Nanostructured bioactive materials prepared by dual nozzle spray drying techniques
Nano-particles of calcium and phosphorous compounds are made in a highly pure generally amorphous state by spray drying a weak acid solution of said compound and evaporating the liquid from the atomized spray in a heated column followed by collection of the precipitated particles. Hydroxyapatite (HA) particles formed by such apparatus and methods are examples of particle manufacture useful in bone and dental therapies. Dual nozzle spraying techniques are utilized for generally insoluble compounds.
1. A method for manufacture of high purity, nanosized particles of a partially water soluble compound for in vivo use, said compound comprised of a first component and a second component, said components capable of precipitation in chemical combination as solid particles of said compound, said method comprising the steps of;
(a) forming a first solely liquid solution of said first component of said compound and a weak acid liquid solvent of said first component;
(b) forming a second solely liquid solution of said second component of said compound and a second liquid solvent of said second compartment, said first and second solutions each including ionic species in solution derived from the first and second compounds respectively;
(c) directing said first and second solutions with a gas through a respective first and a second spray nozzle to generally simultaneously and separately atomize each of said first and second solutions into a spray;
(d) directing and combining said first and second atomized solutions into a common chamber at a temperature to evaporate the first and second liquid solvents and effect thereby chemical combination of ionic species derived from said first and second components to form said compound as dry nano particles; and
(e) collecting said nano particles.
2. The method of claim 1 wherein said collecting step includes electrostatic precipitation of dried particles.
3. The method of claim 1 wherein said compound is selected from the group consisting of FA, CaF 2 , CSH and CP; and said second solvent is selected from the group consisting of water, a weak acid, and a base.
4. The method of claim 3 wherein said weak acid solvent has a pH of about 4.0.
5. The process of claim 1 wherein in the step of atomizing at least one of said solutions comprises spraying through at least one of said nozzles having an orifice with an effective discharge opening of less than about 15 microns.
6. The process of claim 1 wherein the components comprise a first solution of Ca(OH) 2 and a second solution of H 3 PO 4 , each solution being separately discharged substantially simultaneously through a separate one of said spray nozzles into the same chamber to form Ca 5 (PO 4 ) 3 OH particles.
7. The process of claim 1 wherein the components comprise a first solution of Ca(OH) 2 and a second solution of H 3 PO 4 and HF, each solution being separately discharged into the chamber through a separate one of said spray nozzles substantially simultaneously to form (Ca 5 (PO 4 ) 3 F) particles.
8. The process of claim 1 wherein the components comprise a first solution of Ca(OH) 2 and a second solution of NH 4 F, each solution being separately discharged into the chamber through a separate one of said spray nozzles substantially simultaneously to form CaF 2 particles.
9. The process of claim 1 wherein the components comprise a first solution of Ca(OH) 2 and a second solution of SiO 2 in one normal NH 4 OH, each one of said solutions being discharged substantially simultaneously into said chamber to form CSH particles.
10. The method of claim 1 including the further step of compounding said particles in a formulation selected from the group consisting of a dental rinse and a dentifrice.
11. The method of claim 10 including the step of compounding a dental rinse and employing the dental rinse in vivo as an oral rinse.