Composite article providing blast mitigation and method for manufacturing same
A composite article and method for manufacturing the same are disclosed. In one embodiment, a polyurethane-polyurea layer is disposed on a substrate. The polyurethane-polyurea layer includes a reaction product of an isocyanate component having from about 10% to about 90% of a toluene diisocyanate, by weight of the isocyanate component, and an isocyanate-reactive component having amine-terminated and/or hydroxyl-terminated compounds. The polyurethane-polyurea layer provides blast and fragment protection from explosive devices as well as ballistic mitigation.
1. A composite article providing blast mitigation, the composite article comprising:
a fixed structure including a substrate, the fixed structure being subject to blast exposure, the fixed structure being selected from the group consisting of walls, floors, roofs, exterior ceilings, interior ceilings, dikes, dams, reservoirs, containment walls, Jersey barriers, barricades, bunkers, bridges, roadways, aqueducts, flumes, beams, columns, and piers; and
a polyurethane-polyurea layer bonded to the surface of the substrate and oriented in a direction of anticipated blast exposure to provide blast and fragment protection, the polyurethane-polyurea layer including a reaction product of (a) an isocyanate component comprising a toluene diisocyanate prepolymer having from about 50% to about 90% of a toluene diisocyanate, by weight of the toluene diisocyanate prepolymer, and a polyol having a functionality from about 2 to about 3 and being selected such that the toluene diisocyanate prepolymer has an NCO group content from about 2.5% to about 12%, and (b) an isocyanate-reactive component, the reaction product being the result of impingement mixing by plural component spray equipment using pressures between about 2,000 psi and about 3,000 psi and temperatures in the range of about 145° F. to 190° F., the polyurethane-polyurea having the following characteristics:
a gel time between 5 and 9 seconds,
a tack-free time between 10 and 16 seconds,
a tensile strength between 4,109 psi and 4,295 psi, and
a tear strength of between 520 pli and 578 pli.
2. The composite article as recited in claim 1 , wherein the isocyanate-reactive component comprises a compound selected from the group consisting of amine-terminated compounds, hydroxyl-terminated compounds, and blends of amine-terminated and hydroxyl-terminated compounds.
3. The composite article as recited in claim 1 , wherein the substrate comprises a material selected from the group consisting of ceramics, composites, concretes, construction boards, earth building materials, glasses, metals, polymers, and woods.
4. A composite article providing blast mitigation, the composite article comprising:
a first substrate forming a portion of a fixed structure, the first substrate being oriented in a direction of anticipated blast exposure, the fixed structure being subject to blast exposure, the fixed structure being selected from the group consisting of walls, floors, roofs, exterior ceilings, interior ceilings, dikes, dams, reservoirs, containment walls, Jersey barriers, barricades, bunkers, bridges, roadways, aqueducts, flumes, beams, columns, and piers;
a second substrate forming a portion of the fixed structure; and
a polyurethane-polyurea layer adhering the first substrate to the second substrate while providing blast and fragment protection, the polyurethane-polyurea layer including a reaction product of (a) an isocyanate component comprising a toluene diisocyanate prepolymer having from about 50% to about 90% of a toluene diisocyanate, by weight of the toluene diisocyanate prepolymer, and a polyol having a functionality from about 2 to about 3 and being selected such that the toluene diisocyanate prepolymer has an NCO group content from about 2.5% to about 12%, and (b) an isocyanate-reactive component, the reaction product being the result of impingement mixing by plural component spray equipment using pressures between about 2,000 psi and about 3,000 psi and temperatures in the range of about 145° F. to 190° F., the polyurethane-polyurea having the following characteristics:
a gel time between 5 and 9 seconds,
a tack-free time between 10 and 16 seconds,
a tensile strength between 4,109 psi and 4,295 psi, and
a tear strength of between 520 phi and 578 pli.
5. The composite article as recited in claim 4 , wherein the isocyanate-reactive component comprises a compound selected from the group consisting of amine-terminated compounds, hydroxyl-terminated compounds, and blends of amine-terminated and hydroxyl-terminated compounds.
6. The composite article as recited in claim 4 , wherein the first substrate comprises a material selected from the group consisting of ceramics, composites, concretes, construction boards, earth building materials, glasses, metals, polymers, and woods.
