Nanodisk sensor and sensor array
The invention provides a sensor array with different nanodisk sensors that may be fabricated by direct site-specific dip-pen nanopatterning (DPN) using precursor inks. The good flow characteristics and strong affinity of the sols to measurement electrodes enable intimate ohmic contact. The measurable, reproducible and proportionate changes in the resistance of the sensors when exposed to trace quantities of oxidative and reducing gases constitute the basis for nanodisk gas sensors. The nanodisk sensors show rapid response and ultra-fast recovery for the detection of nitrogen dioxide and acetic acid vapor. Based on the principles of pattern recognition of the olfactory system, an electronic nose that can “smell” different gaseous species is provided with the multiple nanodisk sensor array. These nanodisk sensors have gas recognition ability, instant response and rapid recovery, compact size and integration with the established microelectronics platform and are well-suited for the on-site and real-time detection of gases.
1. A sensor for temperature and gas detection comprising a sol gel nanodisk fabricated between conducting electrodes whereby the sol gel nanodisk comprises a semi-crystallized structure having surface oxygen ions.
2. The sensor of claim 1 , wherein the semi-crystallized structure comprises an inorganic molecule selected from the group consisting of SnO 2 , Ti—SnO 2 , Co—SnO 2 , Ni—SnO 2 , Cu—SnO 2 , Zn—SnO 2 , Cd—SnO 2 , Pt—SnO 2 , TiO 2 , ZrO 2 , ZnO, MgO, CaO, Li 2 O, B 2 O 3 , CO, CO 2 , SiO 2 , GeO 2 , N 2 O, NO, N 2 O 3 , NO 2 , N 2 O 5 , SO 2 , SO 3 , SeO 2 , SeO 3 , TeO 2 , TeO 3 , Cl 2 O, ClO 2 , Cl 2 O 7 , Br 2 O, BrO 2 , I 2 O 5 and I 2 O 7 .
3. The sensor of claim 1 , wherein the conducting electrodes are comprised of a metal.
4. The sensor of claim 1 , wherein the sensor is fabricated on an insulating substrate.
5. The sensor of claim 1 , wherein the sol gel nanodisk has a width of about 4 μM and a length of about 5 μM.
6. The sensor of claim 1 , wherein the sol gel nanodisk comprises an ionic surfactant.
7. The sensor of claim 1 , wherein the sol gel nanodisk comprises a nonionic surfactant.
8. The sensor of claim 1 , wherein the sol gel nanodisk comprises poly(ethyleneoxide)-b-poly(propyleneoxide)-b-poly(ethyleneoxide) copolymer.
9. A chemical sensor comprising at least two sol gel nanodisks fabricated between conducting electrodes on a single substrate.
10. A method of fabricating a nanodisk sensor comprising,
a. contacting a reservoir of a sol gel with a tip; and,
b. contacting the tip between electrodes on a surface to deposit a sol gel nanodisk in ohmic contact with the electrodes.
11. The method of claim 10 , comprising the additional step of contacting a second surface with the tip after contacting the reservoir of a sol gel and before contacting the surface between the electrodes.
12. The method of claim 10 , wherein the sol gel nanodisk comprises a compound selected from the group consisting of surfactant, solvent, metal and combinations thereof.
13. The method of claim 10 , wherein the sol gel nanodisk comprises copolymer poly(ethyleneoxide)-b-poly(propyleneoxide)-b-poly(ethyleneoxide), ethanol and tin chloride.
14. The method of claim 13 , wherein the sol gel nanodisk additionally comprises the ethanol-solvable salt of a metal selected from the group consisting of titanium, cobalt, nickel, copper, zinc, cadmium and platinum.
15. The method of claim 10 , wherein the tip is a microcantilever.
16. The method of claim 10 , comprising the additional step of fabricating the electrodes by photolithography and electron bean deposition on a surface prior to contacting the tip.
17. A sensor for temperature and gas detection fabricated by a method comprising,
a. contacting a reservoir of a sol gel with a tip; and,
b. contacting the tip between electrodes on a surface to deposit a sol gel nanodisk in ohmic contact with the electrodes.
