine compound is at least one compound selected from the group consisting of 1-o-tolyl biguanide, polyhexamethylene biguanidine, polyhexaethylenebiguanidine, polypentamethylenebiguanidine, polypentaethylenebiguanidine, polyvinylbiguanidine, and polyallylbiguanidine.
3. The rust prevention coating agent according to claim 1 ,
which comprises the fluorine and zirconium-containing compound in a concentration of 10 to 10000 ppm and the guanidine compound and/or salt thereof of in a concentration of 1 to 10000 ppm and an effective fluorine ion concentration of 0.1 to 1000 ppm and has a pH of 1 to 5.
4. A method of rust-proofing aluminum and/or aluminum alloy comprising a step of treating a metal surface with a rust prevention coating agent,
wherein said rust prevention coating agent is the rust prevention coating agent according to claim 1 .
5. The rust prevention coating agent according to claim 2 ,
which comprises the fluorine and zirconium-containing compound in a concentration of 10 to 10000 ppm and the guanidine compound and/or salt thereof of in a concentration of 1 to 10000 ppm and an effective fluorine ion concentration of 0.1 to 1000 ppm and has a pH of 1 to 5.
6. A method of rust-proofing aluminum and/or aluminum alloy comprising a step of treating a metal surface with a rust prevention coating agent,
wherein said rust prevention coating agent is the rust prevention coating agent according to claim 2 .
7. A method of rust-proofing aluminum and/or aluminum alloy comprising a step of treating a metal surface with a rust prevention coating agent,
wherein said rust prevention coating agent is the rust prevention coating agent according to claim 3 .
8. A method of rust-proofing aluminum and/or aluminum alloy comprising a step of treating a metal surface with a rust prevention coating agent,
wherein said rest prevention coating agent is the rust prevention coating agent according to claim 5 .