The invention relates to the use of used alumina to reduce the level of inorganic contaminants, such as mercury and arsenic, from waste fluid streams. The invention further provides a process for reducing the level of mercury or arsenic in fluid streams by contacting the fluid stream with used alumina, such as used Claus catalyst.
1. A process for reducing the level of arsenic from a liquid stream comprising contacting said liquid stream with used alumina, wherein the used alumina is used Claus catalyst having a sulfur concentration of 0.1% -2.0% by weight, and wherein the liquid stream is an aqueous stream.
2. A process for reducing the level of arsenic from a liquid stream containing arsenic, comprising the steps of:
(a) flowing the liquid stream through a bed containing a sorbent, wherein the sorbent comprises used alumina, wherein the used alumina is used Claus catalyst having a sulfur concentration of 0.1% -2.0% by weight, and wherein the liquid stream is an aqueous stream;
(b) sorbing arsenic from the liquid stream onto the surface of the sorbent; and
(c) allowing the arsenic-depleted effluent stream to exit from the outlet of the bed.
3. The process of claim 1 , wherein the used alumina is crushed prior to contacting said liquid stream.
4. The process of claim 3 , wherein the used alumina is heated to remove moisture prior to contacting said liquid stream.
5. The process of claim 1 , wherein at least about 50% of arsenic is removed from said liquid stream.
6. The process of claim 1 , wherein at least about 75% of arsenic is removed from said liquid stream.
7. The process of claim 1 , wherein at least about 90% of arsenic is removed from said liquid stream.
8. The process of claim 1 , wherein the arsenic is elemental arsenic.
9. The process of claim 1 , wherein the arsenic is ionic arsenic.
10. The process of claim 1 , wherein the arsenic is arsenic(V).
11. The process of claim 2 , wherein the used alumina is crushed prior to being loaded on the bed.
12. The process of claim 11 , wherein the used alumina is heated to remove moisture prior to being loaded on the bed.
13. The process of claim 2 , wherein at least about 50% of arsenic is removed from said liquid stream.
14. The process of claim 2 , wherein at least about 75% of arsenic is removed from said liquid stream.
15. The process of claim 2 , wherein at least about 90% of arsenic is removed from said liquid stream.
16. The process of claim 2 , wherein the arsenic is elemental arsenic.
17. The process of claim 2 , wherein the arsenic is ionic arsenic.
18. The process of claim 2 , wherein the arsenic is arsenic(V).