Thermoforming process for producing class “A” finish, high gloss automotive exterior parts
View Patent ↗A thermoforming methodology for laminated thermoplastic sheets which preserves the class “A” finish and high gloss thereof. In a thermoforming process including heating followed by vacuum and opposing air pressure application, and then followed by application of chilled compressed air, control of spherulite formation using any of: addition of a nucleating agent to the paint film, using the chilled compressed air at a temperature of substantially about 32° F., heating to no more than about 311° F., selecting a paint film having a high melting point temperature, and selecting a paint film that is non-crystalline.
1. A method for controlling spherulite formation during thermoforming a laminated thermoplastic sheet, wherein the thermoforming comprises the steps of: a) heating the laminated thermoplastic sheet, wherein the laminated thermoplastic sheet has a first side and an opposite second side, wherein the first side comprises a class “A” paint film having an initial gloss; b) placing the heated laminated thermoplastic sheet into a thermoformer, wherein the thermoformer has a mold surface and wherein the second side of the laminated thermoplastic film faces toward the mold surface; c) cooling the mold surface; d) applying vacuum to the thermoformer, wherein the vacuum acts suckingly upon the second side of the laminated thermoplastic sheet; and e) applying chilled compressed air having a temperature less than 70 degrees F to the thermoformer during the step d), wherein the chilled compressed air acts pressurably upon the first side of the laminated thermoplastic sheet; wherein the vacuum and the chilled compressed air act on the laminated thermoplastic sheet to cause the laminated thermoplastic sheet to conform to a shape of the mold surface; and wherein the chilled compressed air causes the laminated thermoplastic sheet to cool at a rate which preserves the initial gloss of the class “A” paint film; said method for controlling spherulite formation comprising at least one step selected from the group of steps consisting of:
aa) adding a nucleating agent to the paint film prior to step a);
bb) performing step e) using the chilled compressed air at a temperature of substantially between 32 degrees F and 50 degrees F;
cc) performing step a) such that the paint film of the laminated thermoplastic sheet is kept below substantially between 311 degrees F and 330 degrees F; and
dd) selecting the paint film, prior to step a), such that the paint film has a high melting point temperature relative to a temperature imparted to the paint film in step a).
2. The method of claim 1 , wherein said method for controlling spherulite formation comprises selecting all of said steps aa) through dd).
3. The method of claim 2 , wherein in said step cc) the paint film of the laminated thermoplastic sheet is kept below substantially 330 degrees F.
4. The method of claim 1 , wherein said step dd) comprises selecting a ratio of poly(vinylidene fluoride) to poly(methylmethacrylate) of at least fifty percent poly(vinylidene fluoride).
5. The method of claim 4 , wherein said method for controlling spherulite formation comprises selecting all of said steps aa) through dd).
6. The method of claim 5 , wherein in said step cc) the paint film of the laminated thermoplastic sheet is kept below substantially 330 degrees F.
7. The method of claim 5 , wherein said step dd) comprises selecting a ratio of poly(vinylidene fluoride) to poly(methylmethacrylate) of substantially seventy percent poly(vinylidene fluoride).
8. The method of claim 7 , wherein said method for controlling spherulite formation comprises selecting all of said steps aa) through dd).
9. The method of claim 8 , wherein in said step cc) the paint film of the laminated thermoplastic sheet is kept below substantially 330 degrees F.
10. A method for controlling spherulite formation during thermoforming a laminated thermoplastic sheet, wherein the thermoforming comprises the steps of: a) heating the laminated thermoplastic sheet, wherein the laminated thermoplastic sheet has a first side and an opposite second side, wherein the first side comprises a class “A” paint film having an initial gloss; b) placing the heated laminated thermoplastic sheet into a thermoformer, wherein the thermoformer has a mold surface and wherein the second side of the laminated thermoplastic film faces toward the mold surface; c) cooling the mold surface; d) applying vacuum to the thermoformer, wherein the vacuum acts suckingly upon the second side of the laminated thermoplastic sheet; e) applying compressed air to the thermoformer substantially simultaneously with the step d), wherein the compressed air acts pressurably upon the first side of the laminated thermoplastic sheet; and f) applying chilled compressed air having a temperature less than 70 degrees F to the thermoformer after the step e) and during the step d), wherein the chilled compressed air acts pressurably upon the first side of the laminated thermoplastic sheet; wherein the vacuum and the chilled compressed air act on the laminated thermoplastic sheet to cause the laminated thermoplastic sheet to conform to a shape of the mold surface; and wherein the chilled compressed air causes the laminated thermoplastic sheet to cool at a rate which preserves the initial gloss of the class “A” paint film; said method for controlling spherulite formation comprising at least one step selected from the group of steps consisting of:
aa) adding a nucleating agent to the paint film prior to step a);
bb) performing step e) using the chilled compressed air at a temperature of substantially 32 degrees F;
cc) performing step a) such that the paint film of the laminated thermoplastic sheet is kept below substantially 311 degrees F; and
dd) selecting the paint film, prior to step a), such that the paint film has a high melting point temperature relative to a temperature imparted to the paint film in step a).
11. The method of claim 10 , wherein said method for controlling spherulite formation comprises selecting all of said steps aa) through dd).
12. The method of claim 11 , wherein in said step cc) the paint film of the laminated thermoplastic sheet is kept below substantially 330 degrees F.
13. The method of claim 10 , wherein said step dd) comprises selecting a ratio of poly(vinylidene fluoride) to poly(methylmethacrylate) of at least fifty percent poly(vinylidene fluoride).
14. The method of claim 13 , wherein said method for controlling spherulite formation comprises selecting all of said steps aa) through dd).
15. The method of claim 14 , wherein in said step cc) the paint film of the laminated thermoplastic sheet is kept below substantially 330 degrees F.
16. The method of claim 13 , wherein said step dd) comprises selecting a ratio of poly(vinylidene fluoride) to poly(methylmethacrylate) of substantially seventy percent poly(vinylidene fluoride).
17. The method of claim 16 , wherein said method for controlling spherulite formation comprises selecting all of said steps aa) through dd).
18. The method of claim 17 , wherein in said step cc) the paint film of the laminated thermoplastic sheet is kept below substantially 330 degrees F.