Silver powder and method for producing same
View Patent ↗After a reducing agent is added to a water reaction system containing silver ions to deposit silver particles by reduction, the silver particles are dried to obtain a silver powder which is heat-treated at a temperature of higher than 100° C. and lower than 400° C. The silver powder thus heat-treated has a maximum coefficient of thermal expansion of not greater than 1.5% at a temperature of 50° C. to 800° C., and has no heating peak when the silver powder is heated from 50° C. to 800° C. The silver powder has an ignition loss of not greater than 1.0% when the silver powder is ignited until the weight of the silver powder is constant at 800° C. The silver powder has a tap density of not less than 2 g/cm 3 and a BET specific surface area of not greater than 5 m 2 /g.
1. A method for producing a spherical silver powder, said method comprising the steps of:
preparing a water reaction system containing silver ions;
adding a reducing agent to said water reaction system containing silver ions to deposit silver particles by reduction, said reducing agent being at least one selected from the group consisting of ascorbic acid, alkanol amine, hydroquinone, hydrazine and formalin;
drying said silver particles to produce a spherical silver powder; and
heat-treating said spherical silver powder for decreasing the maximum coefficient of thermal expansion thereof while maintaining the spherical shape thereof, to cause said spherical silver powder to have a maximum coefficient of thermal expansion of not greater than 1.5% at a temperature of 50° C. to 800° C.
2. A method for producing a silver powder as set forth in claim 1 , wherein the heat-treated silver powder has an ignition loss of not greater than 1.0% when said silver powder is ignited until the weight of the silver powder is constant at 800° C.
3. A method for producing a silver powder as set forth in claim 1 , wherein the heat-treated silver powder has no heating peak when the silver powder is heated from 50° C. to 800° C.
4. A method for producing a silver powder as set forth in claim 1 , wherein the heat-treated spherical silver powder has a tap density of not less than 2 g/cm 3 , and a BET specific surface area of not greater than 5 m 2 /g.
5. A method for producing a spherical silver powder, said method comprising the steps of:
preparing a water reaction system containing silver ions;
adding a reducing agent to said water reaction system containing silver ions to deposit silver particles by reduction, said reducing agent being at least one selected from the group consisting of ascorbic acid, alkanol amine, hydroquinone, hydrazine and formalin;
drying said silver particles to produce a spherical silver powder; and
heat-treating said spherical silver powder at a temperature of 150 to 250° C. for decreasing the maximum coefficient of thermal expansion thereof while maintaining the spherical shape thereof, to cause said spherical silver powder to have a maximum coefficient of thermal expansion of not greater than 1.5% at a temperature of 50° C. to 800° C.
6. A method for producing a silver powder as set forth in claim 5 , wherein a dispersing agent is added to said water reaction system before or after said silver particles are deposited.
7. A method for producing a silver powder as set forth in claim 6 , wherein said dispersing agent is at least one selected from the group consisting of fatty acids, fatty acid salts, surface active agents, organic metals, chelating agents and protective colloids.
8. A method for producing a silver powder as set forth in claim 5 , wherein said reducing agent is added at a rate of not lower than 1 equivalent/minute with respect to the content of silver in said water reaction system containing silver ions.
9. A method for producing a silver powder as set forth in claim 5 , wherein the heat-treated silver powder has an ignition loss of not greater than 1.0% when said silver powder is ignited until the weight of the silver powder is constant at 800° C.
10. A method for producing a silver powder as set forth in claim 5 , wherein the heat-treated silver powder has no heating peak when the silver powder is heated from 50° C. to 800° C.
11. A method for producing a silver powder as set forth in claim 5 , wherein the heat-treated spherical silver powder has a tap density of not less than 2 g/cm 3 , and a BET specific surface area of not greater than 5 m 2 /g.