Yellow-emitting phosphor blend for electroluminescent lamps
A phosphor blend for an electroluminescent lamp is described that comprises a green-emitting electroluminescent phosphor and a red-emitting photoluminescent phosphor, the blend exhibiting an x color coordinate from 0.220 to 0.350 and a y color coordinate from 0.450 to 0.475 when stimulated by an electric field.
1. A phosphor blend for an electroluminescent lamp, comprising a green-emitting electroluminescent phosphor and a red-emitting photoluminescent phosphor, the blend exhibiting an x color coordinate from 0.220 to 0.350 and a y color coordinate from 0.450 to 0.475 when stimulated by an electric field.
2. The phosphor blend of claim 1 wherein the blend exhibits an x color coordinate from 0.235 to 0.335 and a y color coordinate from 0.460 to 0.465 when stimulated by an electric field.
3. The phosphor blend of claim 1 wherein the green-emitting electroluminescent phosphor is ZnS:Cu,Cl and the red-emitting photoluminescent phosphor is selected from:
(Sr,Ca)S:Eu; or
(M 1−x M′ x )Si 5 N 8 :Eu where M and M′ are at least one of Ca, Sr, and Ba and 0≦×≦1; or
a combination thereof.
4. The phosphor blend of claim 1 wherein the green-emitting electroluminescent phosphor emits between 470 nm to 550 nm and the red-emitting photoluminescent phosphor exhibits a red emission having an x color coordinate from 0.570 to 0.695 and a y color coordinate from 0.325 to 0.430 when stimulated by the emission from the green-emitting electroluminescent phosphor.
5. The phosphor blend of claim 1 wherein the green-emitting EL phosphor comprises from 85 to 96 weight percent of the blend and the red-emitting photoluminescent phosphor comprises from 4 to 15 weight percent of the blend.
6. A phosphor blend for an electroluminescent lamp, comprising:
a green-emitting electroluminescent phosphor and a red-emitting photoluminescent phosphor, the blend exhibiting an x color coordinate from 0.220 to 0.350 and a y color coordinate from 0.450 to 0.475 when stimulated by an electric field;
the green-emitting electroluminescent phosphor comprising ZnS:Cu,Cl and the red-emitting photoluminescent phosphor being selected from:
(Sr,Ca)S:Eu; or
(M 1−x M′ x )Si 5 N 8 :Eu where M and M′ are at least one of Ca, Sr, and Ba and 0≦×≦1; or
a combination thereof; and
the green-emitting EL phosphor comprising from 85 to 96 weight percent of the blend and the red-emitting photoluminescent phosphor comprising from 4 to 15 weight percent of the blend.
7. The phosphor blend of claim 6 wherein the blend exhibits an x color coordinate from 0.235 to 0.335 and a y color coordinate from 0.460 to 0.465 when stimulated by an electric field.
8. The phosphor blend of claim 7 wherein the red-emitting photoluminescent phosphor is (Sr,Ca)S:Eu.