Carbon electrode for use in aqueous electrochemical devices and method of preparation
View Patent ↗A high tensile strength, highly conductive flexible composite sheet consisting of fibrillated PTFE polymers, performance enhancing dopants, and carbon particles useful in electrochemical devices such as flow through capacitors, capacitive deionization, electronic water purification, fuel cells, capacitors, super-capacitors and a method of preparation. The method consists of mixing the materials and calendering to the desired thickness and strength all at room temperature and leaving the material in a wet state without further drying.
1. A high tensile strength highly conductive flexible composite sheet material for use as an electrode in an electrochemical device, comprising:
a. approximately 80% by dry weight of an activated carbon,
b. approximately 10% by dry weight of a carbon black,
c. approximately 1% by dry weight of a performance enhancing salt dopant, and
d. approximately 9% by dry weight of fibrillated polytetrafluoroethylene.
2. The composition of claim 1 where said activated carbon has a surface area of at least 1,000 square meters per gram.
3. The composition of claim 1 wherein said activated carbon has an average particle size no greater than 20 microns.
4. The composition of claim 1 wherein said carbon black has a surface area of at least 1,000 square meters per gram.
5. The composition of claim 1 wherein said dopant is chosen from the group of alkali metal halides.
6. The composition of claim 1 wherein the total weight of the finished electrode will be on the order of 1 to 4 times greater than the dry weight.