High frequency-weldable articles and method for connecting the same
High frequency-weldable articles, such as sheets or yarns, include at least one high frequency-weldable part that is made from a modified polyethylene terephthalate (PET) material and that has a melting point ranging from 100° C. to 250° C. The modified PET material is prepared from a composition that includes terephthalic acid, ethylene glycol and a diol modifier. The diol modifier is selected from the group consisting of neopentanediol, 1,3-dihydroxy-2-methylpropane, 1,3-dihydroxy-2-methylpropane alkoxylate, 2,5-dimethyl-2,5-hexanediol, polyethylene glycol, and combinations thereof.
1. A high frequency-weldable sheet, comprising a substrate, and a first high frequency-weldable layer formed on said substrate and consisting of a modified polyethylene terephthalate material that is prepared from a composition comprising terephthalic acid, ethylene glycol and a diol modifier, said diol modifier being selected from the group consisting of neopentanediol, 1,3-dihydroxy-2-methylpropane, 1,3-dihydroxy-2-methylprop alkoxylate, 2,5-dimethyl-2,5-hexanediol, polyethylene glycol, and combinations thereof, said first high frequency-weldable layer having a melting point that is at least 208° C. and is up to 250° C., said high frequency-weldable sheet further comprising a second high frequency-weldable layer formed on said substrate such that said substrate is sandwiched between said first and second high frequency-weldable layers, said second high frequency-weldable layer being made from said modified PET material, said modified polyethylene terephthalate material being prepared such that, when said high frequency-weldable sheet is subjected to welding at high frequency, a welded area of said modified polyethylene terephthalate material does not comprise a crystalline structure.
2. The high frequency-weldable sheet of claim 1 , wherein, based on total moles of ethylene glycol, said diol modifier is used in an amount ranging from 2 to 40 mol %.
3. The high frequency-weldable sheet of claim 2 , wherein, based on total moles of ethylene glycol, said diol modifier is used in an amount ranging from 5 to 15 mol %.
4. The high frequency-weldable sheet of claim 1 , wherein said composition further comprises a diacid modifier selected from the group consisting of isophthalic acid, itaconic acid, adipic acid, and combinations thereof.
5. The high frequency-weldable sheet of claim 4 , wherein said diacid modifier is isophthalic acid.
6. The high frequency-weldable sheet of claim 4 , wherein, based on total moles of terephthalic acid, said diacid modifier is used in an amount ranging from 2 to 20 mol %.
7. The high frequency-weldable sheet of claim 1 , wherein said substrate is made from a thermoplastic resin.
8. The high frequency-weldable sheet of claim 1 , wherein said modified PET material has an intrinsic viscosity ranging from 0.60 to 0.90.
9. The high frequency-weldable sheet of claim 1 , wherein, based on total weight of said high frequency-weldable sheet, each of said first and second high frequency-weldable layers has a weight ranging from 3 wt % to 20 wt %.
10. The high frequency-weldable sheet of claim 1 , wherein the melting point of said first high frequency-weldable layer is no greater than 240° C.