Method for producing pellets of liquid-crystalline polymer or pellets of liquid-crystalline polymer composition
The present invention provides a method for producing pellets or pellets of a liquid-crystalline polymer composition with a reduced amount of anionic impurities such as chloride, nitrate and sulfate ions. The present invention provides a method for producing pellets of a liquid-crystalline polymer, which comprises: providing a molten state liquid-crystalline polymer in a polycondensation reaction vessel, pulling out the liquid-crystalline polymer from a valve at the bottom of the reaction vessel through a die to give a strand of the polymer, cooling the strand on a water cooling conveyor positioned below the reaction vessel, and cutting the strand to give the pellets, wherein the cooling water for the strand is pure water whose electrical conductance is not more than 10 μS/cm.
1 . A method for producing pellets of a liquid-crystalline polymer, which comprises:
providing a molten state liquid-crystalline polymer in a polycondensation reaction vessel,
pulling out the liquid-crystalline polymer from a valve at the bottom of the reaction vessel through a die to give a strand of the polymer,
cooling the strand on a water cooling conveyor positioned below the reaction vessel, and
cutting the strand to give the pellets,
wherein the cooling water for the strand is pure water whose electrical conductance is not more than 10 μS/cm.
2 . The method according to claim 1 , wherein the flow amount of the cooling water is 1-20 parts by weight per one part by weight of the liquid-crystalline polymer pulled out from the reaction vessel.
3 . The method according to claim 1 , wherein the pellet of the liquid-crystalline polymer or liquid-crystalline polymer composition is a columnar pellet with a diameter of 2.5-4.0 mm and a height of 2.5-5.0 mm.
4 . A method for producing pellets of a liquid-crystalline polymer composition, which comprises:
pulling out a molten state liquid-crystalline polymer composition which comprises a liquid-crystalline polymer, filler and/or reinforcement from a kneading machine to give a strand of the polymer composition,
cooling the strand with cooling water to solidify the strand, and
cutting the strand to give the pellets,
wherein the cooling water for the strand is pure water whose electrical conductance is not more than 10 μS/cm.
5 . The method according to claim 4 , wherein flow amount of the cooling water is 0.01-2 parts by weight per one part by weight of the liquid-crystalline polymer composition pulled out from the kneading machine.
6 . The method according to any one of claim 4 , wherein the pellet of the liquid-crystalline polymer or liquid-crystalline polymer composition is a columnar pellet with a diameter of 2.5-4.0 mm and a height of 2.5-5.0 mm.
7 . A method for purifying pellets of a crude liquid-crystalline polymer or liquid-crystalline polymer composition, which comprises washing the pellets of the crude liquid-crystalline polymer or liquid-crystalline polymer composition containing more than 0.3 μg/g of chloride, nitrate and sulfate ions in total with pure water whose electrical conductance is not more than 10 μS/cm.
8 . The method according to claim 7 , wherein the pure water used for washing the pellets is 3-15 parts by weight per one part by weight of the pellets of the crude liquid-crystalline polymer or liquid-crystalline polymer composition.
9 . The method according to any one of claim 7 , wherein the pellet of the liquid-crystalline polymer or liquid-crystalline polymer composition is a columnar pellet with a diameter of 2.5-4.0 mm and a height of 2.5-5.0 mm.
10 . Pellets of a liquid-crystalline polymer or liquid-crystalline polymer composition, which contains not more than 0.3 μg/g of chloride, nitrate and sulfate ions in total.
11 . The pellets of the liquid-crystalline polymer or liquid-crystalline polymer composition according to claim 10 , which contains not more than 0.1 μg/g of each of chloride, nitrate and sulfate ions.