7. The composite article as recited in claim 4 , wherein the first and second substrates comprise substantially identical materials.
8. The composite article as recited in claim 4 , wherein the first and second substrates comprise different materials.
9. A method of manufacturing a composite article providing blast mitigation, the method comprising:
providing an isocyanate component comprising a toluene diisocyanate prepolymer having from about 50% to about 90% of a toluene diisocyanate, by weight of the toluene diisocyanate prepolymer, and a polyol having a functionality from about 2 to about 3 and being selected such that the toluene diisocyanate prepolymer has an NCO group content from about 2.5% to about 12%;
providing an isocyanate-reactive component;
reacting the isocyanate component and the isocyanate-reactive component to form a polyurethane-polyurea elastomer, the reaction product being the result of impingement mixing by plural component spray equipment using pressures between about 2,000 psi and about 3,000 psi and temperatures in the range of about 145° F. to 190° F.;
providing the polyurethane-polyurea elastomer with the following characteristics: a gel time between 5 and 9 seconds, a tack-free time between 10 and 16 seconds, a tensile strength between 4,109 psi and 4,295 psi, and a tear strength of between 520 phi and 578 phi; and
disposing the polyurethane-polyurea elastomer onto a substrate, the substrate being a portion of a fixed structure subject to blast exposure, the fixed structure being selected from the group consisting of walls, floors, roofs, exterior ceilings, interior ceilings, dikes, dams, reservoirs, containment walls, Jersey barriers, barricades, bunkers, bridges, roadways, aqueducts, flumes, beams, columns, and piers.
10. The method as recited in claim 9 , wherein disposing the polyurethane-polyurea elastomer onto a substrate further comprises disposing the polyurethane-polyurea elastomer onto a material selected from the group consisting of ceramics, composites, concretes, construction boards, earth building materials, glasses, metals, polymers, and woods.
11. The method as recited in claim 9 , further comprising, upon manufacturing the composite article, impacting the composite article with a blast.
12. A method of manufacturing a composite article providing blast mitigation, the method comprising:
providing an isocyanate component comprising a toluene diisocyanate prepolymer having from about 50% to about 90% of a toluene diisocyanate, by weight of the toluene diisocyanate prepolymer, and a polyol having a functionality from about 2 to about 3 and being selected such that the toluene diisocyanate prepolymer has an NCO group content from about 2.5% to about 12%;
providing an isocyanate-reactive component;
reacting the isocyanate component and the isocyanate-reactive component to form a polyurethane-polyurea elastomer, the reaction product being the result of impingement mixing by plural component spray equipment using pressures between about 2,000 psi and about 3,000 psi and temperatures in the range of about 145° F. to 190° F.;
providing the polyurethane-polyurea elastomer with the following characteristics: a gel time between 5 and 9 seconds, a tack-free time between 10 and 16 seconds, a tensile strength between 4,109 psi and 4,295 psi, and a tear strength of between 520 phi and 578 phi; and
disposing the polyurethane-polyurea elastomer onto a first substrate, the first substrate being a portion of a fixed structure subject to blast exposure, the fixed structure being selected from the group consisting of walls, floors, roofs, exterior ceilings, interior ceilings, dikes, dams, reservoirs, containment walls, Jersey barriers, barricades, bunkers, bridges, roadways, aqueducts, flumes, beams, columns, and piers; and
adhering a second substrate to the polyurethane-polyurea elastomer such that the polyurethane-polyurea elastomer is interposed between the first substrate and the second substrate, the second substrate forming a portion of the fixed structure.
13. The method as recited in claim 12 , wherein disposing the polyurethane-polyurea elastomer onto a first substrate further comprises disposing the polyurethane-polyurea elastomer onto a material selected from the group consisting of ceramics, composites, concretes, construction boards, earth building materials, glasses, metals, polymers, and woods.
14. The method as recited in claim 12 , further comprising selecting the second substrate of a substantially identical material to the first substrate.
15. The method as recited in claim 12 , further comprising selecting the second substrate of a different material than the first substrate.
16. The method as recited in claim 12 , further comprising, upon manufacturing the composite article, impacting the composite article with a blast.