Ultra-hard boride-based metal matrix reinforcement
View Patent ↗A composite of M/AlMgB 14 or M alloy/AlMgB 14 is synthesized, where M=Al, Ti, W, or Cu. Small particles and/or fibers of AlMgB 14 are distributed throughout a metal matrix to strengthen the resulting composite.
1. A reinforced alloy comprising metal or a metal alloy with from 5% vol. % to about 30% vol. % of AlMgB 14 in the form of particles and/or fibers to reinforce said alloy.
2. The reinforced alloy of claim 1 wherein the metal is Al or an Al alloy an the Al alloy comprises from 90 wt. % to 100 wt. Al; from 0 wt. % to 7.0 wt. % Cu; from 0 wt. % to 1 wt. % Bi; from 0 wt. % to 1 wt. Pb; from 0 wt. % to 2 wt. % Fe; from 0 wt. % to 6 wt. % Mg; from 0 wt. % to 2 wt. Mn; from 0 wt. % to 14 wt. % Si; and from 0 wt. % to 8 wt. % Zn.
3. The reinforced Al alloy of claim 2 wherein the Al alloy is from 80 wt. % Al to 100 wt. % Al; and the solid density of said reinforced alloy is from 2.50 g/cc to 2.90 g/cc.
4. The reinforced Al alloy of claim 3 wherein the solid density of said reinforced alloy is from 2.60 g/cc to 2.80 g/cc.