Glass mat laminate comprised of polymerizable cyclic polyester oligomers suitable for composites with a class-A surface
A composition of a fiber reinforced multi-layered laminate that when compression-molded forms a composite having a Class-A surface that is resin rich. The fiber reinforced multi-layered laminate has an outer layer of a cyclic polyester oligomer containing a latent polymerization catalyst; a glass mat; a core layer of a cyclic polyester oligomer containing a latent polymerization catalyst; a second glass mat, and another outer layer of a cyclic polyester oligomer containing a latent polymerization catalyst. When compression molded, the combination of heat and pressure force the core layer through the permeable glass mats and toward the surface. The latent polymerization catalyst initiates polymerization of the cyclic polyester oligomer forming a Class-A surface that is resin rich. The core layer of a cyclic polyester oligomer thoroughly permeates the reinforcing fiber forming a composite having a middle, with a nearly uniform mixture of reinforced glass fiber and thermoplastic in situ polymerized resin.
1. A composition of a fiber reinforced laminate that, on processing with heat and compression, forms a composite with a substantially fiber free surface, said composition comprising:
a) a first extruded layer comprised of a cyclic polyester oligomer containing a latent polymerization catalyst;
b) a first permeable layer of reinforcing fibers;
c) a polyester polymers, or a polycarbonate, or a blend thereof:
wherein the latent polymerization catalyst is activated when exposed to temperatures in excess of 200° C., which initiates polymerization of the cyclic polyester oligomer therein forming a polymerized resin; and
wherein, when processed at temperatures above 200° C., the cyclic polyester oligomer flows impregnating the permeable layer of reinforcing fibers, polymerizes, and forming the composite that has a substantially fiber free surface, wherein the cyclic polyester oligomer is selected from the group consisting of cyclic poly(1,4-butylene terephthalate) (CPBT), poly(1,3-propylene terephthalate) (CPPT), poly(1,4-cyclohexylenedimethylene terephthalate) (CPCT), poly(ethylene terephthalate) (CPET), poly(1,2-ethylene 2,6-naphthalenedicarboxylate) (CPEN), polycaprolactone (CPCL) oligomers, and copolyester oligomers comprising two or more of the above monomer repeat units, wherein the composition is further comprised of a linear polyester oligomer, or a polycarbonate oligomer, or a blend thereof.
2. The composition, as claimed in claim 1 , wherein the cyclic polyester oligomer is substantially cyclic poly(1,4-butylene terephthalate).
3. The composition, as claimed in claim 2 , wherein the linear polyester oligomer is substantially polycaprolactone (PCL).
4. The composition, as claimed in claim 3 , wherein the permeable layer of reinforcing fibers is substantially a fiberglass mat.
5. The composition, as claimed in claim 4 , wherein the latent polymerization catalyst is substantially dibutyl tin dioxide diluted in a plasticizer.
6. The composition, as claimed in claim 4 , wherein the polymerized resin is a tere- polymer of polycaprolactone and poly(1,4-butylene terephthalate).
7. A composition of a fiber reinforced laminate that, on processing with heat and compression, forms a composite with a substantially fiber free surface, said composition comprising:
a) a first extruded layer comprised of a cyclic polyester oligomer containing a latent polymerization catalyst;
b) a first permeable layer of reinforcing fibers;
c) wherein the composition is further comprised of reactive functional groups additives selected from the group consisting of monomers, dimers, trimers, tetramers, or any combination thereof, wherein the reactive functional groups are selected from the group consisting of esters, eposies, anhydrides, lactones and blocked isocyanates;
wherein the latent polymerization catalyst is activated when exposed to temperatures in excess of 200° C., which initiates polymerization of the cyclic polyester oligomer therein forming apolymerized resin; and, wherein, when processed at temperatures above 200° C., the cyclic polyester oligomer flows impregnating the permeable layer of reinforcing fibers, polymerizes, and forming the composite that has a substantially fiber free surface.
8. A composition of a fiber reinforced laminate, wherein upon processing, with heat and compression, forms a composite with a substantially fiber free surface, said composition comprising:
a) at least two extruded layers comprised of a cyclic polyester oligomer containing a latent polymerization catalyst;
b) at least two permeable layers of reinforcing fibers;
c)further comprised of reactive functional groups additives selected from the group consisting of plasticizers, monomers, dimers, trimers, tetramers, or any combination thereof, wherein the reactive functional groups are slected from the group consisting of esters, epoxies, anhydrides, lactones and blocked isocyanates;
wherein the latent polymerization catalyst is activated when exposed to temperatures in excess of 200° C.; and
wherein, when processed at temperatures above 200° C., the cyclis polyester oligomer flows impregnating the permeable layer of reinforcing fibers, polymerizes, and forming the composite that has a substantially fiber free surface.
9. A composition according to claim 8 , wherein the composition is further comprised of additives selected from the group consisting of extenders which are fillers, antioxidants, UV stabilizers, thermal stabilizers, flame retardants, desiccants, buffers, antimicrobials, fillers which are reinforcing, glass beads, colorants, antimicrobial agents, dyes, bluing agents, fluorescing agents, pigments, plasticizers, oils, impact modifiers, processing aides selected for the group consisting of waxes, fluorinated compounds, silicone compounds, surfactants, polymeric processing aides, density modifiers, such as phenolic beads and micro-balloons, crushed stone, fumed silica, titanium dioxide, calcium carbonate, fly ash, talc, clay, carbon blacks, graphite, barium sulfate, quartz, and IR absorbent compounds to facilitate heating including metal oxides.