Open grid fabric resin infusion media and reinforcing composite lamina
An open grid fabric resin infusion medium and reinforcing composite lamina used in the manufacture of fiber reinforced polymer resin composites. The use of the open grid fabric as at least one of a composite lamina provides significant improvements in both the resin infusion rate and resin distribution uniformity throughout the laminate.
1 . An assembly of fabric layers adapted for use in a resin infusion molding process comprising at least one layer of an open grid uni-directional or bidirectional mesh fabric, having a substantially foraminous construction of respectively spaced apart fibers or yarns wherein less than about 50% of the textile volume is occupied by the fiber or yarn, and at least one additional fabric layer adjacent to said open grid fabric and suitable for fibrous reinforcement of a composite laminate, said fibers or yarns of said respective layers or plies being composed of natural, polymeric, or inorganic fibers, or combinations thereof.
2 . The assembly according to claim 1 wherein said open grid fabric layer has less than about 75% of the textile volume occupied by the fiber or yarn.
3 . The assembly according to claim 1 wherein said open grid fabric layer has less than about 90% of the textile volume occupied by the fiber or yarn.
4 . The assembly according to claim 1 wherein the open grid fabric is produced by warp insertion, weft insertion, or pillar stitch knits that are flat, circular, warp or weft knit.
5 . A vacuum induced resin infusion process for forming a fiber reinforced composite laminate, comprising:
forming an assembly of at least two plies of fibrous textile material, wherein one such ply is composed of an open grid uni-directional or bi-directional mesh fabric having a substantially foraminous construction of respectively spaced apart fibers or yarns wherein less than about 50% of the textile volume is occupied by the fiber or yarn, and at least one other additional ply is arranged adjacent to said open grid ply, said additional ply or plies being suitable for fibrous reinforcement of a composite laminate, and wherein said fibers or yarns of said respective layers or plies are composed of natural, polymeric, or inorganic fibers, or combinations thereof;
enclosing said assembly within a substantially air impervious envelope covering, fitted with at least one first means for applying a vacuum and at least one second means for supplying a curable resin to within said envelope;
applying a vacuum to at least one edge or side of the said envelope; and
introducing said curable resin to at least one opposite edge or side of said envelope, whereby aided by the foraminous nature of said open grid fabric the said curable resin flows rapidly at a speed sufficient to enable resin penetration and saturation throughout the fibrous textile assembly prior to a gelation point of the resin, to form, after at least substantial completion of resin curing, a fiber reinforced composite structure.
6 . The process of claim 5 wherein said open grid fabric layer or ply has less than about 75% of the textile volume occupied by the fiber or yarn.
7 . The process of claim 5 wherein said open grid fabric layer or ply has less than about 90% of the textile volume occupied by the fiber or yarn.
8 . The process of claim 5 wherein the open grid fabric is produced by warp insertion, weft insertion, or pillar stitch knits that are flat, circular, warp or weft knit.