Silver oxide powder for alkaline battery and method of producing the same
Alkaline battery silver oxide powder when soaked in a 50° C. KOH 40% aqueous solution for 24 hours experiences dissolution of Ag into the solution of 40 mg/L. Alkaline battery silver oxide powder exhibits substantially no Ag peak by X-ray diffraction even after soaking in a 50° C. KOH 40% aqueous solution for 72 hours. This powder has a crystallite size calculated from the half value breadth of the (111) plane peak by powder X-ray diffraction of greater than 250 Angstrom and equal to or less than 1000 Angstrom, particle diameter such that the average diameter of secondary particles is equal to or greater than 1 μm and equal to or less than 500 μm and that of primary particles forming the secondary particles is equal to or greater than 0.1 μm and equal to or less than 10.0 μm, and specific surface area of 5 m 2 /g or less.
1. An alkaline battery comprising a negative electrode active material, a positive electrode active material, an alkaline electrolyte, a separator and a can body, which alkaline battery uses an alloy composed mainly of Zn as the negative electrode active material, an aqueous solution of NaOH, KOH or a mixture thereof as the electrolyte, and a silver oxide as the positive electrode active material, wherein the silver oxide powder is one whose crystallite size calculated from a half value breadth of the (111) plane peak by powder X-ray diffraction is greater than 250 Angstrom and equal to or less than 1000 Angstrom and whose total content of nitrate ions and sulfate ions is 0.01% or less, and that when a 5 g of its sample is soaked in 50 cc of 50° C. KOH 40% aqueous solution for 24 hours, it experiences dissolution of Ag into the solution of 40 mg/L or less.
2. An alkaline battery comprising a negative electrode active material, a positive electrode active material, an alkaline electrolyte, a separator and a can body, which alkaline battery uses an alloy composed mainly of Zn as the negative electrode active material, an aqueous solution of NaOH, KOH or a mixture thereof as the electrolyte, and a silver oxide powder as the positive electrode active material, wherein the silver oxide powder is one whose crystallite size calculated from a half value breadth of the (111) plane peak by powder X-ray diffraction is greater than 250 Angstrom and equal to or less than 1000 Angstrom and whose total content of nitrate ions and sulfate ions is 0.01% or less, and wherein substantially no Ag peak by X-ray diffraction is exhibited even after soaking in a 50° C. KOH 40% aqueous solution for 72 hours.
3. An alkaline battery comprising a negative electrode active material, a positive electrode active material, an alkaline electrolyte, a separator and a can body, which alkaline battery uses an alloy composed mainly of Zn as the negative electrode active material, an aqueous solution of NaOH, KOH or a mixture thereof as the electrolyte, and a silver oxide powder as the positive electrode active material, wherein the silver oxide powder is one whose crystallite size calculated from a half value breadth of the (111) plane peak by powder X-ray diffraction is greater than 250 Angstrom and equal to or less than 1000 Angstrom and whose total content of nitrate ions and sulfate ions is 0.01% or less, whose average diameter of secondary particles is equal to or greater than 1 μm and equal to or less than 500 μm, that of primary particles forming the secondary particles is equal to or greater than 0.1 μm and equal to or less than 10.0 μm, specific surface area by the BET method is 5 m 2 /g or less, and when a 5 g of its sample is soaked in 50 cc of 50° C. KOH 40% aqueous solution for 24 hours, it experiences dissolution of Ag into the solution of 40 mg/L or less.
4. An alkaline battery silver oxide powder for use as a positive electrode active material of a silver oxide battery in which zinc is used as a negative electrode active material, wherein the silver oxide powder is one that when a 5 g of its sample is soaked in 50 cc of 50° C. KOH 40% aqueous solution for 24 hours, it experiences dissolution of Ag into the solution of 40 mg/L or less and whose crystallite size calculated from the half value breadth of the (111) plane peak by powder X-ray diffraction is greater than 250 Angstrom and equal to or less than 1000 Angstrom.
5. An alkaline battery silver oxide powder for use as a positive electrode active material of a silver oxide battery in which zinc is used as a negative electrode active material, wherein the silver oxide powder is one that when a 5 g of its sample is soaked in 50 cc of 50° C. KOH 40% aqueous solution for 24 hours, it experiences dissolution of Ag into the solution of 40 mg/L or less and whose crystallite size calculated from the half value breadth of the (111) plane peak by powder X-ray diffraction is greater than 250 Angstrom and equal to or less than 1000 Angstrom, and that the average diameter of secondary particles is equal to or greater than 1 μm and equal to or less than 500 μm, that of primary particles forming the secondary particles is equal to or greater than 0.1 μm and equal to or less than 10.0 μm, and specific surface area by the BET method is 5 m 2 /g or less.