18. The sensor of claim 17 , wherein the sol gel comprises a tin dioxide selected from the group consisting of SnO 2 , Ti—SnO 2 , CO—SnO 2 , Ni—SnO 2 , Cu—SnO 2 , Zn—SnO 2 , Cd—SnO 2 , Pt—SnO 2 , TiO 2 , ZrO 2 , ZnO, MgO, CaO, Li 2 O, B 2 O 3 , CO, CO 2 , SiO 2 , GeO 2 , N 2 O, NO, N 2 O 3 , NO 2 , N 2 O5, SO 2 , SO 3 , SeO 2 , SeO 3 , TeO 2 , TeO 3 , Cl 2 O, ClO 2 , Cl 2 O 7 , Br 2 O, BrO 2 , I 2 O 5 and I 2 O 7 .
19. The sensor of claim 17 , wherein the electrodes are comprised of a metal.
20. The sensor of claim 17 , wherein the surface comprises an insulating substrate.
21. The sensor of claim 17 , wherein the sol gel comprises poly(ethyleneoxide)-b-poly(propyleneoxide)-b-poly(ethyleneoxide) copolymer.
22. The sensor of claim 17 , wherein the sol gel nanodisk comprises copolymer poly(ethyleneoxide)-b-poly(propyleneoxide)-b-poly(ethyleneoxide), ethanol and tin chloride.
23. The sensor of claim 17 , wherein the tip is a microcantilever.
24. The sensor of claim 17 , comprising the additional step of fabricating the electrodes by photolithography and electron bean deposition on a surface prior to contacting the tip.
25. A method of detecting an ambient chemical comprising exposing a sensor to at least one ambient chemical wherein the sensor comprises a sol gel nanodisk fabricated between conducting electrodes.
26. The method of claim 25 , wherein the sol gel nanodisk comprises a tin dioxide selected from the group consisting of SnO 2 , Ti—SnO 2 , Co—SnO 2 , Ni—SnO 2 , Cu—SnO 2 , Zn—SnO 2 , Cd—SnO 2 , Pt—SnO 2 , TiO 2 , ZrO 2 , ZnO, MgO, CaO, Li 2 O, B 2 O 3 , CO, CO 2 , SiO 2 , GeO 2 , N 2 O, NO, N 2 O 3 , NO 2 , N 2 O 5 , SO 2 , SO 3 , SeO 2 , SeO 3 , TeO 2 , TeO 3 , Cl 2 O, ClO 2 , Cl 2 O 7 , Br 2 O, BrO 2 , I 2 O 5 and I 2 O 7 .
27. The method of claim 25 , wherein the conducting electrodes are comprised of metal.
28. The method of claim 25 , wherein the sensor is fabricated on an insulating substrate.
29. The method of claim 25 , wherein the sol gel nanodisk has a width of about 4 μM and a length of about 5 μM.
30. The method of claim 25 , wherein the sol gel nanodisk comprises poly(ethyleneoxide)-b-poly(propyleneoxide)-b-poly(ethyleneoxide) copolymer.
31. The method of claim 25 , wherein conductance between the electrodes following exposure of the sensor occurs in less than about 200 seconds.
32. The method of claim 25 , wherein the conductance between the electrodes following exposure of the sensor occurs in less than about 10 seconds.
33. The method of claim 25 , wherein the conductance between the electrodes following exposure of the sensor recovers in less than about 400 seconds.
34. The method of claim 25 , wherein the conductance between the electrodes following exposure of the sensor recovers in less than about 30 seconds.
35. A sensor comprising a sol gel nanodisk in direct ohmic contact with at least two conducting electrodes, wherein the sol gel nanodisk comprises a semi-crystallized structure having surface oxygen ions.
36. The sensor of claim 35 , wherein the semi-crystallized structure comprises an inorganic molecule selected from the group consisting of SnO 2 , Ti—SnO 2 , Co—SnO 2 , Ni—SnO 2 , Cu—SnO 2 , Zn—SnO 2 , Cd—SnO 2 , Pt—SnO 2 , TiO 2 , ZrO 2 , ZnO, MgO, CaO, Li 2 O, B 2 O 3 , CO, CO 2 , SiO 2 , GeO 2 , N 2 O, NO, N 2 O 3 , NO 2 , N 2 O5, SO 2 , SO 3 , SeO 2 , SeO 3 , TeO 2 , TeO 3 , Cl 2 O, ClO 2 , Cl 2 O 7 , Br 2 O, BrO 2 , I 2 O 5 and I 2 O 7 .