Hollow polymer particles, aqueous dispersion thereof and production process thereof
Disclosed are hollow polymer particles composed of a crosslinked polymer having a comparatively small particle diameter and a narrow particle diameter distribution, an aqueous dispersion of the particles, and an ink having good flying property. The hollow polymer particles are obtained by emulsion-polymerizing a crosslinkable polymerizable monomer composition absorbed in seed particles and containing a crosslinkable monomer component and a hydrophilic monomer component, wherein the seed particles are particles of a polymer having a weight average molecular weight of 500 to 15,000, and obtained by emulsion-polymerizing 100 parts by mass of a non-crosslinkable polymerizable monomer in the presence of 0.01 to 5 parts by mass of a chain transfer agent composed of at least one compound selected from the group consisting of α-methylstyrene dimer, thiuram disulfides and terpene hydrocarbons. The ink contains the hollow polymer particles.
1. A process for producing a hollow polymer particle; comprising
emulsion-polymerizing 100 parts by mass of a non-crosslinkable monomer in the presence of 0.01 to 5 parts by mass of a chain transfer agent composed of at least one compound selected from the group consisting of α-methylstyrene dimer, thiuram disulfides and terpene hydrocarbons to obtain a seed particle which is a particle of a polymer having a weight average molecular weight of 500 to 15,000; and
adding a crosslinkable polymerizable monomer composition comprising a crosslinkable monomer component and a hydrophilic monomer component to an aqueous dispersion of the seed particle to subject the monomer composition to an emulsion polymerization treatment in a state absorbed in the seed particle.
2. The production process of the hollow polymer particle according to claim 1 , wherein the crosslinkable monomer contained in the crosslinkable polymerizable monomer composition is divinylbenzene.
3. The production process of the hollow polymer particle according to claim 1 , wherein the hydrophilic monomer is at least one selected from the group consisting of vinylpyridine, acrylonitrile, methyl methacrylate, 2-hydroxyethyl methacrylate, acrylic acid and methacrylic acid.
4. The production process of the hollow polymer particle according to claim 2 , wherein the hydrophilic monomer is at least one selected from the group consisting of vinylpyridine, acrylonitrile, methyl methacrylate, 2-hydroxyethyl methacrylate, acrylic acid and methacrylic acid.
5. The production process of the hollow polymer particle according to claim 1 , wherein the crosslinkable polymerizable monomer composition is added in a proportion of 2 to 500 parts by mass per 1 part by mass of the seed particle.
6. The production process of the hollow polymer particle according to claim 2 , wherein the crosslinkable polymerizable monomer composition is added in a proportion of 2 to 500 parts by mass per 1 part by mass of the seed particle.
7. The production process of the hollow polymer particle according to claim 1 , wherein the seed particle has a number average particle diameter of 0.05 to 1.5 μm.
8. The production process of the hollow polymer particle according to claim 2 , wherein the seed particle has a number average particle diameter of 0.05 to 1.5 μm.
9. The production process of the hollow polymer particle according to claim 1 , wherein the seed particle is composed of a polymer formed of an ethylenic unsaturated monomer.
10. The production process of the hollow polymer particle according to claim 2 , wherein the seed particle is composed of a polymer formed of an ethylenic unsaturated monomer.
11. The production process of the hollow polymer particle according to claim 1 , wherein in the crosslinkable polymerizable monomer composition, the proportion of the crosslinkable monomer component is 1 to 50% by mass, and the proportion of the hydrophilic monomer component is 1 to 99% by mass.
12. The production process of the hollow polymer particle according to claim 2 , wherein in the crosslinkable polymerizable monomer composition, the proportion of the crosslinkable monomer component is 1 to 50% by mass, and the proportion of the hydrophilic monomer component is 1 to 99% by mass.
13. The production process of the hollow polymer particle according to claim 1 , wherein the emulsion polymerization treatment is conducted in a state that the crosslinkable polymerizable monomer composition and an oily substance have been absorbed in the seed particle.
14. The production process of the hollow polymer particle according to claim 2 , wherein the emulsion polymerization treatment is conducted in a state that the crosslinkable polymerizable monomer composition and an oily substance have been absorbed in the seed particle.