Toughened two-part adhesive compositions demonstrating improved impact and/or peel strengths when cured
View Patent ↗Compositions for bonding substrate surfaces, particularly steel, aluminum, and urethane-primed galvanized steel, are disclosed. Desirably, the compositions include a stable emulsion including: (a) at least one curable (meth)acrylate component; (b) at least three different elastomeric polymers that are soluble and/or partially soluble in the (meth)acrylate component; and (c) optionally at least one elastomeric polymer that is not soluble in the (meth)acrylate component. Methods for preparing and methods for using these compositions also are disclosed.
1. An adhesive composition comprising a stable, homogenous emulsion comprising:
(a) at least one curable (meth)acrylate component;
(b) at least three different elastomeric polymers that are soluble in the (meth)acrylate component;
(c) at least one elastomeric polymer that is not soluble in the (meth)acrylate component; and
(d) a urethane polyol, wherein the urethane polyol results in the formation of the stable, homogenous emulsion;
and wherein said emulsion remains stable and homogenous for at least 20 days at room temperature.
2. The composition of claim 1 , wherein the (meth)acrylate component is present in an amount from about 40 percent by weight to about 75 percent by weight of the total composition.
3. The composition of claim 1 , wherein the at least three different elastomeric polymers that are soluble in the (meth)acrylate component are present in an amount from about 5 percent by weight to about 60 percent by weight of the total composition.
4. The composition of claim 1 , wherein the first different elastomeric polymer that is soluble in the (meth)acrylate component is present in an amount from about 1 percent by weight to about 30 percent by weight of the total composition.
5. The composition of claim 1 , wherein the second different elastomeric polymer that is soluble in the (meth)acrylate component is present in an amount from about 1 percent by weight to about 30 percent by weight of the total composition.
6. The composition of claim 1 , wherein the third different elastomeric polymer that is soluble in the (meth)acrylate component is present in an amount from about 1 percent by weight to about 30 percent by weight of the total composition.
7. The composition of claim 1 , wherein the at least one elastomeric polymer that is not soluble in the (meth)acrylate component is present in an amount of about 50 or less percent by weight of the total composition.
8. The composition of claim 1 , wherein the at least three different elastomeric polymers that are soluble in the (meth)acrylate component are selected from the group consisting of rubber and/or rubber copolymers and/or rubber derivatives (both saturated and unsaturated).
9. The composition of claim 8 , wherein the at least three different elastomeric polymers are styrene butadiene styrene, vinyl-terminated butadiene, and chlorosulfonated polyethylene.
10. The composition of claim 1 , wherein the at least one elastomeric polymer that is not soluble in the (meth)acrylate component and/or its solutions in all proportions is selected from the group consisting of rubber and/or rubber copolymers and/or rubber derivatives (both saturated and unsaturated).
11. The composition of claim 10 , wherein the at least one elastomeric polymer that is not soluble in the (meth)acrylate component and/or its solutions in all proportions is acrylonitrile butadiene styrene.
12. The composition of claim 1 , wherein the portion of the at least one elastomeric polymer that is not soluble in the (meth)acrylate component is stably dispersed in the emulsion.
13. The composition of claim 1 , wherein the composition further includes an acetyl acetonate ester capped urethane polyol.
14. The composition of claim 1 , wherein the composition further comprises a free-radical initiator component.
15. The composition of claim 1 , wherein the composition yields one or more of a peel strength on acid-etched aluminum of at least 90 pli at room temperature, wherein the composition is cured for two hours at room temperature and then for 30 minutes at 220° F. and then cooled to room temperature prior to measuring the peel strength; a tensile strength on a substrate of at least 2400 psi at 72° F., wherein the composition is cured for two hours at room temperature and then for 30 minutes at 220° F. and then cooled to 72° F. prior to measuring the tensile strength; upon cure on a substrate, withstands an impact of at least 15 KJ/m 2 when measured at −40° F.; yields a peel strength on a substrate of at least 65 pli at room temperature, wherein the composition is cured for two hours at room temperature and then for 30 minutes at 220° F. and then cooled to room temperature prior to measuring the peel strength.
16. A method for using a composition of claim 1 to bond together two substrates, comprising the steps of:
(a) applying the composition of claim 1 to a first substrate surface;
(b) mating the surface of a second substrate in abutting relationship with composition-applied first substrate surface to form an assembly; and
(c) maintaining the abutting relationship for a time sufficient to allow the composition to cure.
17. A composition comprising the reaction product of:
(a) a first part comprising:
(i) at least one curable (meth)acrylate component;
(ii) at least three different elastomeric polymers that are soluble in the (meth)acrylate component; and
(iii) a urethane polyol; and
(b) a second part optionally comprising at least one elastomeric polymer that is not soluble in the (meth)acrylate component;
wherein the urethane polyol results in the formation of a stable, homogenous emulsion; and wherein said emulsion remains stable and homogenous for at least 20 days at room temperature.