Cathode composition for lithium batteries and method of preparing the same
View Patent ↗Provided is a cathode composition for lithium secondary battery that includes a lithium-chromium-titanium-manganese oxide that has the formula Li[Li (1-x)/3 Cr x Ti (2/3)y Mn 2(1-x-y)/3 ]O 2 where 0≦x≦0.3, 0≦y≦0.3 and 0.1≦x+y≦0.3, and layered a-LiFeO 2 structure. A method of synthesizing the lithium-chromium-titanium manganese oxide includes preparing a first mixed solution by dispersing titanium dioxide (TiO 2 ) in a mixed solution of chrome acetate (Cr 3 (OH) 2 (CH 3 CO 2 ) 7 ) and manganese acetate ((CH 3 CO 2 ) 2 Mn.4H 2 O), adding a lithium hydroxide (LiOH) solution to the first mixed solution to obtain homogeneous precipitates, forming precursor powder that has the formula Li[Li (1-x)/3 Cr x Ti (2/3)y Mn 2(1-x-y)/3 ]O 2 where 0≦x≦0.3, 0≦y≦0.3 and 0.1≦x+y≦0.3 by heating the homogeneous precipitates, and heating the precursor powder to form oxide powder having a layered structure.
1. A cathode composition for a lithium secondary battery, the cathode composition comprising a lithium-chromium-titanium-manganese oxide that has the formula Li[Li (1-x)/3 Cr x Ti (2/3)y Mn 2(1-x-y)/3 ]O 2 where 0<x≦0.3, 0<y≦0.3 and 0.1≦x+y≦0.3.
2. A method of preparing a cathode composition for a lithium secondary battery, the method comprising:
preparing a first mixed solution by dispersing titanium dioxide (TiO 2 ) in a mixed solution of chrome acetate (Cr 3 (OH) 2 (CH 3 CO 2 ) 7 ) and manganese acetate tetrahydrate ((CH 3 CO 2 ) 2 Mn.4H 2 O);
adding a lithium hydroxide (LiOH) aqueous solution to the first mixed solution to obtain homogeneous precipitates;
forming precursor powder that has the formula
Li[Li (1-x)/3 Cr x Ti (2/3)y Mn 2(1-x-y)/3 ]O 2 where 0<x≦0.3, 0<y≦0.3 and 0.1≦x+y≦0.3 by heating the homogeneous precipitates; and
heating the precursor powder to form oxide powder that has a layered structure.
3. The method of claim 2 , wherein the forming of the precursor powder comprises firing the homogeneous precipitates on a hot plate by heating the homogeneous precipitates.
4. The method of claim 3 , wherein the firing of the homogeneous precipitates is performed after coating a titanium foil with the homogeneous precipitates.
5. The method of claim 2 , wherein the heating of the precursor powder comprises:
performing a first thermal process on the precursor powder at a first temperature ranging from 650° C. to 700° C.; and
performing a second thermal process on the first thermally processed oxide powder at a second temperature that is higher than the first temperature.
6. The method of claim 5 , wherein the second temperature ranges from 900° C. to 1000° C.
7. The method of claim 5 , further comprising grinding the first thermally processed oxide powder prior to performing the second thermal process.
8. The method of claim 5 , wherein the second thermal process is performed in an atmospheric condition.
9. The method of claim 5 , further comprising quenching the second thermally processed oxide powder.