Thermo-expansive microcapsules and their application
Thermo-expansive microcapsules comprising a shell of a polymer produced by polymerizing a mixture of monomers, which comprises (I) a nitrile monomer, (II) a monomer having an unsaturated double bond and carboxyl groups in a molecule, (III) a monomer having two or more of polymerizable double bonds in a molecule, and optionally, (IV) a monomer different from and copolymerizable with the monomers (I), (II) and (III) and a blowing agent encapsulated in the shell. The volume retention of the expanded microcapsules of the thermo-expansive microcapsules is 50% or more after loaded with 15 MPa.
1. Thermo-expansive microcapsules comprising a shell of a polymer produced by polymerizing a mixture of monomers, which comprises 40 to 95 weight percent of (I) a nitrile monomer, 7 to 50 weight percent of (II) a monomer having an unsaturated double bond and a carboxyl group in a molecule, 0.01 to 5 weight percent of (III) a monomer having two or more of polymerizable double bonds in a molecule, and optionally, 0 to 15 weight percent of (IV) a monomer different from and copolymerizable with the monomers (I), (II) and (III) and a blowing agent encapsulated in the shell, wherein the mixture of monomers does not substantially contain a monomer having a functional group reactive with the carboxyl group contained in the (II) monomer.
2. The thermo-expansive microcapsules of claim 1 , of which expanded microcapsules have a volume retention of 50% or more after loaded with 15 MPa at 25° C. and/or 140° C.
3. The thermo-expansive microcapsules of claim 1 or 2 , wherein a polymerization initiator for polymerizing the mixture of monomers is an oil-soluble peroxide, an azo compound or a substance having a half life of 1 to 25 hours at a polymerization temperature.
4. The thermo-expansive microcapsules of claim 1 or 2 , of which maximum expanding temperature is 160° C. or higher.
5. Resin compositions comprising the thermo-expansive microcapsules of claim 1 or expanded microcapsules thereof, and a resin.
6. The thermo-expansive microcapsules of claim 1 , wherein the content of the monomer having a functional group reactive with the carboxyl group contained in the (II) monomer is less than 1 weight percent of the mixture of monomers.
7. The thermo-expansive microcapsules of claim 6 , wherein the (IV) monomer includes at least one member selected from the group consisting of vinylidene chloride, vinyl acetate, (meth)acrylates, styrene monomers, acrylamide, and methacrylamide.
8. The thermo-expansive microcapsules of claim 6 , wherein the (meth)acrylates are methyl(meth)acrylate, ethyl(meth)acrylate, n-butyl(meth)acrylate, isobutyl(meth)acrylate, t-butyl(meth)acrylate, isobomyl(meth)acrylate, cyclohexyl(meth)acrylate, benzyl(meth)acrylate, and β-carboxyethyl acrylate.
9. The thermo-expansive microcapsules of claim 6 , of which expanded microcapsules have a volume retention of 50% or more after loaded with 15 MPa at 25° C. and/or 140° C.
10. The thermo-expansive microcapsules of claim 6 , of which maximum expanding temperature is 160° C. or higher.
11. Resin compositions comprising the thermo-expansive microcapsules of claim 6 or expanded microcapsules thereof, and a resin.
12. Thermo-expansive microcapsules comprising a shell of a polymer produced by polymerizing a mixture of monomers, which comprises 40 to 95 weight percent of (I) a nitrile monomer, 7 to 50 weight percent of (II) a monomer having an unsaturated double bond and a carboxyl group in a molecule, 0.01 to 5 weight percent of (III) a monomer having two or more of polymerizable double bonds in a molecule, and optionally, 0 to 20 weight percent of (IV) a monomer different from and copolymerizable with the monomers (I), (II) and (III) and a blowing agent encapsulated in the shell, wherein the (IV) monomer includes at least one member selected from the group consisting of vinylidene chloride, vinyl acetate, methyl(meth)acrylate, ethyl(meth)acrylate, n-butyl(meth)acrylate, isobutyl(meth)acrylate, t-butyl(meth)acrylate, isobomyl(meth)acrylate, cyclohexyl(meth)acrylate, benzyl(meth)acrylate, β-carboxyethyl acrylate, styrene monomers, acrylamide, and methacrylamide, and
of which expanded microcapsules have a volume retention of 50% or more after loaded with 15 MPa at 25° C. and/or 140° C.
13. The thermo-expansive microcapsules of claim 12 , of which maximum expanding temperature is 160° C. or higher.
14. Resin compositions comprising the thermo-expansive microcapsules of claim 12 or expanded microcapsules thereof, and a resin.
15. Thermo-expansive microcapsules comprising a shell of a polymer produced by polymerizing a mixture of monomers, which comprises 40 to 95 weight percent of (I) a nitrile monomer, 7 to 50 weight percent of (II) a monomer having an unsaturated double bond and a carboxyl group in a molecule, 0.01 to 5 weight percent of (III) a monomer having two or more of polymerizable double bonds in a molecule, and optionally, 0 to 15 weight percent of (IV) a monomer different from and copolymerizable with the monomers (I), (II) and (III) and a blowing agent encapsulated in the shell,
and of which expanded microcapsules have a volume retention of 50% or more after loaded with 15 MPa at 25° C. and/or 140° C.
16. Resin compositions comprising the thermo-expansive microcapsules of claim 15 or expanded microcapsules thereof, and a resin.