Blends of perfluoroelastomers and fluoroplastics
View Patent ↗Cured articles are prepared from a composition that comprises a blend of a perfluoroelastomer and 51-300 phr of a semi-crystalline thermoplastic copolymer comprising copolymerized units of tetrafluoroethylene and 5-12 weight percent of a perfluoro(alkyl vinyl ether). The semi-crystalline copolymer is present as particles having an average particle size greater than 100 nm.
1. A process for preparing a cured article, said process comprising:
A. dry blending, at a temperature below 100° C., i) a perfluoroelastomer, ii) 51 to 300 parts by weight per hundred parts by weight perfluoroelastomer of a semi-crystalline copolymer comprising copolymerized units of tetrafluoroethylene and 5-12 weight percent of a perfluoro(alkyl vinyl ether), said semi-crystalline copolymer having an average particle size greater than 100 nm and a melting point, and iii) a curative to form a curable composition;
B. curing said composition to form a cured article; and
C. post curing said cured article at a temperature above the melting point of said semi-crystalline copolymer.
2. A process of claim 1 wherein curing step B) takes place at a temperature below the melting point of said semi-crystalline copolymer.
3. A process of claim 1 wherein said dry blending step A) is at a temperature below 50° C.
4. A process of claim 1 wherein said curable composition contains 60 to 200 parts by weight of said semi-crystalline copolymer per hundred parts by weight perfluoroelastomer.
5. A cured article prepared by a process comprising:
A. dry blending, at a temperature below 100° C., i) a perfluoroelastomer, ii) 51 to 300 parts by weight per hundred parts by weight perfluoroelastomer of a semi-crystalline copolymer comprising copolymerized units of tetrafluoroethylene and 5-12 weight percent of a perfluoro(alkyl vinyl ether), said semi-crystalline copolymer having an average particle size greater than 100 nm and a melting point, and iii) a curative to form a curable composition;
B. curing said composition to form a cured article; and
C. post curing said cured article at a temperature above the melting point of said semi-crystalline copolymer.
6. A cured article of claim 5 wherein curing step B) takes place at a temperature below the melting point of said semi-crystalline copolymer.
7. A cured article of claim 5 wherein said dry blending step A) is at a temperature below 50° C.
8. A cured article of claim 5 wherein said curable composition contains 60 to 200 parts by weight of said semi-crystalline copolymer per hundred parts by weight perfluoroelastomer.
9. A cured article of claim 8 wherein said curable composition contains 75 to 200 parts by weight of said semi-crystalline copolymer per hundred parts by weight perfluoroelastomer.
10. A cured article of claim 5 wherein said perfluoroelastomer comprises copolymerized units of 53.0-79.9 mole percent tetrafluoroethylene, 20.0-46.9 mole percent perfluoro(methyl vinyl) ether and 0.4 to 1.5 mole percent of a cure site monomer.