View Patent ↗A method for producing composite, shelled, alloy and compound nanoparticles as well as nanostructured films of composite, shelled, alloy and compound nanoparticles by using laser ablation of microparticles is disclosed.
1. A method for producing nanoparticles, said method comprising:
performing a first ablation on an aerosol gas of microparticles of a first material to transform said aerosol gas of microparticles of said first material to an aerosol gas of nanoparticles of said first material;
adding an aerosol gas of microparticles of a second material to said aerosol gas of nanoparticles of said first material; and
performing a second ablation on said microparticles of said second material and said aerosol gas of nanoparticles of said first material to transform said aerosol gas of microparticles of said second material to an aerosol gas of nanoparticles of said second material, such that said nanoparticles of said first material are nucleated by said nanoparticles of said second material.
2. The method of claim 1 , wherein said first ablation and second ablation are performed via a first and second energy beams, respectively.
3. The method of claim 2 , wherein said first and second energy beams are laser beams having wavelengths in a range between 0.15 and 11 microns.
4. The method of claim 1 , wherein said first ablation and second ablation are performed via a single energy beam.
5. The method of claim 4 , wherein said single energy beam is a laser beam having a wavelength in a range between 0.15and 11microns.
6. The method of claim 4 , wherein each of said microparticles of said second material and said nanoparticles of said first material absorb less than half of the energy of said single energy beam during said second ablation.
7. The method of claim 1 , wherein said method further includes collecting said nanoparticles using a collection module.
8. The method of claim 7 , wherein said collecting further includes collecting said nanoparticles using an electric field.
9. The method of claim 1 , wherein said nanoparticles include shelled, alloy, compound, or mixtures thereof.
10. The method of claim 5 , wherein the laser beam has a wavelength of 533nanometers and has a pulse length of 8 nanoseconds.
11. The method of claim 5 , wherein the laser beam has a wavelength of 248nanometer and has a pulse length of 12 nanoseconds.
12. The method of claim 5 , wherein the laser beam has a wavelength of 1064nanometer and has a pulse length of 10 nanoseconds.
13. The method of claim 5 , wherein the laser beam has an energy sufficient to exceed a plasma formation threshold of each of the microparticles of the first material and the microparticles of the second material by a factor of at least 1.5.
14. The method of claim 13 , wherein the laser beam has a fluence of about 0.5 J/cm 2 .
15. The method of claim 1 , further comprising filtering, based at least in part on size, the nanoparticles of the first material nucleated by the nanoparticles of the second material.
16. The method of claim 1 , further comprising depositing onto a substrate the nanoparticles of the first material nucleated by the nanoparticles of the second material.
17. The method of claim 1 , wherein the performing of the first ablation comprises shock heating the microparticles of the first material to form the nanoparticles of the first material, and wherein the performing of the second ablation comprises vaporizing the nanoparticles of the first material to form a vapor of the first material.