Pressure-sensitive adhesive product
A pressure-sensitive adhesive product contains a substrate having formed on at least one surface thereof a pressure-sensitive adhesive layer, wherein the substrate is formed from a styrene-based resin composition and the pressure-sensitive adhesive layer is formed from an acrylic pressure-sensitive adhesive containing an acrylic polymer, a liquid paraffin, and a rosin-based tackifying resin. In the acrylic pressure-sensitive adhesive, the ratio of the liquid paraffin is preferably 6 to 50 parts by weight based on 100 parts by weight of the acrylic polymer and the ratio of the rosin-based tackifying resin is preferably 1 to 30 parts by weight based on 100 parts by weight of the acrylic polymer. The liquid paraffin may have a number-average molecular weight of 300 to 500 and may have a dynamic viscosity at 37.8° C. of 6 to 80 mm 2 /second.
1. A pressure-sensitive adhesive product comprising a substrate having formed on at least one surface thereof a pressure-sensitive adhesive layer, wherein the substrate is formed from a styrene-based resin composition and the pressure-sensitive adhesive layer is formed from an acrylic pressure-sensitive adhesive containing an acrylic polymer, a liquid paraffin, and a rosin-based tackifying resin, and
wherein in the acrylic pressure-sensitive adhesive, the ratio of the liquid paraffin is 6 to 50 parts by weight based on 100 parts by weight of the acrylic polymer, and
wherein the number-average molecular weight of the liquid paraffin is 300 to 500.
2. The pressure-sensitive adhesive product according to claim 1 , wherein in the acrylic pressure-sensitive adhesive, the ratio of the rosin-based tackifying resin is 1 to 30 parts by weight based on 100 parts by weight of the acrylic polymer.
3. The pressure-sensitive adhesive product according to claim 1 , wherein the dynamic viscosity of the liquid paraffin at 37.8° C. is 6 to 80 mm 2 /second.
4. The pressure-sensitive adhesive product according to claim 1 , wherein the rosin-based tackifying resin is a polymerized rosin.
5. The pressure-sensitive adhesive product according to claim 1 , wherein the acrylic pressure-sensitive adhesive further contains a crosslinking agent.
6. The pressure-sensitive adhesive product according to claim 5 , wherein the crosslinking agent is an isocyanate-based crosslinking agent.
7. The pressure-sensitive adhesive product according to claim 1 , wherein the acrylic polymer is an acrylic polymer containing an alkyl acrylate having an alkyl group of 8 or more carbon atoms as a main monomer component.
8. The pressure-sensitive adhesive product according to claim 1 , wherein the thickness of the pressure-sensitive adhesive layer is 5 to 50 μm.
9. The pressure-sensitive adhesive product according to claim 1 , wherein a 180° peeling adhesive force (tensile rate: 300 mm/minute, 23° C., 50% RH) is 2 to 5 N/20 mm.