Yttria containing high-density chrome based refractory composites
The invention presents yttria elements containing high-density chrome based refractory composites, which consist of: (A) Fused polymeric compound as aggregate, containing: 40 to 50 wt % of particles in size from 1 to 4 mm and 15 to 25 wt % of particles in size below 1 mm; (B) A matrix consisting of fused polymeric compounds with particle sizes below 66 μm, active sintered Al 2 O 3 , active industrial Cr 2 O 3 and Y 2 O 3 , (C) Binders accounting for 2.5 to 3.5 wt %. Since Y 2 O 3 has resistance to the slag corrosion and penetration with its compatibility with slag, it has been introduced to activate the major component Cr 2 O 3 crystal lattice in favor with Al 2 O 3 so that it helps to reduce the sintering temperature, increase the rate of finished products as well as reduce the manufacturing cost.
1. Yttria containing high-density chrome based refractory composites consisting of:
(A) fused polymeric compounds as aggregates, containing:
(a) 40 to 50 wt % of particles in size from 1 to 4 mm;
(b) 15 to 25 wt % of particles in size below 1 mm;
(B) matrix consisting of fused polymeric compounds with particle sizes of below 66 μm, active sintered Al 2 O 3 , active industrial Cr 2 O 3 and Y 2 O 3 containing as follows:
(a) 16 to 25 wt % of fused polymeric compound particles in size below 66 μm;
(b) 3 to 7 wt % of active sintered Al 2 O 3 particles in size below 5 μm;
(c) 4 to 9 wt % of active industrial Cr 2 O 3 particles in size below 44 μm;
(d) 0.2 to 5 wt % of Y 2 O 3 particles in size below 44 μm;
(e) binders being added accounting for 2.5 to 3.5 wt %.
2. The yttria containing high-density chrome based refractory composites according to claim 1 wherein the fused polymeric compound as aggregates containing 44˜48 wt % of particles in size from 1 mm to 4 mm and 17˜22 wt % of particles in size below 1 mm.
3. The yttria containing high-density chrome based refractory composites according to claim 1 wherein the matrix contains 0.4˜2.0 wt % of Y 2 O 3 particles, 20˜24 wt % of fused polymeric compound particles in size below 66 μm, 4˜6 wt % of active sintered Al 2 O 3 and 5˜7 wt % of active industrial Cr 2 O 3 .
4. The yttria containing high-density chrome based refractory composites according to claim 1 wherein aluminum di-hydrogen phosphate or other phosphate and sulphate or mixture in two in random with certain proportion are taken as the binder.
5. The yttria containing high-density chrome based refractory composites according to claim 1 wherein Cr 2 O 3 accounts for 40˜95 wt % of the composite.
6. The yttria containing high-density chrome based refractory composites according to claim 1 wherein the material is molded with a forming machine, dried at 60˜110° C. and then sintered in a slightly reducing atmosphere at 1630˜1680° C.