Method of producing a pigmented composite microporous material
Disclosed is a method for producing a pigmented composite comprising contacting a microporous material with a tin compound to form a composite then contacting the composite with a pigment comprising an elemental metal, a metal oxide, a metal alloy, a metal salt, or a combination thereof to produce the pigmented composite. The pigmented composites described herein are useful for separating one or more analytes present in a fluid sample.
1. A method for producing a pigmented composite, comprising:
a. contacting a microporous material with an aqueous solution of a tin compound to produce a first composite, wherein the microporous material comprises a ceramic, a metal, metal oxide, carbon, or glass; and
b. contacting the first composite with an aqueous solution of a first pigment comprising a palladium compound followed by contacting the first composite with an aqueous solution of a second pigment comprising a nickel compound to produce the pigmented composite.
2. The method of claim 1 , wherein the metal oxide comprises aluminum oxide, zirconium oxide, titanium oxide, a zeolite, or a combination thereof.
3. The method of claim 1 , wherein the microporous material comprises an inorganic electrochemically formed material or an etch material.
4. The method of claim 1 , wherein the microporous material comprises aluminum oxide that is electrochemically formed or etched.
5. The method of claim 1 , wherein the microporous material comprises micropores having a diameter of from about 0.02 microns to about 0.2 microns.
6. The method of claim 1 , wherein the microporous material comprises aluminum or titanium that has been anodized.
7. The method of claim 1 , wherein the tin compound comprises an organotin compound or a tin salt.
8. The method of claim 1 , wherein the tin compound comprises a compound that produces Sn +2 ions in solution.
9. The method of claim 1 , wherein the tin compound comprises SnCl 2 .
10. The method of claim 1 , wherein the microporous material comprises aluminum oxide and the tin compound comprises a tin salt.
11. The method of claim 1 , wherein after step (b), heating the pigmented composite.
12. The method of claim 1 , further comprising after step (b), applying a suspension matrix to the pigmented composite, wherein the suspension matrix is localized near the surface of the pigmented composite.
13. The method of claim 12 , wherein the suspension matrix comprises an oligonucleotide, a polysaccharide, a protein, an organic or inorganic polymer or macromolecule, or a combination thereof.
14. The method of claim 12 , wherein when the suspension matrix comprises an oligonucleotide, wherein the oligonucleotide comprises a nucleic acid.
15. A method for producing a pigmented composite, comprising:
a. contacting a microporous material with an aqueous solution of a tin compound to produce a first composite, wherein the microporous material comprises aluminum oxide that is electrochemically formed or etched, or aluminum or titanium that has been anodized, and
b. contacting the first composite with an aqueous solution of a pigment comprising an elemental metal, a metal oxide, a metal alloy, a metal salt, or a combination thereof to produce the pigmented composite.
16. The method of claim 15 , wherein the microporous material comprises micropores having a diameter of from about 0.02 microns to about 0.2 microns.
17. The method of claim 15 , wherein the tin compound comprises an organotin compound or a tin salt.
18. The method of claim 15 , wherein the tin compound comprises a compound that produces Sn +2 ions in solution.
19. The method of claim 15 , wherein the tin compound comprises SnCl 2 .
20. The method of claim 15 , wherein the pigment comprises a metal salt.
21. The method of claim 20 , wherein when the metal salt comprises a transition metal salt.
22. The method of claim 21 , wherein the transition metal salt comprises a palladium compound, a nickel compound, silver compound, gold compound, or a combination thereof.
23. The method of claim 15 , wherein in step (b), the first composite is contacted with an aqueous solution of a first pigment followed by contacting the first composite with an aqueous solution of a second pigment.
24. The method of claim 23 , wherein the aqueous solution of the first pigment comprises a palladium compound and the aqueous solution of the second pigment comprises a nickel compound.
25. The method of claim 15 , wherein the microporous material comprises aluminum oxide and the tin compound comprises a tin salt, and wherein the first composite is contacted with an aqueous solution of a first pigment comprising a palladium compound and then an aqueous solution of a second pigment comprising a nickel compound.
26. The method of claim 15 , wherein after step (b), heating the pigmented composite.
27. The method of claim 15 , further comprising after step (b), applying a suspension matrix to the pigmented composite, wherein the suspension matrix is localized near the surface of the pigmented composite.
28. The method of claim 27 , wherein the suspension matrix comprises an oligonucleotide, a polysaccharide, a protein, an organic or inorganic polymer or macromolecule, or a combination thereof.
29. The method of claim 27 , wherein when the suspension matrix comprises an oligonucleotide, wherein the oligonucleotide comprises a nucleic acid.