Carboxylic ester dispersant and sulfide phosphor paste composition having same
View Patent ↗Disclosed herein is a carboxylic ester dispersant shown in the following Formula 1 and a sulfide phosphor paste composition containing the dispersant. The dispersant improves the dispersibility of the sulfide phosphor paste composition and prevents oxidation by a solvent, thus improving processability and the luminescent properties of a phosphor film made from the paste and of a display produced using the film. In Formula 1, n is 1-20.
1. A sulfide phosphor paste composition comprising:
40-70 wt % of a phosphor;
0.1-3 wt % of a carboxylic ester dispersant of Formula 1 based on the phosphor, and
a balance of a binder solution including a solvent having an evaporation temperature of 150° C. or higher and an organic binder;
wherein n is 1-20.
2. The sulfide phosphor paste composition as set forth in claim 1 , wherein the binder solution comprises 1.5-5 wt % of organic binder and a balance of mixed solvent.
3. The sulfide phosphor paste composition as set forth in claim 1 , wherein the organic binder is selected from a group consisting of acryls, styrenes, celluloses, a methacrylic acid ester polymer, a styrene-acrylic ester copolymer, polystyrene, polyvinyl butyral, polyvinyl alcohol, polyethylene oxide, polypropylene carbonate, and polymethylmethacrylate.
4. The sulfide phosphor paste composition as set forth in claim 1 , wherein the solvent is one or more selected from a group consisting of an aromatic hydrocarbon compound including toluene and xylene, an ether compound including tetrahydrofuran and 1,2-butoxy ethane, a ketone compound including acetone and methyl ethyl ketone, an ester compound including ethyl acetate, butyl acetate, and butyl carbitol acetate (BCA), and an alcohol compound including isopropyl alcohol, diethylene glycol monobutyl ether, terpineol, and 2-phenoxyethanol.
5. The sulfide phosphor paste composition as set forth in claim 1 , wherein the organic binder is ethyl cellulose and the solvent is a mixed solvent of terpineol and butyl carbitol acetate.
6. The sulfide phosphor paste composition as set forth in claim 5 , wherein the mixed solvent includes terpineol and butyl carbitol acetate mixed with each other in a weight ratio of 1:1-1:2.5.
7. The sulfide phosphor paste composition as set forth in claim 1 , wherein the phosphor is selected from a group consisting of SrS:Eu 2+ , SrGaS:Eu 2+ , SrCaS:Eu 2+ , ZnS:Ag + , CaS:Eu 2+ , ZnS:Cu + Al 3+ ZnS:Ag + ,Cl − , La 2 O 2 S:Eu 3+ , Y 2 O 2 S:Eu 3+ , CaAl 2 S 4 , and BaAl 2 S 4 :Eu 2+ .
8. A phosphor film for a display produced using the phosphor paste composition according to claim 1 .
9. A display comprising the phosphor film of claim 8 .
10. The display as set forth in claim 9 , wherein the display is a cathodoluminescent display, a liquid crystal display, an electroluminescent display, a field emission display, or a vacuum fluorescent display.
11. The sulfide phosphor paste composition as set forth in claim 4 , wherein the solvent is one or more selected from the group consisting of toluene, xylene, tetrahydrofuran, 1,2-butoxy ethane, acetone, methyl ethyl ketone, ethylacetate, butyl acetate, butyl carbitol acetate (BCA), isopropyl alcohol, diethylene glycol monobutyl ether, terpineol, and 2-phenoxyethanol.