Coated polymeric film with oxygen barrier properties
A coating compositions for providing substrates with oxygen barrier properties is disclosed. The substrate may be, for instance, a film, such as a polyester film. The coating composition includes a copolymer of maleic acid and acrylic acid and a copolymer of vinyl alcohol and a vinylamine. The barrier coating formed from the coating composition is typically less than about 1 micron in thickness and provides reduced oxygen transmission even at relatively high relative humidities.
1. A coated polymeric film comprising:
a polymer film; and
a coating disposed on at least one side of the film, the coating comprising a copolymer of vinyl alcohol and a vinylamine reacted with a copolymer of a maleic acid and an acrylic acid, the coating being present in an amount sufficient to increase the oxygen barrier properties of the film.
2. A coated polymeric film as defined in claim 1 , wherein the polymer film comprises a polyester film.
3. A coated polymeric film as defined in claim 1 , wherein the copolymer of vinyl alcohol and a vinylamine comprises from about 8 mole percent to about 15 mole percent vinylamine.
4. A coated polymeric film as defined in claim 1 , wherein the copolymer of a maleic acid and an acrylic acid has an average molecular weight of from about 3500 to about 5000.
5. A coated polymeric film as defined in claimed 1 , wherein a coating composition forming the coating contains the copolymer of polyvinyl alcohol and a vinylamine in an amount from about 35% to about 65% by weight of percent solids.
6. A coated polymeric film as defined in claim 1 , wherein a coating composition forming the coating contains the copolymer of polyvinyl alcohol and a vinylamine in an amount from about 45% to about 55% by weight of percent solids.
7. A coated polymeric film as defined in claim 1 , wherein the coating has a thickness of less than about 0.3 microns.
8. A coated polymeric film as defined in claim 1 , wherein the coated polymeric film further comprises a metal layer.
9. A coated polymeric film as defined in claim 1 , wherein the coating provides the film with an oxygen transmission rate of less than about 4 cc.mil/m 2 /day/atm at 23° C. and 0% relative humidity.
10. A coated polymeric film as defined in claim 1 , wherein the coating provides the film with an oxygen transmission rate of less than about 6 cc.mil/m 2 /day/atm at 23° C. and 50% relative humidity.
11. A coated polymeric film as defined in claim 1 , wherein the coating provides the film with an oxygen transmission rate of less than about 20 cc.mil/m 2 /day/atm at 23° C. and 70% relative humidity.
12. A coated polymeric film as defined in claim 1 , wherein the coating provides the film with an oxygen transmission of less than about 4 cc.mil/m 2 /day/atm at 23° C. and 50% relative humidity.
13. A coated polymeric film as defined in claim 1 , wherein the coating further comprises a crosslinker.
14. A coated polymeric film as defined in claim 13 , wherein the crosslinker comprises a hydroxy acid.
15. A coated polymeric film as defined in claim 14 , wherein the hydroxy acid contains a carboxylic acid group.
16. A coated polymeric film as defined in claim 13 , wherein the crosslinker comprises glycolic acid.
17. A coated polymeric film as defined in claim 1 , wherein the polymer film is laminated to a second polymer film, the coating being located in between the first polymer film and the second polymer film.
18. A coated polymeric film as defined in claim 17 , wherein the second polymer film comprises a polyolefin.
19. A coated polymeric film as defined in claim 17 , wherein the second polymer film comprises a polyethylene.
20. A coated polymeric film as defined in claim 1 , wherein the copolymer of vinyl alcohol and the vinylamine is formed by hydrolyzing in water under a basic condition a N-vinylamide and a vinyl acetate.
21. A coated polymeric film as defined in claim 1 , wherein the copolymer of vinyl alcohol and the vinylamine is formed by hydrolyzing the acetate functionality of a poly(vinyl acetate)-co-poly(N-vinyl formamide) in an alcohol medium to yield a vinyl alcohol copolymer and then hydrolyzing the vinyl alcohol copolymer as a slurry in an alcohol.
22. A coated polymeric film comprising:
a polymer film comprising a polyester polymer, the film having a first side and a second side; and
an oxygen barrier coating disposed on the first side of the polymeric film, the oxygen barrier coating having a thickness of less than about 0.5 microns, the oxygen barrier coating comprising a vinyl alcohol and vinylamine random copolymer, the barrier coating reducing the oxygen transmissivity of the film such that the coated polymeric film has an oxygen transmission rate of less than about 4 cc.mil/m 2 /day/atm at 23° C. and 0% relative humidity, less than about 6 cc.mil/m 2 /day/atm at 23° C. and 50% relative humidity, less than 8 cc.mil/m 2 /day/atm at 23° C. and 60% relative humidity and less than about 20 cc.mil/m 2 /day/atm at 23° C. and 70% relative humidity.
23. A coated polymeric film as defined in claim 22 , wherein the copolymer of vinyl alcohol and a vinylamine comprises from about 8 mole percent to about 15 mole percent vinylamine.
24. A coated polymeric film as defined in claim 22 , wherein the oxygen barrier coating further comprises a copolymer of a maleic acid and an acetic acid, the copolymer having an alternating structure, the barrier coating being crosslinked.
25. A coated polymeric film comprising:
a polymer film; and
a coating disposed on at least on side of the film, the coating comprising a first polymer reacted with a second polymer through the use of a crosslinker, the first polymer comprising a copolymer of vinyl alcohol and a vinylamine, the crosslinker comprising glycolic acid.
26. A coated polymeric film as defined in claim 25 , wherein the second polymer comprises a copolymer of a maleic acid and an acrylic acid.
27. A coated polymeric film as defined in claim 25 , wherein the polymer film comprises a polyester film.
28. A coated polymeric film as defined in claim 25 , wherein the copolymer of vinyl alcohol and a vinylamine comprises from about 8 mole percent to about 15 mole percent vinylamine.