View Patent ↗The invention concerns a texturing film that is flexible enough to be applied to a clay model to add texture and color to the surface of the clay model, and a method of forming and using the texturing film. The texturing film may be formed of a latex-based paint mixed with a high-solids water-based butyl ester polymer peelable coating.
1. A method of forming a texturing film comprising the steps of:
(a) mounting a mold surface having a surface texture;
(b) applying a graining material onto the surface texture, with the graining material including a mixture of a latex based paint and a high-solids water-based butyl ester polymer peelable coating;
(c) waiting a predetermined amount of time for the graining material to partially polymerize, forming the texturing film; and
(d) removing the texturing film from the surface texture after step (c) and before the graining material fully polymerizes, to thereby retain flexibility for application to a surface while maintaining the surface texture.
2. The method of claim 1 wherein step (a) is further defined by the mold surface being mounted horizontally.
3. The method of claim 1 wherein step (a) is further defined by applying a parting agent to the mold surface, with the parting agent defining the surface texture.
4. The method of claim 3 wherein step (a) is further defined by the parting agent including a mixture of a polyethylene emulsion water-based mold release compound and water.
5. The method of claim 1 wherein step (b) is further defined by the mixture including equal parts by weight of the latex based paint and the high-solids water-based butyl ester polymer peelable coating.
6. The method of claim 1 wherein step (a) is further defined by applying a parting agent to the mold surface, with the parting agent defining the surface texture.
7. The method of claim 1 wherein step (c) is further defined by the predetermined amount of time being about two to five hours.
8. The method of claim 1 further including a step of: (e) applying the texturing film to a surface of a model before the graining material fully polymerizes.
9. The method of claim 1 further including a step of: (e) coloring the graining material prior to step (b).
10. A method of forming a texture on a surface comprising the steps of:
(a) mounting a mold surface having a surface texture;
(b) applying a first mixture of a latex based paint and a high-solids water-based butyl ester polymer peelable coating onto the surface texture, wherein the first mixture includes equal parts by weight of the latex based paint and the high-solids water-based butyl ester polymer peelable coating;
(c) waiting a first predetermined amount of time for the second mixture to form a texturing film;
(d) removing the texturing film from the surface texture after the first predetermined amount of time; and
(e) applying the texturing film to the surface before a second predetermined amount of time, which is greater than the first predetermined amount of time.
11. The method of claim 10 wherein step (c) is further defined by the first predetermined amount of time being about two to five hours.
12. The method of claim 10 wherein (e) is further defined by the second predetermined amount of time being about three weeks.
13. The method of claim 10 wherein the surface is a clay surface on a model of a portion of a vehicle.
14. The method of claim 10 wherein step (d) is further defined by removing the texturing film by rolling the texturing film about a generally cylindrical object.
15. The method of claim 10 wherein step (a) is further defined by applying a second mixture of a polyethylene emulsion water-based mold release compound and water to the mold surface, with second mixture defining the surface texture to which the first mixture is applied.