Method of synthesizing small-diameter carbon nanotubes with electron field emission properties
View Patent ↗Carbon nanotube material having an outer diameter less than 10 nm and a number of walls less than ten are disclosed. Also disclosed are an electron field emission device including a substrate, an optionally layer of adhesion-promoting layer, and a layer of electron field emission material. The electron field emission material includes a carbon nanotube having a number of concentric graphene shells per tube of from two to ten, an outer diameter from 2 to 8 nm, and a nanotube length greater than 0.1 microns. One method to fabricate carbon nanotubes includes the steps of (a) producing a catalyst containing Fe and Mo supported on MgO powder, (b) using a mixture of hydrogen and carbon containing gas as precursors, and (c) heating the catalyst to a temperature above 950° C. to produce a carbon nanotube. Another method of fabricating an electron field emission cathode includes the steps of (a) synthesizing electron field emission materials containing carbon nanotubes with a number of concentric graphene shells per tube from two to ten, an outer diameter of from 2 to 8 nm, and a length greater than 0.1 microns, (b) dispersing the electron field emission material in a suitable solvent, (c) depositing the electron field emission materials onto a substrate, and (d) annealing the substrate.
1. A method of manufacturing carbon nanotubes comprising the steps of:
(a) producing by a combustion process a catalyst containing Mo and one or more other metals supported on MgO powder;
(b) using a gas mixture containing carbon-containing gas as a precursor; and
(c) heating the catalyst and the gas mixture to a temperature above 900° C. to produce a carbon nanotube having an outer diameter equal to or smaller than about 10 nm and the carbon nanotube having from 2 to 5 walls.
2. The method of claim 1 , wherein the other metals include Fe and Co.
3. The method of claim 1 , wherein the carbon-containing gas includes hydrogen and methane.
4. The method of claim 3 , wherein a ratio of hydrogen to methane in the gas mixture is 1 to 20.
5. The method of claim 1 , wherein the produced nanotubes have enhanced field emission properties.
6. The method of claim 5 , wherein the carbon-containing gas includes hydrogen and methane.
7. The method of claim 6 , wherein a ratio of hydrogen to methane in the mixture is 1 to 20.
8. The method of claim 1 , wherein the produced carbon nanotube has a current density of no less than about 4 mA/cm 2 at an applied field of 1.5 to 3 v/μm when measured using a parallel plate geometry.
9. The method of claim 1 , wherein the produced carbon nanotube has an outer diameter equal to or smaller than 10 nm and a number of walls of the nanotube is less than 10.
10. The method of claim 1 , wherein the precursor contains oxidizer and organic fuel, wherein the combustion process includes using the precursor to generate a large amount of gaseous byproduct and to produce high surface area solids.