Polymer-based orthopedic screw and driver system with increased insertion torque tolerance and associated method for making and using same
An orthopedic screw with an internal bore and mating driver has a bioabsorbable polymer component. To increase the torque tolerance of the screw and to minimize the likelihood of the driver stripping inside the bore of the screw, the screw and driver are heat treated together to shrink fit the screw onto the driver thereby increasing the driver-to-screw contact and distributing the loading force over a greater area to protect against material failure. The heat treatment involves heating the screw to an elevated temperature and holding that temperature for a period to promote stress relaxation and/or crystallization of the material.
1. A medical screw and driver system, comprising:
an elongated polymer screw having external threads and an internal bore extending through said screw along at least a portion of the length of said screw, said screw being formed from a biocompatible material and at least partially formed from a bioabsorbable material that is shrinkable upon heating, and said bore having an inner surface that is formed of said bioabsorbable material; and
an elongated driver having a non-circular cross-sectional shape approximating the cross-sectional shape of said bore, said driver being insertable into said bore, wherein said inner surface of said bore has been shrunken against said driver and conformed thereto upon heating said screw, thus achieving a closely mating shrink-fit of said bore relative to said driver such that said driver is matingly received within said bore to transfer rotational motion of said driver to said screw.
2. The system of claim 1 , wherein said driver and said bore have a mating taper, each exhibiting a diminishing cross-sectional area in the direction of insertion of said driver into said cannula.
3. The system of claim 1 , wherein said shrinkage is due to crystallization of said bioabsorbable material.
4. The system of claim 1 , wherein said shrinkage is due to stress relaxation of said bioabsorbable material.
5. The system of claim 1 , wherein said bioabsorbable material is selected from the group consisting of aliphatic polyesters, polyorthoesters, polyanhydrides, polycarbonates, polyurethanes, polyamides, and polyalkylene oxides.
6. The system of claim 5 , wherein said screw has an additive to the composition thereof selected from the group consisting of bioabsorbable glass, bioabsorbable ceramic, biocompatible glass and biocompatible ceramic.
7. The system of claim 1 , where said screw is composed of a 15/85 (vol/vol) blend of TCP/PLA.
8. The system of claim 1 , wherein said screw is an orthopedic screw.
9. The system of claim 1 , wherein said shrink-fit causes said bore to be in substantially continuous contact with said driver along the length of said bore.
10. The system of claim 9 , wherein said shrink fit causes said bore to be in substantially continuous contact with said driver about the circumferential periphery of said bore.
11. The system of claim 1 , wherein said driver is made of a material that does not plastically deform in response to the heating of said bioabsorbable material of said screw.
12. A medical screw and driver system, comprising:
an elongated polymer screw having external threads and an internal bore extending through said screw along at least a portion of the length of said screw, said screw being formed from a biocompatible material and at least partially formed from a bioabsorbable material that is shrinkable upon heating; and
an elongated driver having a non-circular cross-sectional shape approximating the cross-sectional shape of said bore, said driver being insertable into said bore, said screw and said bore having been shrunken and conformed to said driver by heating said screw so as to achieve a closely mating shrink-fit of said bore relative to said driver such that said driver is matingly received within said bore to transfer rotational motion of said driver to said screw and is withdrawn from and inserted into said bore without making further changes to said bore.
13. The system of claim 12 , wherein said driver and said bore have a mating taper, each exhibiting a diminishing cross-sectional area in the direction of insertion of said driver into said cannula.
14. The system of claim 12 , wherein said shrinkage is due to crystallization of said bioabsorbable material.
15. The system of claim 12 , wherein said shrinkage is due to stress relaxation of said bioabsorbable material.
16. The system of claim 12 , wherein said bioabsorbable material is selected from the group consisting of aliphatic polyesters, polyorthoesters, polyanhydrides, polycarbonates, polyurethanes, polyamides, and polyalkylene oxides.
17. The system of claim 16 , wherein said screw has an additive to the composition thereof selected from the group consisting of bioabsorbable glass, bioabsorbable ceramic, biocompatible glass and biocompatible ceramic.
18. The system of claim 12 , where said screw is composed of a 15/85 (vol/vol) blend of TCP/PLA.
19. The system of claim 12 , wherein said screw is an orthopedic screw.
20. The system of claim 12 , wherein said shrink-fit causes said bore to be in substantially continuous contact with said driver along the length of said bore.
21. The system of claim 20 , wherein said shrink fit causes said bore to be in substantially continuous contact with said driver about the circumferential periphery of said bore.
22. The system of claim 12 , wherein said driver is made of a material that does not plastically deform in response to the heating of said bioabsorbable material of said screw.