Silicone lubricant with good wetting on PET surfaces
The passage of a container along a conveyor is lubricated by applying to the container or conveyor a composition comprising a water-miscible silicone material wherein the composition has good wetting to polyethylene terephthalate surfaces. The compatibility of the lubricating composition with polyethylene terephthalate is increased because the wetting of the composition to polyethylene terephthalate is improved.
1. A method for lubricating the passage of a container along a conveyor, comprising applying an aqueous, phase-stable lubricant composition to at least a portion of the container—contacting surface of the conveyor, the aqueous, phase-stable lubricant composition comprising
from about 0.0005 wt. % to about 5.0 wt. % of a water-miscible silicone material; and
from about 0.01 wt. % to about 0.50 wt. % of at least one wetting agent selected from the group consisting of fatty amine, alcohol ethoxylate, and mixtures thereof;
wherein the lubricant composition directly contacts the container, the lubricant composition forms a substantially contiguous coating which covers greater than 30% of the surface when coated and dried onto polyethylene terephthalate film, the contact angle between the lubricant composition and container is less than about 60 degrees.
2. The method of claim 1 , wherein the silicone material is selected from the group consisting of silicone emulsion, finely divided silicone powder, and silicone surfactant.
3. The method of claim 1 , wherein the lubricant composition further comprises one or more functional ingredients selected from the group of water-miscible lubricants, hydrophilic diluents, antimicrobial agents, stabilizing/coupling agents, detergents/dispersing agents, anti-wear agents, viscosity modifiers, sequestrants, corrosion inhibitors, and mixtures thereof.
4. The method of claim 1 , wherein the lubricant composition comprises from about 0.002 wt, % to about 0.5 wt, % of a water-miscible silicone material.
5. The method of claim 1 , wherein the container comprises one or more polymers selected from the group of polyethylene terephthalate, polyethylene naphthalate, and bisphenol A carbonate.
6. The method of claim 1 , wherein the contact angle between the lubricant composition and container is less than about 50 degrees.
7. The method of claim 1 , wherein the contact angle between the lubricant composition and container is less than about 40 degrees.
8. The method of claim 1 , wherein the lubricant composition is applied for a period of time and off for a period of time and the ratio of applied time to off time is at least 1:1.
9. The method of claim 1 , wherein the lubricant composition further comprises from about 0.02 wt, % to about 0.30% of at least one wetting agent.
10. A method for lubricating the passage of a container along a conveyor, comprising applying an aqueous, phase-stable lubricant composition to at least a portion of the container-contacting surface of the conveyor or to at least a portion of the conveyor-contacting surface of the container, the aqueous, phase-stable lubricant composition comprising
from about 0.0005% to about 5.0% of a water-miscible silicone material; and
from about 0.01 wt. % to about 0.50 wt. % of at least one wetting agent selected from the group consisting of fatty amine, alcohol ethoxylate, and mixtures thereof;
wherein the lubricant composition directly contacts the container, the lubricant composition forms a substantially contiguous coating which covers greater than about 30% of the surface when coated and dried onto polyethylene terephthalate film with a wet coating thickness of about 14 microns.
11. The method of claim 10 , wherein the silicone material is selected from the group consisting of silicone emulsion, finely divided silicone powder, and silicone surfactant.
12. The method of claim 10 , wherein the lubricant composition further comprises one or more functional ingredients selected from the group of water-miscible lubricants, hydrophilic diluents, antimicrobial agents, stabilizing/coupling agents, detergents/dispersing agents, anti-wear agents, viscosity modifiers, sequestrants, corrosion inhibitors, and mixtures thereof.
13. The method of claim 10 , wherein the lubricant composition comprises from about 0.002 wt, % to about 0.5 wt, % of a water-miscible silicone lubricant.
14. The method of claim 10 , wherein the container comprises one or more polymers selected from the group of polyethylene terephthalate, polyethylene naphthalate, and bisphenol A carbonate.
15. The method of claim 10 , wherein the lubricant composition forms a substantially contiguous coating which covers greater than about 50% of the surface when coated and dried onto polyethylene terephthalate film with a wet coating thickness of about 14 microns.
16. The method of claim 10 , wherein the lubricant composition forms a substantially contiguous coating which covers greater than about 70% of the surface when coated and dried onto polyethylene terephthalate film with a wet coating thickness of about 14 microns.
17. The method of claim 10 , wherein the lubricant composition is applied for a period of time and off for a period of time and the ratio of applied time to off time is at least 1:1.
18. The method of claim 10 , wherein the lubricant composition comprises from about 0.02 wt, % to about 0.30 wt, % of at least one wetting agent.
19. A method for lubricating the passage of a container along a conveyor, comprising applying aqueous, phase-stable lubricant composition to at least a portion of the container-contacting surface of the conveyor or to at least a portion of the conveyor-contacting surface of the container, the aqueous, phase-stable lubricant composition comprising
from about 0.0005 wt, % to about 5.0 wt, % of a water-miscible silicone material; and
from about 0.01 wt. % to about 0.50 wt. % of at least one wetting agent selected from the group consisting of fatty amine, alcohol ethoxylate, and mixtures thereof;
wherein the lubricant composition directly contacts the container, the foam profile for the composition is greater than about 1.1.
20. The method of claim 19 , wherein the silicone material is selected from the group consisting of silicone emulsion, finely divided silicone powder, and silicone surfactant.
21. The method of claim 19 , wherein the lubricant composition further comprises one or more functional ingredients selected from the group of water-miscible lubricants, hydrophilic diluents, antimicrobial agents, stabilizing/coupling agents, detergents/dispersing agents, anti-wear agents, viscosity modifiers, sequestrants, corrosion inhibitors and mixtures thereof.
22. The method of claim 19 , wherein the lubricant composition comprises from about 0.002 wt. % to about 0.5 wt. % of a water-miscible silicone material.
23. The method of claim 19 , wherein the container comprises one or more polymers selected from the group of polyethylene terephthalate, polyethylene naphthalate, and bisphenol A carbonate.
24. The method of claim 19 , wherein the foam profile for the composition is greater than about 1.3.
25. The method of claim 19 , wherein the foam profile for the composition is greater than about 1.5.
26. The method of claim 19 , wherein the lubricant composition is applied for a period of time and off for a period of time and the ratio of applied time to off time is at least 1:1.
27. The method of claim 19 , wherein the lubricant composition further comprises from about 0.02 wt. % to about 0.30 wt. % of at least one wetting agent.
28. A method for lubricating the passage of a container along a conveyor, comprising applying an aqueous, phase-stable lubricant composition to at least a portion of the container-contacting surface of the conveyor or to at least a portion of the conveyor-contacting surface of the container, the aqueous, phase-stable lubricant composition comprising from about 0.0005 wt. % to about 5.0 wt. % of a water-miscible silicone material, and from about 0.01 wt. % to about 0.50 wt. % of at least one wetting agent selected from the group consisting of a fatty amine, an alcohol ethoxylate and mixtures thereof, wherein the lubricant composition directly contacts the container, the contact angle between the lubricant composition and container is less than about 60 degrees.