Light-diffusing film having pores
Disclosed herein is a light-diffusing film having pores for use in a backlight unit of a TFT-LCD. The light-diffusing film having pores of this invention comprises a base sheet composed of a synthetic resin; a light-diffusing layer laminated on one surface of the base sheet and having pores formed by applying a composition including a light-diffusing resin and light-diffusing particles contained in the light-diffusing resin under controlled composition supply pressure of 1˜5 kgf/cm 2 and travel speed of the base sheet of 10˜200 m/min; and an antiblocking layer laminated on the other surface of the base sheet. According to this invention, the light-diffusing film has improved total light transmittance and light diffusibility owing to the pores formed in the light-diffusing layer, and is thus usefully applicable to a backlight unit of a TFT-LCD.
1. A method of manufacturing a light-diffusing film having pores, for a backlight unit of a TFT-LCD, the method comprising:
preparing a base sheet comprising a synthetic resin;
applying a composition including a light-diffusing resin and light-diffusing particles to a first surface of the base sheet under a composition supply pressure of 1 to 5 kgf/cm 2 and at a travel speed of 10 to 200 m/min of the base sheet to form a light-diffusing layer having pores; and
applying a composition including an antiblocking resin and antiblocking particles to a second surface of the base sheet to laminate an antiblocking layer on the second surface of the base sheet.
2. The method of manufacturing a light-diffusing film as set forth in claim 1 , wherein the light-diffusing layer is 0.2 to 500 μm thick.
3. The method of manufacturing a light-diffusing film as set forth in claim 1 , wherein the antiblocking layer is 0.1 to 100 μm thick.
4. The method of manufacturing a light-diffusing film as set forth in claim 1 , wherein the composition comprises 100 parts by weight of the light-diffusing resin and 0.1 to 1000 parts by weight of the light-diffusing particles.
5. The method of manufacturing a light-diffusing film as set forth in claim 1 , wherein the composition further comprises 0.01 to 10 parts by weight of a foaming agent.
6. The method of manufacturing a light-diffusing film as set forth in claim 5 , wherein the foaming agent comprises any inorganic foaming agent selected from the group consisting of carbonium carbonate, ammonium azoate, sodium borohydride, azides; and mixtures thereof.
7. The method of manufacturing a light-diffusing film as set forth in claim 5 , wherein the foaming agent comprises any one organic foaming agent selected from the group consisting of chlorofluorocarbons, azo compounds, hydrazide compounds, and nitroso compounds; and mixtures thereof.
8. The method of manufacturing a light-diffusing film as set forth in claim 1 , wherein the light-diffusing particles are selected from the group consisting of acrylic resin, polyurethane, polyvinyl chloride, polystyrene, polyacrylonitrile, polyamide, and polymethylmethacrylate.