High temperature investment material and method for making solid investment molds
An improved phosphate-type refractory investment material and method for making solid investment molds especially useful for casting high melting point metals and alloys, such as platinum and the like. The material consists essentially of one or more phosphate salts, a water soluble acidic constituent, and refractory powder. The material can be prepared as a dry powder blend which is easily shipped to the user and mixed with water at the time of investing the flask. Alternatively, the salt and/or acidic constituent can be combined with the refractory powder at the time of mixing with water.
1. A dry investment powder blend suitable for making investment molds consisting essentially of:
phosphate salt,
water soluble acidic constituent, and
at least one refractory powder selected from the group consisting of silica, alumina, zirconia and high alumina aluminum silicates.
2. A dry investment powder blend as claimed in claim 1 wherein said phosphate salt is at least one member of the group consisting of phosphate salts of metals and inorganic, nonmetallic cations.
3. A dry investment powder blend as claimed in claim 1 wherein said phosphate salt is at least one member of the group consisting of:
a) monobasic, dibasic, and tribasic simple phosphate salts, and
b) condensed polyphosphate salts.
4. A dry investment powder blend as claimed in claim 1 where said water soluble acidic constituent is at least one member selected from the class consisting of organic acids having a melting point above room temperature, boric acid, and acidic salts that produce pH values of about 5 or lower when in solution.
5. A dry investment powder blend as claimed 3 wherein:
a) said monobasic phosphate salts have the general formulae AH 2 PO 4 and BH 4 (PO 4 ) 2 where A is ammonium or at least one monovalent metal of Group IA of the Periodic Table and B is a divalent metal,
b) said dibasic phosphate salts have the general formulae A 2 HPO 4 and BHPO 4 wherein A and B are as defined above, and
c) said tribasic phosphate salts have the general fomulae A 3 PO 4 , ABPO 4 , B 3 (PO 4 ) 2 and CPO 4 where A and B are as defined above and C is at least one trivalent element of Group III of the Periodic Table.
6. A dry investment powder blend as claimed in claim 5 wherein B is at least one metal selected from Group IIA of the Periodic Table.
7. A dry investment powder blend as claimed in claim 3 wherein said condensed polyphosphate salt is at least one member selected from the group consisting of pyrophosphates, long-chain polyphosphates and metaphosphates.
8. A dry investment powder blend for making investment molds consisting essentially of:
a) from about 0.02-4.00% phosphate salt which is at least one member of the group consisting of monobasic, dibasic, tribasic and condensed polyphosphate salts,
b) from about 0.01-3.00% of a water soluble acidic constituent which is at least one member from the class consisting of organic acids having a melting point above room temperature, boric acid, and acidic salts that produce pH values of about 5 or lower when in solution, and
c) the balance refractory powder, said refractory powder being at least one member selected from the group consisting of silica, alumina, zircon, zirconia, and high alumina aluminum silicates.
9. A dry investment powder blend as claimed in claim 8 wherein:
a) said monobasic phosphate salts have the general formulae AH 2 PO 4 and BH 4 (PO 4 ) 2 where A is ammonium or at least one monovalent metal of Group IA of the Periodic Table and B is a divalent metal,
b) said dibasic phosphate salts have the general formulae A 2 HPO 4 and BHPO 4 wherein A and B are as defined above, and
c) said tribasic phosphate salts have the general fomulae A 3 PO 4 , ABPO 4 , B 3 (PO 4 ) 2 and CPO 4 where A and B are as defined above and C is at least one trivalent element of Group III of the Periodic Table.
10. A dry investment powder blend as claimed in claim 8 wherein said condensed polyphosphate salt is at least one member selected from the group consisting of pyrophosphates, long-chain polyphosphates and metaphosphates.
11. A method of making an investment mold comprising the steps of:
a) providing a slurry consisting essentially of a refractory powder, phosphate salt, water soluble organic acid and water, wherein the refractory powder is at least one member selected from the group consisting of silica, alumina, zircon, zirconia, and high alumina aluminum silicates,
b) investing a disposable pattern with the slurry,
c) allowing the slurry to set to form a mold, and
d) removing the disposable pattern from the mold.
12. The method as claimed in claim 11 wherein step a) is carried out by forming a dry mixture of the refractory powder, phosphate salt and acidic constituent, and thereafter combining the dry mixture with the water.
13. The method as claimed in claim 11 wherein said phosphate salt is at least one member of the group consisting of:
a) monobasic, dibasic, and tribasic simple phosphate salts, and
b) condensed polyphosphate salts.
14. The method as claimed in claim 13 wherein:
a) said monobasic phosphate salts have the general formulae AH 2 PO 4 and BH 4 (PO 4 ) 2 where A is ammonium or at least one monovalent metal of Group IA of the Periodic Table and B is a divalent metal,
b) said dibasic phosphate salts have the general formulae A 2 HPO 4 and BHPO 4 wherein A and B are as defined above, and
c) said tribasic phosphate salts have the general fomulae A 3 PO 4 , ABPO 4 , B 3 (PO 4 ) 2 and CPO 4 where A and B are as defined above and C is at least one trivalent element of Group III of the Periodic Table.
15. A The method as claimed in claim 14 wherein said condensed polyphosphate salt is at least one member selected from the group consisting of pyrophosphates, long-chain polyphosphates and metaphosphates.