Compositions for protective films for optical discs
View Patent ↗Compositions for protective films include inorganic microparticles dispersed in an acrylic radical-based binder resin. Binder resins are formed from binder monomers including base components, scratch-resistant components and diluent components. Diluent components include diluent monomers having principal chain structures including a functional group having a cyclic structure or a branched carbon chain structure.
1. A composition for protective films for optical discs comprising inorganic microparticles dispersed in an acrylic radical-based binder resin, wherein:
the binder resin is formed from a binder monomer comprising a base component, a scratch-resistant component and a diluent component, wherein:
the base component is a monomer having a viscosity of less than 100 mPa·s;
the scratch-resistant component is a monomer having an acrylic functionality of three or more, wherein the scratch-resistant component monomer is selected from the group consisting of tris (acryloxyethyl) isocyanurate, dipentaerythritol penta- and hexa-acrylate, ditrimethylolpropane tetraacrylate, and pentaerythritol tetraacrylate; and
the diluent component comprises a diluent monomer, a principal chain structure of the diluent monomer comprising a functional group having a cyclic structure, the diluent component having a viscosity of 10 mPa·s or more and 50 mPa·s or less; and
a ratio of the base component, scratch-resistant component and diluent component in the binder monomer is from 70:5:25 to 60:20:20, and wherein
the composition for protective films for optical discs has a viscosity of 20 mPa·s or more and less than 100 mPa·s.
2. The composition according to claim 1 , wherein the diluent component comprises a monofunctional or bifunctional group.
3. The composition according to claim 1 , wherein a viscosity of the diluent component is less than a viscosity of the composition.
4. A protective film for optical discs, comprising a film obtained by curing a composition comprising inorganic microparticles dispersed in an acrylic radical-based binder resin formed from a binder monomer comprising a base component, a scratch-resistant component and a diluent component,
wherein:
the base component is a monomer having a viscosity of less than 100 mPa·s;
the scratch-resistant component is a monomer having an acrylic functionality of three or more, wherein the scratch-resistant component monomer is selected from the group consisting of tris (acryloxyethyl)isocyanurate, dipentaerythritol penta- and hexa-acrylate, ditrimethylolpropane tetraacrylate, and pentaerythritol tetraacrylate;
the diluent component comprises a diluent monomer, a principal chain structure of the diluent monomer comprising a functional group having a cyclic structure, but not a branched carbon chain structure, the diluent component having a viscosity of 10 mPa·s or more and 50 mPa·s or less; and
a ratio of the base component, scratch-resistant component and diluent component in the binder monomer is from 70:5:25 to 60:20:20, and wherein
the composition has a viscosity of 20 mPa·s or more and less than 100 mPa·s.
5. An optical disc, comprising:
a substrate having a recording pattern; and
a protective film formed on a surface of a readout side of the substrate; wherein:
the protective film is obtained by curing a composition comprising inorganic microparticles dispersed in an acrylic radical-based binder resin;
the binder resin is formed from a binder monomer comprising a base component, a scratch-resistant component and a diluent wherein:
the base component is a monomer having a viscosity of less than 100 mPa·s;
the scratch-resistant component is a monomer having an acrylic functionality of three or more, wherein the scratch-resistant component monomer is selected from the group consisting of tris (acryloxyethyl) isocyanurate, dipentaerythritol penta and hexa-acrylate, ditrimethylolpropane tetraacrylate, and pentaerythritol tetraacrylate; and
the diluent component comprises a monomer having a principal chain structure comprising a functional group having a cyclic structure,
the diluent component having a viscosity of 10 mPa·s or more and 50 mPa·s or less;
a ratio of the base component, scratch-resistant component and diluent component in the binder monomer is from 70:5:25 to 60:20:20, and wherein
the composition comprising inorganic microparticles dispersed in an acrylic radical-based binder resin has a viscosity of 20 mPa·s or more and less than 100 mPa's.