The present invention is a substantially non-adhesive elastic gelatin matrix. The matrix is both non-adhesive to wounds, tissues and organs and is also elastic such that it is flexible. The matrix is a lyophilized mixture of protein(s), polymer(s), cross-linking agent(s) and optional plasticizer(s). The invention also provides methods for making the non-adhesive elastic gelatin matrix.
1. An elastic non-adhesive protein matrix comprising:
(a) about 50-90% by wgt of one or more proteins selected from the group consisting of collagen, and denatured collagen and mixtures thereof;
(b) about 10-40% by wgt of one or more biocompatible polymers selected from the group consisting of polyetheylene glycol, poly-L-lysine, alginate, chitosan, hyaluronic acid, and chondroitin sulfate and mixtures thereof; and
(c) about 0.5-5% by wgt of diglycidyl ether;
wherein the matrix is lyophilized after addition of (c) to result in a matrix that is non-adherent to wounds tissues, and organs and can be removed after 24 hours.
2. The matrix of claim 1 , wherein the matrix additionally comprises one or more plasticizers.
3. The matrix of claim 1 , wherein said matrix contains less than 10% moisture content.
4. The matrix of claim 2 , wherein said plasticizer is provided in an amount of up to 10% by weight of said matrix.
5. The matrix of claim 1 , wherein said matrix is provided as a film, sheet, tube or sponge.
6. The matrix of claim 1 , wherein said matrix is provided together with a material selected from the group consisting of polymer sheets, polymer films, threads, silicone membranes, silicone meshes, polyurethane, polyethylene, polyethylene terephthalate, nylon, silk, and cellulose and combinations thereof.
7. The matrix of claim 1 , wherein said matrix is provided as a wound dressing, wound barrier, tissue cover or vascular cover.
8. The matrix of claim 1 , wherein said matrix absorbs exudates.
9. The matrix of claim 1 , wherein said matrix promotes a moist environment.
10. A method for making a non-adhesive elastic protein matrix, the method comprising, in order, the steps of:
(a) mixing collagen, denatured collagen, or a combination thereof in a solution and heating said solution;
(b) adding polyethylene glycol, poly-L-lysine, alginate, chitosan, hyaluronic acid, or chondroitin sulfate or any combination thereof to the solution of (a);
(c) adding 1-[3-(dimethylamino)propyl]-3-ethyl carbodiimide (EDC), N-hydroxysuccinimide (NHS), formaldehyde, glutaraldehyde, a polyaziridine, or a diglycidyl ether or any combination thereof to the solution of (b) under conditions that induce protein cross-linking while maintaining a solution;
(d) mixing (c) until a pourable gel is formed;
(e) cooling the gel of (d); and
(f) lyophilizing the cooled gel of (e) to form the non-adhesive elastic protein matrix;
wherein the non-adhesive elastic protein matrix comprises:
about 50-90% by wgt collagen or denatured collagen or a combination thereof;
about 10-40% by wgt polyetheylene glycol, poly-L-lysine, alginate, chitosan, hyaluronic acid, or chondroitin sulfate or any combination thereof;
about 0.5-5% by wgt of 1-[3-(dimethylamino)propyl]-3-ethyl carbodiimide (EDC), N-hydroxysuccinimide (NHS), formaldehyde, glutaraldehyde, a polyaziridine, or a diglycidyl ether or any combination thereof; and
wherein the matrix is non-adherent to wounds, tissues and organs and can be removed after 24 hours.
11. The method of claim 10 , wherein one or more plasticizers is added to the solution of (b), and/or the solution of (c), or both.
12. The method of claim 10 , wherein the one or more cross-linking agents comprise diglycidyl ether.
13. A method for making a non-adhesive elastic protein matrix, the method comprising, in order, the steps of:
(a) mixing 0.5-30% by wgt collagen or denatured collagen; up to 10% by wgt of one or more biocompatible polymers; 0.1-2% by wgt of one or more cross-linking agents; about 50% to about 99% by weight solvent; and optionally up to 5% by weight plasticizer in a solution until a pourable gel is formed;
(b) cooling the gel of (a); and
(c) lyophilizing the cooled gel of (b) to form the non-adhesive elastic protein matrix that is removable after 24 hours.
14. The method of claim 13 , wherein the one or more cross-linking agents comprise diglycidyl ether.
15. A method for making a non-adhesive elastic protein matrix, the method comprising, in order, the steps of:
(a) mixing collagen or denatured collagen or a combination thereof in a solution and heating said solution;
(b) adding polyethylene glycol, poly-L-lysine, alginate, chitosan, hyaluronic acid, or chondroitin sulfate or any combination thereof to the solution of (a);
(c) adding one or more cross-linking agents selected from the group consisting of 1-[3-(dimethylamino)propyl]-3-ethyl carbodiimide (EDC), N-hydroxysuccinimide (NHS), formaldehyde, glutaraldehyde, a polyaziridine, and a diglycidyl ether or any combination thereof to the solution of (b);
(d) cooling the solution of (c); and
(e) lyophilizing the cooled solution of (d) to form the non-adhesive elastic protein matrix that can be removed after 24 hours.
16. The method of claim 15 , wherein the one or more cross-linking agents comprise diglycidyl ether.