Long fiber-reinforced thermoplastic compositions, articles made therefrom and methods of making the same
The present invention relates to a high melt flow thermoplastic resin filled with long fibers, such as long glass fibers, stainless steel fibers, carbon fibers, aramid fibers, or other like fibers, and having high melt flow properties. The high melt flow properties of the thermoplastic resin contribute to its ease of production, allowing for the production of long fiber-reinforced thermoplastic compositions having good dispersion and wet-out in the pellet and molded article, and characterized by low levels of loose fiber in the pellet and/or compound. Although any concentration of fibers may be present in the fiber-reinforced thermoplastic composition, the high melt flow thermoplastic resins are especially suitable for high concentrate long glass fiber-reinforced thermoplastic compositions.
1. A thermoplastic resin blend comprising:
a thermoplastic resin selected from the group consisting of polypropylene, low density polyethylene, ethylene vinyl acetate copolymer, ethylene acrylic acid copolymer, and blends thereof, having a melt flow above about 400 g/10 min as measured by ASTM D-1238-95, wherein the melt flow of polypropylene is measured at 230° C. and with a weight of 2.16 kg, the melt flow of low density polyethylene is measured at 190° C. and with a weight of 2.16 kg, the melt flow of ethylene vinyl acetate copolymer is measured at 125° C. and with a weight of 0.325 kg, and the melt flow of ethylene acrylic acid copolymer is measured at 125° C. with a weight of 0.325 kg; and
long fibers blended into the thermoplastic resin,
wherein the long fibers are present in a concentration of between about 8 percent and about 75 percent by volume.
2. The thermoplastic resin blend of claim 1 wherein the long fibers are selected from the group consisting of long glass fibers, stainless steel fibers, carbon fibers, aramid fibers, and mixtures thereof.
3. The thermoplastic resin blend of claim 1 wherein the long fibers are present in a concentration of between about 35 percent and about 65 percent by volume.
4. The thermoplastic resin blend of claim 1 wherein the long fibers are present in an amount of about 45 percent by volume.
5. The thermoplastic resin blend of claim 1 wherein the thermoplastic resin comprises polypropylene.
6. The thermoplastic resin blend of claim 1 wherein the thermoplastic resin is maleic anhydride modified polypropylene.
7. The thermoplastic resin blend of claim 1 wherein the thermoplastic resin has a melt flow of about 1100 g/10 min, as measured by ASTM D-1238-95.
8. A product made from the thermoplastic resin blend of claim 1 wherein said product is selected from the group consisting of an article and pellets.
9. A method of making a long fiber-reinforced thermoplastic resin blend comprising the steps of:
pulling a long fiber roving into an extruder, and
adding a thermoplastic resin to the long fiber roving to form a blend of long fibers and thermoplastic resin, wherein the thermoplastic resin is selected from the group consisting of polypropylene, low density polyethylene, ethylene vinyl acetate copolymer, ethylene acrylic acid copolymer and blends thereof, having a melt flow of above about 400 g/10 min, as measured by ASTM D-1238-95, wherein the melt flow of polypropylene is measured at 230° C. and with a weight of 2.16 kg, the melt flow of low density polyethylene is measured at 190° C. and with a weight of 2.16 kg, the melt flow of ethylene vinyl acetate copolymer is measured at 125° C. and with a weight of 0.325 kg, and the melt flow of ethylene acrylic acid copolymer is measured at 125° C. with a weight of 0.325 kg,
wherein the concentration of long fibers is between about 8 percent and about 75 percent by volume.
10. The method of claim 9 wherein the long fibers are selected from the group consisting of glass fibers, stainless steel fibers, carbon fibers, aramid fibers, and mixtures thereof.
11. The method of claim 9 wherein the concentration of long fibers is between about 35 percent and 65 percent by volume.
12. The method of claim 9 wherein the concentration of long fibers is about 45 percent by volume.
13. The method of claim 9 wherein the thermoplastic resin is selected from the group consisting of polypropylene, maleic anhydride modified polypropylene, or blends thereof.
14. The method of claim 9 wherein the thermoplastic resin has a melt flow rate of about 1100 g/10 min, as measured by ASTM D-1238-95.
15. A method of making a long fiber-reinforced thermoplastic resin blend comprising the steps of:
melting a thermoplastic resin selected from the group consisting of polypropylene, low density polyethylene, ethylene vinyl acetate copolymer, ethylene acrylic acid copolymer and blends thereof, having a melt flow of above about 400 g/10 min, as measured by ASTM D-1238-95, wherein the melt flow of polypropylene is measured at 230° C. and with a weight of 2.16 kg, the melt flow of low density polyethylene is measured at 190° C. and with a weight of 2.16 kg, the melt flow of ethylene vinyl acetate copolymer is measured at 125° C. and with a weight of 0.325 kg, and the melt flow of ethylene acrylic acid copolymer is measured at 125° C. with a weight of 0.325 kg, and
blending an amount of long fiber rovings into the thermoplastic resin to form a blend of long fibers and the thermoplastic resin,
wherein the blend of long fibers and thermoplastic resin has a concentration of long fibers of between about 8 percent and about 75 percent by volume.
16. The method of claim 15 wherein the long fibers are selected from the group consisting of long glass fibers, stainless steel fibers, carbon fibers, aramid fibers and mixtures thereof.
17. The method of claim 15 wherein the concentration of long fibers is between about 35 percent and 65 percent by volume.
18. The method of claim 15 wherein the concentration of long fibers is about 45 percent by volume.
19. The method of claim 15 wherein the thermoplastic resin is selected from the group consisting of polypropylene, maleic anhydride modified polypropylene, or blends thereof.
20. The method of claim 15 wherein the thermoplastic resin has a melt flow rate of about 1100 g/10 min, as measured by ASTM D-1238-95.